Description : Minimum compressive strength of cement required at the age of 3 days for ordinary Portland cement of grade 33 is [ A ] 1.15 N/mm2 [ B ] 11.5 N/mm2 [ C ] 2.10 N/mm2 [ D ] 21 N/mm2
Last Answer : [ B ] 11.5 N/mm2
Description : According to IS specifications, the compressive strength of ordinary Portland cement after three days should not be less than (A) 7 MPa (B) 11.5 MPa (C) 16 MPa (D) 21 MPa
Last Answer : Answer: Option C
Description : For an ordinary Portland cement (A) Residual does not exceed 10% when sieved through IS Sieve No. 9 (B) Soundness varies from 5 to 10 mm (C) Initial setting time is not less than 30 minutes (D) Compressive stress after 7 days, is not less than 175 kg/cm2
Last Answer : (C) Initial setting time is not less than 30 minutes
Description : Which of the following cements is expected to have the highest compressive strength after 3 days (a) Ordinary Portland cement (b) Rapid hardening cement (c) High alumina cement (d) Sulphate resisting cement.
Last Answer : (c) High alumina cement
Description : Newly constructed pavement with ordinary Portland cement attains its working strength after (A) 7 days (B) 14 days (C) 21 days (D) 28 days
Last Answer : Answer: Option D
Description : A muff coupling is connecting two shafts. The torque involved is 650N-m. The shaft diameter is 45mm with length and height of the key being 14mm and 80mm respectively. Find the compressive stress induced in the key. a) 70.1 N/mm2 b) 51.6N/mm2 c) 45.5N/mm2 d) None of the listed
Last Answer : b) 51.6N/mm2
Description : The compressive strength of cement should not be less than about 110Kg/cm2 after three days & not less than 170Kg/cm2 after seven days. The fineness of an ordinary cement as determined by turbidimetric method should be about __________ cm2 /gm. (A) 800 (B) 1600 (C) 4000 (D) 8500
Last Answer : (B) 1600
Description : For lime concrete, (A) Slump is 50 to 75 mm (B) Flexural strength at 90 days is 0.2 N/mm2 (C) Compressive strength at 90 days is 1.5 N/mm2 (D) All the above
Description : For Ordinary Portland cement concrete exposed to dry and hot weather conditions, good moist curing period is [ A ] 7 days [ B ] 10 days [ C ] 14 days [ D ] None of the above
Last Answer : [ B ] 10 days
Description : The cement whose strength is a little lower than the ordinary cement during the first three months but attains afterwards the same strength, is known as (A) Low-heat Portland cement (B) Rapid hardening Portland cement (C) Portland blast slag cement (D) Portland pozzolana cement
Last Answer : Answer: Option A
Description : As compared to ordinary Portland cement, use of pozzolana cement (A) Reduces workability (B) Increases bleeding (C) Increases shrinkage (D) Increases strength
Description : The initial setting time for ordinary Portland cement as per IS specifications should not be less than (A) 10 minutes (B) 30 minutes (C) 60 minutes (D) 600 minutes
Last Answer : Answer: Option B
Description : According to IS Code , the requirement of an ordinary Portland cement is (a) The residue does not exceed 10% when sieved through is sieve no .9 (b) Its initial setting time is not less than 30 minutes. (c) its expansion is not morethan 10mm for unaerated cement (d) All the above.
Last Answer : (d) All the above.
Description : As per IS: 456, permissible direct compressive stress M20 grade concrete in working stress method of designer [ A ] 5.0 N/mm2 [ B ] 7.0 N/mm2 [ C ] 10.0 N/mm2 [ D ] 20.0 N/mm2
Last Answer : [ A ] 5.0 N/mm2
Description : In working stress method of design, permissible compressive bending stress for M20 grade concrete is given by [ A ] 5.0 N/mm2 [ B ] 7.0 N/mm2 [ C ] 10.0 N/mm2 [ D ] 20 N/mm2
Last Answer : [ B ] 7.0 N/mm2
Description : The effective depth of a singly reinforced rectangular beam is 300mm. the section is over-reinforced and the neutral axis is 120mm below the top. If the maximum stress attained by concrete is 5N/mn2 and the modular ratio ... in the steel will (a) 130N/mm2 (b) 135N/mm2 (c) 160N/mm2 (d) 180N/mm2
Last Answer : (b) 135N/mm2
Description : For performing the compressive strength test of cement, the size of cube mould should be (a) 7.06cm (b)75mm (c)80mm (d)All the above
Last Answer : (a) 7.06cm
Description : A beam of uniform rectangular section 200 mm wide and 300mm deep is simply supported at its ends.It carries a uniformly distributed load of 9KN/m run over the entire span of 5m.If E=1×104 N/mm2, what is the maximum deflection? a.14.26 mm b.17.28 mm c.18.53 mm d.16.27 mm.
Last Answer : d.16.27 mm.
Description : An ordinary Portland cement when tested for its fineness, should not leave any residue on I.S. sieve No. 9, more than (A) 5 % (B) 10 % (C) 15 % (D) 20 %
Last Answer : (B) 10 %
Description : Low heat cement contains more amount of __________ than that of ordinary Portland cement [ A ] C3S [ B ] C2S [ C ] C3A [ D ] None of the above
Last Answer : [ B ] C2S
Description : For quality control of Portland cement, the test essentially done is (A) Setting time (B) Tensile strength (C) Consistency (D) All the above
Last Answer : D
Description : Stress may be expressed in Newtons (A) Per millimetre square (N/mm2 ) (B) Per centimetre square (N/cm2 ) (C) Per metre square (N/m2 ) (D) None of these
Last Answer : (A) Per millimetre square (N/mm2 )
Description : The pressure measured with the help of a Piezometer tube is in (A) N/mm2 (B) N/m2 (C) Head of liquid (D) All of these
Description : Ordinary Portland cement is manufactured from (A) Lime stone and clay (B) Gypsum and lime (C) Pozzolana (D) Lime, pozzolana and clay
Description : You are asked to construct a massive dam, the type of cement you will use, is (A) Ordinary Portland cement (B) Rapid hardening cement (C) Low heat cement (D) Blast furnace slag cement
Description : As compared to ordinary Portland cement, high alumina cement has (A) Higher initial setting time but lower final setting time (B) Lower initial setting time but higher final setting time (C) Higher initial and final setting times (D) Lower initial and final setting times
Description : For the construction of thin R.C.C. structures, the type of cement to be avoided, is (A) Ordinary Portland cement (B) Rapid hardening cement (C) Low heat cement (D) Blast furnace slag cement
Description : For road pavements, the cement generally used, is (A) Ordinary Portland cement (B) Rapid hardening cement (C) Low heat cement (D) Blast furnace slag cement
Description : The normal consistency of ordinary Portland cement is about (A) 10 % (B) 20 % (C) 30 % (D) 40 %
Description : Addition of pozzolana to ordinary Portland cement increases (A) Bleeding (B) Shrinkage (C) Permeability (D) Heat of hydration
Description : Which of the following cements is suitable for use in massive concrete structures such as large dams? (A) Ordinary Portland cement (B) Low heat cement (C) Rapid hardening cement (D) Sulphate resisting cement
Description : As per IS specifications, the maximum final setting time for ordinary Portland cement should be (A) 30 minutes (B) 1 hour (C) 6 hours (D) 10 hour
Description : Which of the following cements contains maximum percentage of dicalcium silicate? (A) Ordinary Portland cement (B) Low heat cement (C) Rapid hardening cement (D) Sulphate resisting cement
Description : Chief constituent of ordinary Portland cement is [ A ] Lime [ B ] Alumina [ C ] Magnesia [ D ] Iron oxide
Last Answer : [ A ] Lime
Description : For mass concrete work, the type of cement preferable is [ A ] Ordinary Portland cement [ B ] Rapid hardening cement [ C ] Low heat cement [ D ] Blast furnace slag cement
Last Answer : [ C ] Low heat cement
Description : For road pavements, the cement generally used, is [ A ] Ordinary Portland cement [ B ] Rapid hardening cement [ C ] Low heat cement [ D ] Blast furnace slag cement
Last Answer : [ A ] Ordinary Portland cement
Description : Ordinary Portland cement requires a specific surface of [ A ] 1250 cm2/gm [ B ] 2250 cm 2/gm [ C ] 3250 cm 2/gm [ D ] 3500 cm 2/gm
Last Answer : [ B ] 2250 cm 2/gm
Description : When compared to ordinary Portland cement, Rapid hardening Portland cement contains ______________ amount of lime content [ A ] Equal [ B ] Greater [ C ] Lesser [ D ] Zero
Last Answer : [ B ] Greater
Description : A compound bar consists of two bars of equal length. Steel bar cross-section is 3500 mm2 and that of brass bar is 3000 mm2 . These are subjected to a compressive load 100,000 N. If Eb = 0.2 MN/mm2 and Eb = 0.1 ... 6 N/mm2 s = 12 N/mm2 (D) b = 5 N/mm2 s = 10 N/mm
Last Answer : (A) b = 10 N/mm2 s = 20 N/mm
Description : A spring of mean radius 40 mm contains 8 action coils of steel (N = 80000 N/mm2 ), 4 mm in diameter. The clearance between the coils being 1 mm when unloaded, the minimum compressive load to remove the clearance, is (A) 25 N (B) 30 N (C) 35 N (D) 40 N
Last Answer : (C) 35 N
Description : For determining the compressive strength test on cement is, the percentage amount of water to be added as (Pa = Percentage of water for required consistency) [ A ] 0.25 Pa + 2.5 [ B ] 0.25 Pa + 3.5 [ C ] 0.35 Pa + 2.5 [ D ] 0.35 Pa + 3.5
Last Answer : [ B ] 0.25 Pa + 3.5
Description : Pick up the incorrect statement from the following. For performing compressive strength test of cement (A) Cement and standard sand mortar are used in the ratio of 1 : 3 (B) Water is added at the ... cm 10 cm is used (D) The prepared moulds are kept in a atmosphere of 50% relative humidity
Description : Pick up the correct statement regarding low heat cement from the following: (A) It possesses less compressive strength (B) Its initial setting time is about one hour (C) Its final setting time is about 10 hours (D) All the above
Description : The proportion of lime, silica, alumina and iron oxide in a Portland cement is (a) 63:22:6:3 (b) 63:22:3:6 (c) 22:63:6:3 (d) All the above
Last Answer : (a) 63:22:6:3
Description : The compound of Portland cement which contributes to the strength after two to three years is (A) Tri-calcium silicate (B) Di-calcium silicate (C) Tri-calcium aluminate (D) Tetra-calcium alumino ferrite
Description : Pick up the correct statement from the following: (A) A soil having pH value more than 7 is an acidic soil (B) A soil having pH value less than 7 is an acidic soil (C) A soil ... more than 7 is an alkaline soil (D) A soil containing chemicals for the manufacture of Portland cement is preferred
Description : Formation of ordinary Portland cement?
Last Answer : Ordinary Portland cement is form from materials of limestone or chalk and clay in proportion of 78and 22% respectively. The limestone and the clay are crushed and water is added to form slurry. The ... powder and a range of gypsum is added which generate setting or hardening when water is added.
Description : List four major compounds of cement with their percentage in ordinary Portland cement.
Last Answer : List four major compounds of cement with their percentage in ordinary Portland cement.
Description : The strength of brick masonry in 1:6 cement mortar, is (A) 20 tonnes/m2 (B) 40 tonnes/m2 (C) 50 tonnes/m2 (D) 60 tonnes/m
Description : Under normal conditions using an ordinary cement, the period of removal of the form work, is: (A) 7 days for beam soffits (B) 14 days for bottom slabs of spans 4.6 m and more (C) 21 days for bottom beams over 6 m spans (D) All the above