For an ordinary Portland cement (A) Residual does not exceed 10% when sieved through IS Sieve No. 9 (B) Soundness varies from 5 to 10 mm (C) Initial setting time is not less than 30 minutes (D) Compressive stress after 7 days, is not less than 175 kg/cm2

For an ordinary Portland cement
(A) Residual does not exceed 10% when sieved through IS Sieve No. 9
(B) Soundness varies from 5 to 10 mm
(C) Initial setting time is not less than 30 minutes
(D) Compressive stress after 7 days, is not less than 175 kg/cm2
by

1 Answer

Answer :

(C) Initial setting time is not less than 30 minutes
by

Related questions

According to IS Code , the requirement of an ordinary Portland cement is (a) The residue does not exceed 10% when sieved through is sieve no .9 (b) Its initial setting time is not less than 30 minutes. (c) its expansion is not morethan 10mm for unaerated cement (d) All the above.

Description : According to IS Code , the requirement of an ordinary Portland cement is (a) The residue does not exceed 10% when sieved through is sieve no .9 (b) Its initial setting time is not less than 30 minutes. (c) its expansion is not morethan 10mm for unaerated cement (d) All the above.

Last Answer : (d) All the above.

The initial setting time for ordinary Portland cement as per IS specifications should not be less than (A) 10 minutes (B) 30 minutes (C) 60 minutes (D) 600 minutes

Description : The initial setting time for ordinary Portland cement as per IS specifications should not be less than (A) 10 minutes (B) 30 minutes (C) 60 minutes (D) 600 minutes

Last Answer : Answer: Option B

According to IS specifications, the compressive strength of ordinary Portland cement after three days should not be less than (A) 7 MPa (B) 11.5 MPa (C) 16 MPa (D) 21 MPa

Description : According to IS specifications, the compressive strength of ordinary Portland cement after three days should not be less than (A) 7 MPa (B) 11.5 MPa (C) 16 MPa (D) 21 MPa

Last Answer : Answer: Option C

The compressive strength an ordinary Portland cement (1:3) after 7 days test should not be less than. (a) 11N/mm2 (b) 17.5 N/mm2 (c) 22 N/mm2 (d) 27.5N/m2

Description : The compressive strength an ordinary Portland cement (1:3) after 7 days test should not be less than. (a) 11N/mm2 (b) 17.5 N/mm2 (c) 22 N/mm2 (d) 27.5N/m2

Last Answer : (b) 17.5 N/mm2

An R.C.C. column of 30 cm diameter is reinforced with 6 bars 12 mm placed symmetrically along the circumference. If it carries a load of 40, 000 kg axially, the stress is (A) 49.9 kg/cm2 (B) 100 kg/cm2 (C) 250 kg/cm2 (D) 175 kg/cm

Description : An R.C.C. column of 30 cm diameter is reinforced with 6 bars 12 mm placed symmetrically along the circumference. If it carries a load of 40, 000 kg axially, the stress is (A) 49.9 kg/cm2 (B) 100 kg/cm2 (C) 250 kg/cm2 (D) 175 kg/cm

Last Answer : Answer: Option A

An ordinary Portland cement when tested for its fineness, should not leave any residue on I.S. sieve No. 9, more than (A) 5 % (B) 10 % (C) 15 % (D) 20 %

Description : An ordinary Portland cement when tested for its fineness, should not leave any residue on I.S. sieve No. 9, more than (A) 5 % (B) 10 % (C) 15 % (D) 20 %

Last Answer : (B) 10 %

As per IS specifications, the maximum final setting time for ordinary Portland cement should be (A) 30 minutes (B) 1 hour (C) 6 hours (D) 10 hour

Description : As per IS specifications, the maximum final setting time for ordinary Portland cement should be (A) 30 minutes (B) 1 hour (C) 6 hours (D) 10 hour

Last Answer : Answer: Option D

After the final grinding, the cement is sieved through IS sieve number (a) 9 (b) 12 (c) 24 (d) 48

Description : After the final grinding, the cement is sieved through IS sieve number (a) 9 (b) 12 (c) 24 (d) 48

Last Answer : (a) 9

Le Chatelier apparatus is used to determine which of the following properties for cement A) Soundness* b) Initial setting time c) Compressive strength d) Tensile strength

Description : Le Chatelier apparatus is used to determine which of the following properties for cement A) Soundness* b) Initial setting time c) Compressive strength d) Tensile strength

Last Answer : A) Soundness*

Minimum compressive strength of cement required at the age of 3 days for ordinary Portland cement of grade 33 is [ A ] 1.15 N/mm2 [ B ] 11.5 N/mm2 [ C ] 2.10 N/mm2 [ D ] 21 N/mm2

Description : Minimum compressive strength of cement required at the age of 3 days for ordinary Portland cement of grade 33 is [ A ] 1.15 N/mm2 [ B ] 11.5 N/mm2 [ C ] 2.10 N/mm2 [ D ] 21 N/mm2

Last Answer : [ B ] 11.5 N/mm2

If 20 kg of coarse aggregate is sieved through 80 mm, 40 mm, 20 mm, 10 mm, 4.75 mm, 2.36 mm, 1.18 mm, 600 micron, 300 micron and 150 micron standard sieves and the weights retained are 0 kg, 2 kg, 8 kg, 6 kg, 4 kg respectively, the fineness modulus of the aggregate, is (A) 7.30 (B) 7.35 (C) 7.40 (D) 7.45

Description : If 20 kg of coarse aggregate is sieved through 80 mm, 40 mm, 20 mm, 10 mm, 4.75 mm, 2.36 mm, 1.18 mm, 600 micron, 300 micron and 150 micron standard sieves and the weights retained are 0 kg, 2 kg, 8 kg, ... , the fineness modulus of the aggregate, is (A) 7.30 (B) 7.35 (C) 7.40 (D) 7.45

Last Answer : Answer: Option C

In fineness test on cement, residue left on I.S. sieve no.9 shall not exceed __________ by weight of the sample of cement [ A ] 5% [ B ] 10% [ C ] 15% [ D ] 20%

Description : In fineness test on cement, residue left on I.S. sieve no.9 shall not exceed __________ by weight of the sample of cement [ A ] 5% [ B ] 10% [ C ] 15% [ D ] 20%

Last Answer : [ B ] 10%

Which of the following cements is expected to have the highest compressive strength after 3 days (a) Ordinary Portland cement (b) Rapid hardening cement (c) High alumina cement (d) Sulphate resisting cement.

Description : Which of the following cements is expected to have the highest compressive strength after 3 days (a) Ordinary Portland cement (b) Rapid hardening cement (c) High alumina cement (d) Sulphate resisting cement.

Last Answer : (c) High alumina cement

As compared to ordinary Portland cement, high alumina cement has (A) Higher initial setting time but lower final setting time (B) Lower initial setting time but higher final setting time (C) Higher initial and final setting times (D) Lower initial and final setting times

Description : As compared to ordinary Portland cement, high alumina cement has (A) Higher initial setting time but lower final setting time (B) Lower initial setting time but higher final setting time (C) Higher initial and final setting times (D) Lower initial and final setting times

Last Answer : Answer: Option A

The compressive strength of cement should not be less than about 110Kg/cm2 after three days & not less than 170Kg/cm2 after seven days. The fineness of an ordinary cement as determined by turbidimetric method should be about __________ cm2 /gm. (A) 800 (B) 1600 (C) 4000 (D) 8500

Description : The compressive strength of cement should not be less than about 110Kg/cm2 after three days & not less than 170Kg/cm2 after seven days. The fineness of an ordinary cement as determined by turbidimetric method should be about __________ cm2 /gm. (A) 800 (B) 1600 (C) 4000 (D) 8500

Last Answer : (B) 1600

Le-Chatelier's device is used for determining the (A) Setting time of cement (B) Soundness of cement (C) Tensile strength of cement (D) Compressive strength of cement

Description : Le-Chatelier's device is used for determining the (A) Setting time of cement (B) Soundness of cement (C) Tensile strength of cement (D) Compressive strength of cement

Last Answer : Answer: Option B

Soundness test of cement determines (A) Quality of free lime (B) Ultimate strength (C) Durability (D) Initial setting

Description : Soundness test of cement determines (A) Quality of free lime (B) Ultimate strength (C) Durability (D) Initial setting

Last Answer : Answer: Option A

Ordinary Portland cement requires a specific surface of [ A ] 1250 cm2/gm [ B ] 2250 cm 2/gm [ C ] 3250 cm 2/gm [ D ] 3500 cm 2/gm

Description : Ordinary Portland cement requires a specific surface of [ A ] 1250 cm2/gm [ B ] 2250 cm 2/gm [ C ] 3250 cm 2/gm [ D ] 3500 cm 2/gm

Last Answer : [ B ] 2250 cm 2/gm

If the width of a pavement slab is 7.5 m, thickness 20 cm and working stress 1400 kg/cm2 , spacing of 10 mm tie bars for the longitudinal joint, is (A) 10 cm (B) 20 cm (C) 30 cm (D) 40 cm

Description : If the width of a pavement slab is 7.5 m, thickness 20 cm and working stress 1400 kg/cm2 , spacing of 10 mm tie bars for the longitudinal joint, is (A) 10 cm (B) 20 cm (C) 30 cm (D) 40 cm

Last Answer : Answer: Option C

Pick up the correct statement regarding low heat cement from the following: (A) It possesses less compressive strength (B) Its initial setting time is about one hour (C) Its final setting time is about 10 hours (D) All the above

Description : Pick up the correct statement regarding low heat cement from the following: (A) It possesses less compressive strength (B) Its initial setting time is about one hour (C) Its final setting time is about 10 hours (D) All the above

Last Answer : Answer: Option D

Initial setting time of cement for asbestos cement products should be not less than (A) 30 minutes (B) 50 minutes (C) 75 minutes (D) 90 minutes

Description : Initial setting time of cement for asbestos cement products should be not less than (A) 30 minutes (B) 50 minutes (C) 75 minutes (D) 90 minutes

Last Answer : Answer: Option D

(3) preventing rapid setting of cement Explanation: Portland cement clinker is a hydraulic material which shall consist of at least two-thirds by mass of calcium silicates, the remainder consisting of aluminium- and ironcontaining clinker phases and other compounds. The ratio of CaO to SiO2 shall not be less than 2.0. The magnesium oxide content (MgO) shall not exceed 5.0% by mass. Cement sets when mixed with water by way of a complex series of chemical reactions still only partly understood.

Description : (3) preventing rapid setting of cement Explanation: Portland cement clinker is a hydraulic material which shall consist of at least two-thirds by mass of calcium silicates, the remainder consisting of ... mixed with water by way of a complex series of chemical reactions still only partly understood.

Last Answer : Milk is a colloidal system in which: (1) Water is dispersed in fat (2) Fat is dispersed in water (3) Fat and water are dispersed in each other (4) Fat is dissolved

For Ordinary Portland cement concrete exposed to dry and hot weather conditions, good moist curing period is [ A ] 7 days [ B ] 10 days [ C ] 14 days [ D ] None of the above

Description : For Ordinary Portland cement concrete exposed to dry and hot weather conditions, good moist curing period is [ A ] 7 days [ B ] 10 days [ C ] 14 days [ D ] None of the above

Last Answer : [ B ] 10 days

A short column 20 cm × 20 cm in section is reinforced with 4 bars whose area of cross section is 20 sq. cm. If permissible compressive stresses in concrete and steel are 40 kg/cm2 and 300 kg/cm2 , the Safe load on the column, should not exceed (A) 4120 kg (B) 41,200 kg (C) 412,000 kg (D) None of these

Description : A short column 20 cm 20 cm in section is reinforced with 4 bars whose area of cross section is 20 sq. cm. If permissible compressive stresses in concrete and steel are 40 kg/cm2 and 300 kg/cm2 , the Safe load on ... should not exceed (A) 4120 kg (B) 41,200 kg (C) 412,000 kg (D) None of these

Last Answer : Answer: Option B

Newly constructed pavement with ordinary Portland cement attains its working strength after (A) 7 days (B) 14 days (C) 21 days (D) 28 days

Description : Newly constructed pavement with ordinary Portland cement attains its working strength after (A) 7 days (B) 14 days (C) 21 days (D) 28 days

Last Answer : Answer: Option D

A short, hollow cast iron cylinder with a wall thickness of 1 cm is to carry a compressive load of 10 tonnes. If the working stress in compression is 800 kg/cm2, the outside diameter of the cylinder should not be less than a) 0.5cm b) 5 cm c) 2.5cm d) 4.5 cm

Description : A short, hollow cast iron cylinder with a wall thickness of 1 cm is to carry a compressive load of 10 tonnes. If the working stress in compression is 800 kg/cm2, the outside diameter of the cylinder should not be less than a) 0.5cm b) 5 cm c) 2.5cm d) 4.5 cm

Last Answer : b) 5 cm

In a combined footing if shear stress does not exceed 5 kg/cm2 , the nominal stirrups provided are (A) 6 legged (B) 8 legged (C) 10 legged (D) 12 legged

Description : In a combined footing if shear stress does not exceed 5 kg/cm2 , the nominal stirrups provided are (A) 6 legged (B) 8 legged (C) 10 legged (D) 12 legged

Last Answer : Answer: Option B

Soundness of cement is tested by (A) Vicat's apparatus (B) Le-chatelier apparatus (C) Compressive strength testing apparatus (D) None of these

Description : Soundness of cement is tested by (A) Vicat's apparatus (B) Le-chatelier apparatus (C) Compressive strength testing apparatus (D) None of these

Last Answer : Answer: Option B

The maximum compressive stress at the top of a beam is 1600 kg/cm2 and the corresponding tensile stress at its bottom is 400 kg/cm2 . If the depth of the beam is 10 cm, the neutral axis from the top, is(A) 2 cm (B) 4 cm (C) 6 cm (D) 8 cm

Description : The maximum compressive stress at the top of a beam is 1600 kg/cm2 and the corresponding tensile stress at its bottom is 400 kg/cm2 . If the depth of the beam is 10 cm, the neutral axis from the top, is (A) 2 cm (B) 4 cm (C) 6 cm (D) 8 cm

Last Answer : (D) 8 cm

The section modulus of a rectangular light beam 25 metres long is 12.500 cm3 . The beam is simply supported at its ends and carries a longitudinal axial tensile load of 10 tonnes in addition to a point load of 4 tonnes at the centre. The maximum stress in the bottom most fibre at the mid span section, is (A) 13.33 kg/cm2 tensile (B) 13.33 kg/cm2 compressive (C) 26.67 kg/cm2 tensile (D) 26.67 kg/cm2 compressive

Description : The section modulus of a rectangular light beam 25 metres long is 12.500 cm3 . The beam is simply supported at its ends and carries a longitudinal axial tensile load of 10 tonnes in addition to a point load of ... 13.33 kg/cm2 compressive (C) 26.67 kg/cm2 tensile (D) 26.67 kg/cm2 compressive

Last Answer : (C) 26.67 kg/cm2 tensile

The normal consistency of ordinary Portland cement is about (A) 10 % (B) 20 % (C) 30 % (D) 40 %

Description : The normal consistency of ordinary Portland cement is about (A) 10 % (B) 20 % (C) 30 % (D) 40 %

Last Answer : Answer: Option C

If a steel rod of 20 mm diameter and 5 metres long elongates by 2.275 mm when subjected to an axial pull of 3000 kg, the stress developed, is (A) 9.5541 kg/cm2 (B) 95.541 kg/cm2 (C) 955.41 kg/cm2 (D) 9554.1 kg/cm

Description : If a steel rod of 20 mm diameter and 5 metres long elongates by 2.275 mm when subjected to an  axial pull of 3000 kg, the stress developed, is  (A) 9.5541 kg/cm2 (B) 95.541 kg/cm2 (C) 955.41 kg/cm2 (D) 9554.1 kg/cm

Last Answer : (C) 955.41 kg/cm2

If a steel rod of 20 mm diameter and 5 metres long elongates by 2.275 mm when subjected to an axial pull of 3000 kg, the stress developed, is (A) 9.5541 kg/cm2 (B) 95.541 kg/cm2 (C) 955.41 kg/cm2 (D) 9554.1 kg/cm

Description : If a steel rod of 20 mm diameter and 5 metres long elongates by 2.275 mm when subjected to an  axial pull of 3000 kg, the stress developed, is  (A) 9.5541 kg/cm2 (B) 95.541 kg/cm2 (C) 955.41 kg/cm2 (D) 9554.1 kg/cm

Last Answer : (C) 955.41 kg/cm2

Pick up the incorrect statement from the following: (A) The degree of grinding of cement, is called fineness (B) The process of changing cement paste into hard mass, is known as setting of cement (C) The phenomenon by virtue of which cement does not allow transmission of sound, is known as soundness of cement (D) The heat generated during chemical reaction of cement with water, is known as heat of hydration

Description : Pick up the incorrect statement from the following: (A) The degree of grinding of cement, is called fineness (B) The process of changing cement paste into hard mass, is known as setting of ... (D) The heat generated during chemical reaction of cement with water, is known as heat of hydration

Last Answer : Answer: Option C

Minimum number of 50 kg cement bags per cubic metre of concrete for a mix corresponding to crushing strength 280 kg/cm2 at 28 days, are (A) 5.0 (B) 6.5(C) 7.0 (D) 7.5

Description : Minimum number of 50 kg cement bags per cubic metre of concrete for a mix corresponding to crushing strength 280 kg/cm2 at 28 days, are (A) 5.0 (B) 6.5 (C) 7.0 (D) 7.5

Last Answer : Answer: Option B

Pick out the wrong statement. (A) High early strength cement are made from materials having high silica to lime ratio (B) The function of gypsum in cement is to enhance its initial setting rate (C) Acid resistant cements are known as silicate cement (D) Major component of greyish Portland cement is tricalcium silicate

Description : Pick out the wrong statement. (A) High early strength cement are made from materials having high silica to lime ratio (B) The function of gypsum in cement is to enhance its initial ... cements are known as silicate cement (D) Major component of greyish Portland cement is tricalcium silicate

Last Answer : (A) High early strength cement are made from materials having high silica to lime ratio

If aggregates completely pass through a sieve of size 75 mm and are retained on a sieve of size 60 mm, the particular aggregate will be flaky if its minimum dimension is less than (A) 20.5 mm (B) 30.5 mm (C) 40.5 mm (D) 50.5 mm

Description : If aggregates completely pass through a sieve of size 75 mm and are retained on a sieve of size 60 mm, the particular aggregate will be flaky if its minimum dimension is less than (A) 20.5 mm (B) 30.5 mm (C) 40.5 mm (D) 50.5 mm

Last Answer : Answer: Option C

The allowable tensile stress in mild steel stirrups, reinforced cement concrete, is(A) 1400 kg/cm2(B) 190 kg/cm2(C) 260 kg/cm2(D) 230 kg/cm

Description : The allowable tensile stress in mild steel stirrups, reinforced cement concrete, is (A) 1400 kg/cm2 (B) 190 kg/cm2 (C) 260 kg/cm2 (D) 230 kg/cm

Last Answer : Answer: Option A

In Portland Blast furnace slag cement, the blast furnace slag content shall not exceed [ A ] 50% [ B ] 65% [ C ] 80% [ D ] 90%

Description : In Portland Blast furnace slag cement, the blast furnace slag content shall not exceed [ A ] 50% [ B ] 65% [ C ] 80% [ D ] 90%

Last Answer : [ B ] 65%

The preliminary test is repeated if the difference of compressive strength of three test specimens, exceeds (A) 5 kg/cm2 (B) 8 kg/cm2 (C) 10 kg/cm2 (D) 15 kg/cm2

Description : The preliminary test is repeated if the difference of compressive strength of three test specimens, exceeds (A) 5 kg/cm2 (B) 8 kg/cm2 (C) 10 kg/cm2 (D) 15 kg/cm2

Last Answer : Answer: Option D

If the average compressive strength is 4000 kg/cm2 and standard deviation is 500, the co-efficient of variation is (A) 10 % (B) 12.5 % (C) 15 % (D) 18.5%

Description : If the average compressive strength is 4000 kg/cm2 and standard deviation is 500, the co-efficient of variation is (A) 10 % (B) 12.5 % (C) 15 % (D) 18.5%

Last Answer : Answer: Option B

The sum of the percentage of tricalcium silicate and dicalcium silicate for Portland cement varies from. (a) 50 to 60% (b) 60 to 70% (c) 70 to 80% (d) 80 to 90%

Description : The sum of the percentage of tricalcium silicate and dicalcium silicate for Portland cement varies from. (a) 50 to 60% (b) 60 to 70% (c) 70 to 80% (d) 80 to 90%

Last Answer : (c) 70 to 80%

The difference in the reservoir level and the lowest point of the water mains is 180 m. The expected pressure due to water hammer is 7.5 kg/cm2 in a pressure conduit of diameter 1 m. Assuming the efficiency of the riveted joints of the pipe as 0.6 and minimum cover 3 mm for corrosion, the thickness of the pipe materials, is (A) 10 mm (B) 15 mm (C) 20 mm (D) 25 mm

Description : The difference in the reservoir level and the lowest point of the water mains is 180 m. The  expected pressure due to water hammer is 7.5 kg/cm2  in a pressure conduit of diameter 1 m.  Assuming the efficiency of the ... , is  (A) 10 mm  (B) 15 mm  (C) 20 mm  (D) 25 mm 

Last Answer : (C) 20 mm

The cement whose strength is a little lower than the ordinary cement during the first three months but attains afterwards the same strength, is known as (A) Low-heat Portland cement (B) Rapid hardening Portland cement (C) Portland blast slag cement (D) Portland pozzolana cement

Description : The cement whose strength is a little lower than the ordinary cement during the first three months but attains afterwards the same strength, is known as (A) Low-heat Portland cement (B) Rapid hardening Portland cement (C) Portland blast slag cement (D) Portland pozzolana cement

Last Answer : Answer: Option A

Low heat cement contains more amount of __________ than that of ordinary Portland cement [ A ] C3S [ B ] C2S [ C ] C3A [ D ] None of the above

Description : Low heat cement contains more amount of __________ than that of ordinary Portland cement [ A ] C3S [ B ] C2S [ C ] C3A [ D ] None of the above

Last Answer : [ B ] C2S

A rectangular beam 20 cm wide is subjected to a maximum shearing force of 10,000 kg, the corresponding maximum shearing stress being 30 kg/cm2 . The depth of the beam is (A) 15 cm (B) 20 cm (C) 25 cm (D) 30 cm

Description : A rectangular beam 20 cm wide is subjected to a maximum shearing force of 10,000 kg, the corresponding maximum shearing stress being 30 kg/cm2 . The depth of the beam is (A) 15 cm (B) 20 cm (C) 25 cm (D) 30 cm

Last Answer : (C) 25 cm

If the shear stress in a R.C.C. beam is (A) Equal or less than 5 kg/cm2 , no shear reinforcement is provided (B) Greater than 4 kg/cm2 , but less than 20 kg/cm2 , shear reinforcement is provided (C) Greater than 20 kg/cm2 , the size of the section is changed (D) All the above

Description : If the shear stress in a R.C.C. beam is (A) Equal or less than 5 kg/cm2 , no shear reinforcement is provided (B) Greater than 4 kg/cm2 , but less than 20 kg/cm2 , shear reinforcement is provided (C) Greater than 20 kg/cm2 , the size of the section is changed (D) All the above

Last Answer : Answer: Option D

Ordinary Portland cement is manufactured from (A) Lime stone and clay (B) Gypsum and lime (C) Pozzolana (D) Lime, pozzolana and clay

Description : Ordinary Portland cement is manufactured from (A) Lime stone and clay (B) Gypsum and lime (C) Pozzolana (D) Lime, pozzolana and clay

Last Answer : Answer: Option B

You are asked to construct a massive dam, the type of cement you will use, is (A) Ordinary Portland cement (B) Rapid hardening cement (C) Low heat cement (D) Blast furnace slag cement

Description : You are asked to construct a massive dam, the type of cement you will use, is (A) Ordinary Portland cement (B) Rapid hardening cement (C) Low heat cement (D) Blast furnace slag cement

Last Answer : Answer: Option C

As compared to ordinary Portland cement, use of pozzolana cement (A) Reduces workability (B) Increases bleeding (C) Increases shrinkage (D) Increases strength

Description : As compared to ordinary Portland cement, use of pozzolana cement (A) Reduces workability (B) Increases bleeding (C) Increases shrinkage (D) Increases strength

Last Answer : Answer: Option C