According to Water-Cement Ratio Law, the strength of workable plastic concrete (A) Depends upon the amount of water used in the mix (B) Does not depend upon the quality of cement mixed with aggregates (C) Does not depend upon the quantity of cement mixed with aggregates (D) All the above

According to Water-Cement Ratio Law, the strength of workable plastic concrete
(A) Depends upon the amount of water used in the mix
(B) Does not depend upon the quality of cement mixed with aggregates
(C) Does not depend upon the quantity of cement mixed with aggregates
(D) All the above
by

1 Answer

Answer :

Answer: Option D
by

Related questions

According to the rule of water cement ratio, the strength of concrete wholly depends upon. (a) The quality of cement. (b) The quality of cement mixed with aggregate. (c) The amount of water used in preparation of concrete mix. (d) All of the above

Description : According to the rule of water cement ratio, the strength of concrete wholly depends upon. (a) The quality of cement. (b) The quality of cement mixed with aggregate. (c) The amount of water used in preparation of concrete mix. (d) All of the above

Last Answer : (c) The amount of water used in preparation of concrete mix.

Strength of cement concrete primarily depends upon (A) Quality of water (B) Quantity of aggregate (C) Quantity of cement (D) Water-cement

Description : Strength of cement concrete primarily depends upon (A) Quality of water (B) Quantity of aggregate (C) Quantity of cement (D) Water-cement

Last Answer : Answer: Option D

The strength and quality of concrete, depend upon: (A) Grading of aggregates (B) Surface area of aggregates (C) Shape of aggregates (D) All the above

Description : The strength and quality of concrete, depend upon: (A) Grading of aggregates (B) Surface area of aggregates (C) Shape of aggregates (D) All the above

Last Answer : Answer: Option D

If 50 kg of fine aggregates and 100 kg of coarse aggregates are mixed in a concrete whose water cement ratio is 0.6, the weight of water required for harsh mix, is (A) 8 kg (B) 10 kg (C) 12 kg (D) 14 kg

Description : If 50 kg of fine aggregates and 100 kg of coarse aggregates are mixed in a concrete whose water cement ratio is 0.6, the weight of water required for harsh mix, is (A) 8 kg (B) 10 kg (C) 12 kg (D) 14 kg

Last Answer : Answer: Option C

A concrete using an air entrained cement (A) Has strength less than 10% to 15% (B) Has more resistance to weathering (C) Is more plastic and workable (D) Is free from segregation and bleeding

Description : A concrete using an air entrained cement (A) Has strength less than 10% to 15% (B) Has more resistance to weathering (C) Is more plastic and workable (D) Is free from segregation and bleeding

Last Answer : Answer: Option C

The strength and quality of concrete depends upon (i)Grading of aggregates (ii)Shape of aggregates (iii)Surface area of aggregates (iv)Surface texture of aggregates [ A ] i, ii and iv [ B ] ii, iii and iv [ C ] i, iii and iv [ D ] i, ii, iii and iv

Description : The strength and quality of concrete depends upon (i)Grading of aggregates (ii)Shape of aggregates (iii)Surface area of aggregates (iv)Surface texture of aggregates [ A ] i, ii and iv [ B ] ii, iii and iv [ C ] i, iii and iv [ D ] i, ii, iii and iv

Last Answer : [ D ] i, ii, iii and iv

The strength of durability of concrete depends upon. (a) Size of aggregates (b) Grading of aggregates (c) Moisture contents of aggregates (d) All of these.

Description : The strength of durability of concrete depends upon. (a) Size of aggregates (b) Grading of aggregates (c) Moisture contents of aggregates (d) All of these.

Last Answer : (d) All of these.

Minimum required water cement ratio for a workable concrete, is (A) 0.30 (B) 0.40 (C) 0.50 (D) 0.60

Description : Minimum required water cement ratio for a workable concrete, is (A) 0.30 (B) 0.40 (C) 0.50 (D) 0.60

Last Answer : Answer: Option B

Shrinkage in concrete can be reduced by using (i) Low water cement ratio (ii) More amount of cement in the concrete (iii) Presaturated aggregates [ A ] i [ B ] i and ii [ C ] i and iii [ D ] i, ii and iii

Description : Shrinkage in concrete can be reduced by using (i) Low water cement ratio (ii) More amount of cement in the concrete (iii) Presaturated aggregates [ A ] i [ B ] i and ii [ C ] i and iii [ D ] i, ii and iii

Last Answer : [ C ] i and iii

Pick up the correct statement from the following: (A) The weight of ingredients of concrete mix, is taken in kilograms (B) Water and aggregates are measured in litres (C) 20 bags of cement make one tonne (D) All the above

Description : Pick up the correct statement from the following: (A) The weight of ingredients of concrete mix, is taken in kilograms (B) Water and aggregates are measured in litres (C) 20 bags of cement make one tonne (D) All the above

Last Answer : Answer: Option D

Pick up the correct statement from the following: (A) An increase in water content must be accompanied by an increase in cement content (B) Angular and rough aggregates reduce the workability of the concrete (C) The slump of the concrete mix decreases due to an increase in temperature (D) All the above

Description : Pick up the correct statement from the following: (A) An increase in water content must be accompanied by an increase in cement content (B) Angular and rough aggregates reduce the workability of the ... The slump of the concrete mix decreases due to an increase in temperature (D) All the above

Last Answer : Answer: Option D

For batching 1:3:6 concrete mix by volume, the ingredients required per bag of 50 kg cement, are: (A) 70 litres of sand and 120 litres of aggregates (B) 70 kg of sand and 140 litres of aggregates (C) 105 litres of sand and 140 litres of aggregates (D) 105 litres of sand and 210 litres of aggregates

Description : For batching 1:3:6 concrete mix by volume, the ingredients required per bag of 50 kg cement, are: (A) 70 litres of sand and 120 litres of aggregates (B) 70 kg of sand and 140 litres of ... C) 105 litres of sand and 140 litres of aggregates (D) 105 litres of sand and 210 litres of aggregates

Last Answer : Answer: Option D

For preparing ordinary concrete, the quantity of water used, is (A) 5% by weight of aggregates plus 20% of weight of cement (B) 10% by weight of aggregates plus 10% of weight of cement (C) 5% by weight of aggregates plus 30% of weight of cement (D) 30% by weight of aggregates plus 10% of weight of cement

Description : For preparing ordinary concrete, the quantity of water used, is (A) 5% by weight of aggregates plus 20% of weight of cement (B) 10% by weight of aggregates plus 10% of weight of cement (C) ... aggregates plus 30% of weight of cement (D) 30% by weight of aggregates plus 10% of weight of cement

Last Answer : Answer: Option C

For a concrete mix 1:3:6 and water cement ratio 0.6 both by weight, the quantity of water required per bag, is (A) 10 kg (B) 12 kg (C) 14 kg (D) 16 k

Description : For a concrete mix 1:3:6 and water cement ratio 0.6 both by weight, the quantity of water required per bag, is (A) 10 kg (B) 12 kg (C) 14 kg (D) 16 kg

Last Answer : Answer: Option C

Pick up the correct statement from the following: (A) Water enables chemical reaction to take place with cement (B) Water lubricates the mixture of gravel, sand and cement (C) Strength of concrete structure largely depends upon its workability (D) All the above

Description : Pick up the correct statement from the following: (A) Water enables chemical reaction to take place with cement (B) Water lubricates the mixture of gravel, sand and cement (C) Strength of concrete structure largely depends upon its workability (D) All the above

Last Answer : (D) All the above

Pick up the correct statement from the following: (A) Segregation is necessary for a workable concrete (B) Consistency does not affect the workability of concrete (C) If the concrete mix is dry, the slump is maximum (D) None of these

Description : Pick up the correct statement from the following: (A) Segregation is necessary for a workable concrete (B) Consistency does not affect the workability of concrete (C) If the concrete mix is dry, the slump is maximum (D) None of these

Last Answer : Answer: Option D

The concrete mix is said to be workable if it has (a) Compatibility (b) Movability (c) Stability (d) All of these

Description : The concrete mix is said to be workable if it has (a) Compatibility (b) Movability (c) Stability (d) All of these

Last Answer : (d) All of these

For a good concrete (A) Aggregates should be hard and durable (B) Water should be free from organic materials (C) Cement should be sufficient to produce the required strength (D) All the above

Description : For a good concrete (A) Aggregates should be hard and durable (B) Water should be free from organic materials (C) Cement should be sufficient to produce the required strength (D) All the above

Last Answer : Answer: Option D

Pick up the correct statement from the following: (A) Water cement paste hardens due to hydration (B) During hardening cement binds the aggregates together (C) Cement provides strength, durability and water tightness to the concrete (D) All the above

Description : Pick up the correct statement from the following: (A) Water cement paste hardens due to hydration (B) During hardening cement binds the aggregates together (C) Cement provides strength, durability and water tightness to the concrete (D) All the above

Last Answer : Answer: Option D

Concrete gains strength due to (A) Chemical reaction of cement with sand and coarse aggregates (B) Evaporation of water from concrete (C) Hydration of cement (D) All the above

Description : Concrete gains strength due to (A) Chemical reaction of cement with sand and coarse aggregates (B) Evaporation of water from concrete (C) Hydration of cement (D) All the above

Last Answer : Answer: Option C

Concrete gains strength due to [ A ] Chemical reaction of cement with sand and coarse aggregates [ B ] Evaporation of water from concrete [ C ] Hydration of cement [ D ] All the above

Description : Concrete gains strength due to [ A ] Chemical reaction of cement with sand and coarse aggregates [ B ] Evaporation of water from concrete [ C ] Hydration of cement [ D ] All the above

Last Answer : [ C ] Hydration of cement

Workability of concrete mix with low water cement ratio is determined by (A) Tensile strength test (B) Slump test (C) Compaction factor test (D) Flexural strength test

Description : Workability of concrete mix with low water cement ratio is determined by (A) Tensile strength test (B) Slump test (C) Compaction factor test (D) Flexural strength test

Last Answer : Answer: Option C

Workability of concrete mix with low water cement ratio is determined by [ A ] Tensile strength test [ B ] Slump cone test [ C ] Compaction factor test [ D ] Flexural strength test

Description : Workability of concrete mix with low water cement ratio is determined by [ A ] Tensile strength test [ B ] Slump cone test [ C ] Compaction factor test [ D ] Flexural strength test

Last Answer : [ C ] Compaction factor test

Pick up the correct statement from the following: (A) Plain cement concrete is equally strong in compression as well as in tension (B) Slump test is performed to check concrete strength (C) Curing of concrete is done for proper compaction of cement (D) Fineness modulus is the index number expressing the relative sizes of both coarse and fine aggregates

Description : Pick up the correct statement from the following: (A) Plain cement concrete is equally strong in compression as well as in tension (B) Slump test is performed to check concrete strength (C ... D) Fineness modulus is the index number expressing the relative sizes of both coarse and fine aggregates

Last Answer : Option D

If P, Y and Z are the weights of cement, fine aggregates and coarse aggregates respectively and W/C is the water cement ratio, the minimum quantity of water to be added to first batch, is obtained by the equation (A) 0.1P + 0.3Y + 0.1Z = W/C × P (B) 0.3P + 0.1Y + 0.01Z = W/C × P (C) 0.4P + 0.2Y + 0.01Z = W/C × P (D) 0.5P + 0.3Y + 0.01Z = W/C × P

Description : If P, Y and Z are the weights of cement, fine aggregates and coarse aggregates respectively and W/C is the water cement ratio, the minimum quantity of water to be added to first batch, is obtained by the equation (A) 0.1P + 0.3Y + 0. ... + 0.2Y + 0.01Z = W/C P (D) 0.5P + 0.3Y + 0.01Z = W/C P

Last Answer : Answer: Option B

While designing an air entrained concrete (A) Water cement ratio is reduced (B) Proportion of aggregates is reduced (C) An allowance for the entrained air is made (D) All the above

Description : While designing an air entrained concrete (A) Water cement ratio is reduced (B) Proportion of aggregates is reduced (C) An allowance for the entrained air is made (D) All the above

Last Answer : (D) All the above

The ratio of various ingredients (cement, sand, aggregates) in concrete of grade M 200, is (A) 1 : 2 : 4 (B) 1 : 3 : 6 (C) 1 : 1½ : 3 (D) 1 : 1 : 2

Description : The ratio of various ingredients (cement, sand, aggregates) in concrete of grade M 200, is (A) 1 : 2 : 4 (B) 1 : 3 : 6 (C) 1 : 1½ : 3 (D) 1 : 1 : 2

Last Answer : (C) 1 : 1½ : 3

If the various concrete ingredients i.e. cement, sand and aggregates are in the ratio of 1:3:6, the grade of concrete, is (A) M 100 (B) M 150 (C) M 200 (D) M 250

Description : If the various concrete ingredients i.e. cement, sand and aggregates are in the ratio of 1:3:6, the grade of concrete, is (A) M 100 (B) M 150 (C) M 200 (D) M 250

Last Answer : Answer: Option A

Pick up the incorrect statement from the following. While performing preliminary test on concrete (A) Proportions of the material and water should be the same as to be used at the work site (B) Cement should be mixed by hand in order to maintain uniformity (C) Concrete mix should be stored in air-tight containers (D) Concrete ingredients should be kept at a temperature of 37° ± 2°C

Description : Pick up the incorrect statement from the following. While performing preliminary test on concrete (A) Proportions of the material and water should be the same as to be used at the work site (B) ... in air-tight containers (D) Concrete ingredients should be kept at a temperature of 37° 2°C

Last Answer : Answer: Option D

The condition not applicable to water cement ratio law, is (A) Internal moisture conditions on hydration continue till complete strength is gained (B) Concrete specimens may be tested at any temperature (C) Concrete specimens need be of same age (D) Concrete specimens need be of same size

Description : The condition not applicable to water cement ratio law, is (A) Internal moisture conditions on hydration continue till complete strength is gained (B) Concrete specimens may be tested at any temperature (C) Concrete specimens need be of same age (D) Concrete specimens need be of same size

Last Answer : Answer: Option B

Minimum number of 50 kg cement bags per cubic metre of concrete for a mix corresponding to crushing strength 280 kg/cm2 at 28 days, are (A) 5.0 (B) 6.5(C) 7.0 (D) 7.5

Description : Minimum number of 50 kg cement bags per cubic metre of concrete for a mix corresponding to crushing strength 280 kg/cm2 at 28 days, are (A) 5.0 (B) 6.5 (C) 7.0 (D) 7.5

Last Answer : Answer: Option B

The bulk density of aggregates does not depend upon: (A) Size and shape of aggregates (B) Specific gravity of aggregates (C) Grading of aggregates (D) Size and shape of the container

Description : The bulk density of aggregates does not depend upon: (A) Size and shape of aggregates (B) Specific gravity of aggregates (C) Grading of aggregates (D) Size and shape of the container

Last Answer : Answer: Option D

For preparing a test-specimen, it is necessary (A) To mix cement and fine aggregate by dry hand (B) To mix coarse aggregates (C) To mix water to the cement, fine aggregates and coarse aggregates (D) All the above

Description : For preparing a test-specimen, it is necessary (A) To mix cement and fine aggregate by dry hand (B) To mix coarse aggregates (C) To mix water to the cement, fine aggregates and coarse aggregates (D) All the above

Last Answer : Answer: Option D

Pick up the incorrect statement from the following: (A) Concrete for which preliminary tests are conducted, is called controlled concrete (B) Bulking of sand depends upon the fineness of grains (C) Concrete mix 1 : 6 : 12, is used for mass concrete in piers (D) All the above

Description : Pick up the incorrect statement from the following: (A) Concrete for which preliminary tests are conducted, is called controlled concrete (B) Bulking of sand depends upon the fineness of grains (C) Concrete mix 1 : 6 : 12, is used for mass concrete in piers (D) All the above

Last Answer : Answer: Option D

The depth of concrete bed of the foundation depends upon (A) The projection of the concrete block beyond the footing over it (B) The upward soil pressure (C) The mix of the concrete (D) All the above

Description : The depth of concrete bed of the foundation depends upon (A) The projection of the concrete block beyond the footing over it (B) The upward soil pressure (C) The mix of the concrete (D) All the above

Last Answer : Answer: Option D

Internal friction between the ingredients of concrete, is decreased by using (A) Less water (B) Fine aggregates (C) Rich mix (D) More water and coarse aggregates

Description : Internal friction between the ingredients of concrete, is decreased by using (A) Less water (B) Fine aggregates (C) Rich mix (D) More water and coarse aggregates

Last Answer : Answer: Option D

For constructing a terrazzo floor, Pick up the incorrect statement from the following: (A) A base course is prepared as in cement concrete flooring (B) A 32 mm thick layer of cement concrete (1 : 2 : 4) is laid on the base course and the surface is made smooth by trowelling (C) Glass strips are driven into the layer according to the pattern required (D) After final grinding is over, oxalic acid mixed with water is spread over and rubbed hard with soft material

Description : For constructing a terrazzo floor, Pick up the incorrect statement from the following: (A) A base course is prepared as in cement concrete flooring (B) A 32 mm thick layer of cement concrete ... final grinding is over, oxalic acid mixed with water is spread over and rubbed hard with soft material

Last Answer : Answer: Option B

Batching error means inaccuracy in the quantity of (A) Aggregates (B) Cement (C) Water (D) All the above

Description : Batching error means inaccuracy in the quantity of (A) Aggregates (B) Cement (C) Water (D) All the above

Last Answer : Option D

Which of the following represents a carpet of sand-bitumen mix without coarse aggregates? (A) Mastic asphalt (B) Sheet asphalt (C) Bituminous carpet (D) Bituminous concrete

Description : Which of the following represents a carpet of sand-bitumen mix without coarse aggregates? (A) Mastic asphalt (B) Sheet asphalt (C) Bituminous carpet (D) Bituminous concrete

Last Answer : Answer: Option B

In the method of voids for determination of the quantity of cement paste, it is assumed that (A) Voids in coarse aggregates are filled by fine aggregates (B) Voids in fine aggregates are filled by the cement paste (C) Volume of fine aggregates is equal to total voids in coarse aggregates plus 10% extra (D) All the above

Description : In the method of voids for determination of the quantity of cement paste, it is assumed that (A) Voids in coarse aggregates are filled by fine aggregates (B) Voids in fine aggregates are filled by ... of fine aggregates is equal to total voids in coarse aggregates plus 10% extra (D) All the above

Last Answer : Answer: Option D

Concrete mainly consists of (A) Cement (B) Aggregates (C) Water (D) All the above

Description : Concrete mainly consists of (A) Cement (B) Aggregates (C) Water (D) All the above

Last Answer : Answer: Option D

The inert mineral material used for the manufacture of mortars and concrete is (a) Cement (b) Water (c) Aggregates (d) Admixture

Description : The inert mineral material used for the manufacture of mortars and concrete is (a) Cement (b) Water (c) Aggregates (d) Admixture

Last Answer : (c) Aggregates

Workability of concrete is inversely proportional to (A) Time of transit (B) water-cement ratio (C) The air in the mix (D) Size of aggregate

Description : Workability of concrete is inversely proportional to (A) Time of transit (B) water-cement ratio (C) The air in the mix (D) Size of aggregate

Last Answer : Answer: Option A

Shrinkage in concrete can be reduced by using (A) Low water cement ratio (B) Less cement in the concrete (C) Proper concrete mix (D) All the above

Description : Shrinkage in concrete can be reduced by using (A) Low water cement ratio (B) Less cement in the concrete (C) Proper concrete mix (D) All the above

Last Answer : Answer: Option D

The factors which effects the design of concrete mix is (a) Fineness modulus (b) Water cement ratio (c) Slump (d) All of these

Description : The factors which effects the design of concrete mix is (a) Fineness modulus (b) Water cement ratio (c) Slump (d) All of these

Last Answer : (d) All of these

An excess of flaky particles in concrete aggregates (A) Decreases the workability (B) Increases the quantity of water and sand (C) More than 15% are not desirable (D) All the above

Description : An excess of flaky particles in concrete aggregates (A) Decreases the workability (B) Increases the quantity of water and sand (C) More than 15% are not desirable (D) All the above

Last Answer : Answer: Option D

When each particle of aggregates is thinly coated with cement paste, a heterogeneous solid is formed, which is known as (A) Hydration (B) Gel (C) Concrete (D) None of these

Description : When each particle of aggregates is thinly coated with cement paste, a heterogeneous solid is formed, which is known as (A) Hydration (B) Gel (C) Concrete (D) None of these

Last Answer : Answer: Option C

For the construction of cement concrete dams, the maximum permissible size of the aggregates, is (A) 40 mm (B) 50 mm (C) 60 mm (D) 70 mm

Description : For the construction of cement concrete dams, the maximum permissible size of the aggregates, is (A) 40 mm (B) 50 mm (C) 60 mm (D) 70 mm

Last Answer : Answer: Option A

The ratio of differenct ingredients (cement, sand and aggregate) in concrete mix of grade M20 is. (a) 1:1:2 (b) 1:1.5:2 (c) 1:2:4 (d) 1:3:6

Description : The ratio of differenct ingredients (cement, sand and aggregate) in concrete mix of grade M20 is. (a) 1:1:2 (b) 1:1.5:2 (c) 1:2:4 (d) 1:3:6

Last Answer : (b) 1:1.5:2

Allowable shear strength of concrete, depends upon (A) Shear strength (B) Tensile strength (C) Compressive strength (D) None of these

Description : Allowable shear strength of concrete, depends upon (A) Shear strength (B) Tensile strength (C) Compressive strength (D) None of these

Last Answer : Answer: Option A