Description : The inert mineral material used for the manufacture of mortars and concrete is (a) Cement (b) Water (c) Aggregates (d) Admixture
Last Answer : (c) Aggregates
Description : The most common admixture which is used to accelerate the initial set of concrete is (A) Gypsum (B) Calcium chloride (C) Calcium carbonate (D) None of the above
Last Answer : Answer: Option B
Description : For highly loaded columns, the concrete mix used is (a) 1:1:2 (b) 1:1.5:2 (c) 1:2:4 (d) 1:3:6
Last Answer : (a) 1:1:2
Description : Explain the significance of water reducing admixture in concrete with respect to properties of concrete.
Last Answer : Significance of water reducing admixture in concrete: Water reducing admixtures are essential for several purposes. The effect of using such admixtures on concrete properties is described below. 1. Water ... strength. 7. The durability of concrete structures can be ensured by using these admixtures.
Description : The Most common admixture used to accelerate the initial setting of concrete is a) Gypsum b) Calcium chloride* c) Calcium carbonate d) Calcium bicarbonate
Last Answer : b) Calcium chloride*
Description : Pick up the correct statement from the following: (A) Insufficient quantity of water makes the concrete mix harsh (B) Insufficient quantity of water makes the concrete unworkable (C) Excess quantity of water makes the concrete segregated (D) All the above
Last Answer : (D) All the above
Description : Excess quantity of water (a) Makes the concrete mix harsh (b) Makes the concrete mix unworkable (c) Causes segregation in concrete (d) Causes bleeding in concrete.
Last Answer : both c&d
Description : Insufficient quantity of water (a) Makes the concrete mix harsh (b) Makes the concrete mix unworkable (c) Causes segregation in concrete (d) Causes bleeding in concrete.
Last Answer : both a&b
Description : ick up the incorrect statement from the following: (A) Admixtures accelerate hydration (B) Admixtures make concrete water proof (C) Admixtures make concrete acid proof (D) Admixtures give high strength
Last Answer : Answer: Option A
Description : For preparing a test-specimen, it is necessary (A) To mix cement and fine aggregate by dry hand (B) To mix coarse aggregates (C) To mix water to the cement, fine aggregates and coarse aggregates (D) All the above
Last Answer : Answer: Option D
Description : The most commonly used admixture which prolongs the setting and hardening time is (A) Gypsum (B) Calcium chloride (C) Sodium silicate (D) All of the above
Last Answer : (A) Gypsum
Description : The admixture of coarser particles like sand or silt to clay causes (A) Decrease in liquid limit and increase in plasticity index (B) Decrease in liquid limit and no change in plasticity index ... in both liquid limit and plasticity index (D) Increase in both liquid limit and plasticity index
Last Answer : Answer: Option C
Description : For preparing ordinary concrete, the quantity of water used, is (A) 5% by weight of aggregates plus 20% of weight of cement (B) 10% by weight of aggregates plus 10% of weight of cement (C) ... aggregates plus 30% of weight of cement (D) 30% by weight of aggregates plus 10% of weight of cement
Description : Which of the following reagents is most suitable for preparing chlorobenzene from benzene? (a) Aqueous chlorine (b) Chlorine in the presence of ultraviolet light (c) Chlorine in acetic acid (d) Chlorine in the presence of FeCl3
Last Answer : Chlorine in the presence of FeCl3
Description : An ordinary concrete may be made water proof by adding (A) Pudlo (B) Impermo (C) Snowcem (D) All of these
Description : The measurement is not made in square metres in case of (A) D.P.C. (Damp proof course) (B) Form works (C) Concrete Jeffries (D) R.C. Chhajja
Last Answer : (D) R.C. Chhajja
Description : In the activated sludge process A. Aeration is continued till stability B. Aeration is done with an admixture of previously aerated sludge C. Sludge is activated by constant stirring D. Water is removed by centrifugal action
Last Answer : ANS: B
Description : Granite is not suitable for ordinary building purpose because (A) It cannot be polished (B) It is not a fire proof material (C) It is costly (D) It has less crushing strength
Description : Workability of concrete is inversely proportional to (A) Time of transit (B) water-cement ratio (C) The air in the mix (D) Size of aggregate
Description : The basic purpose of a retarder in concrete is (A) To increase the initial setting time of cement paste in concrete (B) To decrease the initial setting time of cement paste in concrete (C) To render the concrete more water tight (D) To improve the workability of concrete mix
Description : Pick up the correct statement from the following: (A) A highly absorptive aggregate reduces the workability of concrete considerably (B) The specific gravity of aggregate is important for the determination ... and porosity of an aggregate influence the property of the concrete (D) All the above
Description : The shrinkage of concrete (A) Is proportional to water content is the mix (B) Is proportional to cement concrete (C) Increases with age of concrete (D) All the above
Description : Pick up the correct statement from the following: (A) The weight of ingredients of concrete mix, is taken in kilograms (B) Water and aggregates are measured in litres (C) 20 bags of cement make one tonne (D) All the above
Description : According to Water-Cement Ratio Law, the strength of workable plastic concrete (A) Depends upon the amount of water used in the mix (B) Does not depend upon the quality of cement mixed with aggregates (C) Does not depend upon the quantity of cement mixed with aggregates (D) All the above
Description : If 50 kg of fine aggregates and 100 kg of coarse aggregates are mixed in a concrete whose water cement ratio is 0.6, the weight of water required for harsh mix, is (A) 8 kg (B) 10 kg (C) 12 kg (D) 14 kg
Description : Inert material of a cement concrete mix, is (A) Water (B) Cement (C) Aggregate (D) None of these
Description : Shrinkage in concrete can be reduced by using (A) Low water cement ratio (B) Less cement in the concrete (C) Proper concrete mix (D) All the above
Description : For a concrete mix 1:3:6 and water cement ratio 0.6 both by weight, the quantity of water required per bag, is (A) 10 kg (B) 12 kg (C) 14 kg (D) 16 kg
Description : Pick up the incorrect statement from the following. While performing preliminary test on concrete (A) Proportions of the material and water should be the same as to be used at the work site (B) ... in air-tight containers (D) Concrete ingredients should be kept at a temperature of 37° 2°C
Description : Pick up the correct statement from the following: (A) An increase in water content must be accompanied by an increase in cement content (B) Angular and rough aggregates reduce the workability of the ... The slump of the concrete mix decreases due to an increase in temperature (D) All the above
Description : Workability of concrete mix with low water cement ratio is determined by (A) Tensile strength test (B) Slump test (C) Compaction factor test (D) Flexural strength test
Description : The property of fresh concrete, in which the water in the mix tends to rise to the surface while placing and compacting, is called (A) Segregation (B) Bleeding (C) Bulking (D) Creep
Description : Internal friction between the ingredients of concrete, is decreased by using (A) Less water (B) Fine aggregates (C) Rich mix (D) More water and coarse aggregates
Description : The factors which effects the design of concrete mix is (a) Fineness modulus (b) Water cement ratio (c) Slump (d) All of these
Last Answer : (d) All of these
Description : According to the rule of water cement ratio, the strength of concrete wholly depends upon. (a) The quality of cement. (b) The quality of cement mixed with aggregate. (c) The amount of water used in preparation of concrete mix. (d) All of the above
Last Answer : (c) The amount of water used in preparation of concrete mix.
Description : Inert material of a cement concrete mix, is [ A ] Water [ B ] Aggregate [ C ] Cement [ D ] None of these
Last Answer : [ B ] Aggregate
Description : Workability of concrete mix with low water cement ratio is determined by [ A ] Tensile strength test [ B ] Slump cone test [ C ] Compaction factor test [ D ] Flexural strength test
Last Answer : [ C ] Compaction factor test
Description : For M 150 mix concrete, according to I.S. specifications, local bond stress, is (A) 5 kg/cm2 (B) 10 kg/cm2 (C) 15 kg/cm2 (D) 20 kg/cm
Description : Minimum number of 50 kg cement bags per cubic metre of concrete for a mix corresponding to crushing strength 280 kg/cm2 at 28 days, are (A) 5.0 (B) 6.5 (C) 7.0 (D) 7.5
Description : Which of the following represents a carpet of sand-bitumen mix without coarse aggregates? (A) Mastic asphalt (B) Sheet asphalt (C) Bituminous carpet (D) Bituminous concrete
Description : For the construction of R.C.C. slabs, columns, beams, walls, etc. the grade of concrete mix used, is (A) 1 : 3 : 6 (B) 1 : 1½ : 3 (C) 1 : 2 : 4 (D) 1 : 1 : 2
Last Answer : (C) 1 : 2 : 4
Description : 1% of voids in a concrete mix would reduce its strength by about (A) 5 % (B) 10 % (C) 15 % (D) 20 %
Last Answer : (A) 5 %
Description : After casting, an ordinary cement concrete on drying (A) Expands (B) Mix (C) Shrinks (D) None of these
Last Answer : (C) Shrinks
Description : M 150 grade of concrete approximates (A) 1 : 3 : 6 mix (B) 1 : 1 :2 mix (C) 1 : 2 : 4 mix (D) 1 : 1.5 : 3 mix
Last Answer : (B) 1 : 1 :2 mix
Description : For the construction of the retaining structures, the type of concrete mix to be used, is (A) 1 : 3 : 6 (B) 1 : 2 : 4 (C) 1 : 1½ : 3 (D) 1 : 4 : 8
Description : If the slump of a concrete mix is 60 mm, its workability is (A) Very low (B) Low (C) Medium (D) High
Description : M10 grade of concrete approximates (A) 1 : 3 : 6 mix (B) 1 : 1 : 2 mix (C) 1 : 2 : 4 mix (D) 1 : 1.5 : 3 mix
Description : Pick up the correct statement from the following: (A) Higher workability indicates unexpected increase in the moisture content (B) Higher workability indicates deficiency of sand (C) If the concrete mix is dry, the slump is zero (D) All the above
Description : The concrete mix which causes difficulty in obtaining a smooth finish, possess (A) Segregation (B) Internal friction (C) Hardness (D) Bleeding
Description : The following proportion of the ingredients of concrete mix, is not in conformation to arbitrary method of proportioning (A) 1 : 1 : 2 (B) 1 : 2 : 4 (C) 1 : 3 : 6 (D) 1 : 4 : 10