Description : According to IS specifications, the compressive strength of ordinary Portland cement after three days should not be less than (A) 7 MPa (B) 11.5 MPa (C) 16 MPa (D) 21 MPa
Last Answer : Answer: Option C
Description : The cement whose strength is a little lower than the ordinary cement during the first three months but attains afterwards the same strength, is known as (A) Low-heat Portland cement (B) Rapid hardening Portland cement (C) Portland blast slag cement (D) Portland pozzolana cement
Last Answer : Answer: Option A
Description : Minimum compressive strength of cement required at the age of 3 days for ordinary Portland cement of grade 33 is [ A ] 1.15 N/mm2 [ B ] 11.5 N/mm2 [ C ] 2.10 N/mm2 [ D ] 21 N/mm2
Last Answer : [ B ] 11.5 N/mm2
Description : The compressive strength an ordinary Portland cement (1:3) after 7 days test should not be less than. (a) 11N/mm2 (b) 17.5 N/mm2 (c) 22 N/mm2 (d) 27.5N/m2
Last Answer : (b) 17.5 N/mm2
Description : In ideal pavement is constructed with (A) Bricks (B) Hard soil (C) Portland cement concrete (D) Tar
Description : For Ordinary Portland cement concrete exposed to dry and hot weather conditions, good moist curing period is [ A ] 7 days [ B ] 10 days [ C ] 14 days [ D ] None of the above
Last Answer : [ B ] 10 days
Description : Which of the following cements is expected to have the highest compressive strength after 3 days (a) Ordinary Portland cement (b) Rapid hardening cement (c) High alumina cement (d) Sulphate resisting cement.
Last Answer : (c) High alumina cement
Description : Under normal conditions using an ordinary cement, the period of removal of the form work, is: (A) 7 days for beam soffits (B) 14 days for bottom slabs of spans 4.6 m and more (C) 21 days for bottom beams over 6 m spans (D) All the above
Last Answer : Answer: Option D
Description : For an ordinary Portland cement (A) Residual does not exceed 10% when sieved through IS Sieve No. 9 (B) Soundness varies from 5 to 10 mm (C) Initial setting time is not less than 30 minutes (D) Compressive stress after 7 days, is not less than 175 kg/cm2
Last Answer : (C) Initial setting time is not less than 30 minutes
Description : In favourable circumstances a 15 cm concrete cube after 28 days, attains a maximum crushing strength (A) 100 kg/cm2 (B) 200 kg/cm2 (C) 300 kg/cm2 (D) 400 kg/cm
Description : How long will it take for the concrete to achieve 100% of its strength? (A) 7 days (B) 14 days (C) 21 days (D) 28 day
Description : As compared to ordinary Portland cement, use of pozzolana cement (A) Reduces workability (B) Increases bleeding (C) Increases shrinkage (D) Increases strength
Description : At 28 days of curing concrete attains a strength of [ A ] 20 to 25% [ B ] 60 to 70% [ C ] 65 to 80% [ D ] 90 to 95%
Last Answer : [ D ] 90 to 95%
Description : Pavement is said to be flexible if it contains (A) Water bound macadam surface (B) Stabilised soil base constructed of lime cement or tar (C) Bitumen-bound stone layer of varying aggregates (D) All the above
Description : Rapid hardening cement attains early strength due to (A) Larger proportion of lime grounded finer than normal cement (B) Lesser proportion of lime grounded coarser than normal cement (C) Lesser proportion of lime grounded finer than normal cement (D) Excess percentage of gypsum
Description : Specified compressive strength of concrete is obtained from cube tests at the end of (A) 3 days (B) 7 days (C) 21 days (D) 28 day
Description : An ordinary Portland cement when tested for its fineness, should not leave any residue on I.S. sieve No. 9, more than (A) 5 % (B) 10 % (C) 15 % (D) 20 %
Last Answer : (B) 10 %
Description : According to IS Code , the requirement of an ordinary Portland cement is (a) The residue does not exceed 10% when sieved through is sieve no .9 (b) Its initial setting time is not less than 30 minutes. (c) its expansion is not morethan 10mm for unaerated cement (d) All the above.
Last Answer : (d) All the above.
Description : Minimum number of 50 kg cement bags per cubic metre of concrete for a mix corresponding to crushing strength 280 kg/cm2 at 28 days, are (A) 5.0 (B) 6.5 (C) 7.0 (D) 7.5
Last Answer : Answer: Option B
Description : Ordinary Portland cement is manufactured from (A) Lime stone and clay (B) Gypsum and lime (C) Pozzolana (D) Lime, pozzolana and clay
Description : You are asked to construct a massive dam, the type of cement you will use, is (A) Ordinary Portland cement (B) Rapid hardening cement (C) Low heat cement (D) Blast furnace slag cement
Description : As compared to ordinary Portland cement, high alumina cement has (A) Higher initial setting time but lower final setting time (B) Lower initial setting time but higher final setting time (C) Higher initial and final setting times (D) Lower initial and final setting times
Description : For the construction of thin R.C.C. structures, the type of cement to be avoided, is (A) Ordinary Portland cement (B) Rapid hardening cement (C) Low heat cement (D) Blast furnace slag cement
Description : For road pavements, the cement generally used, is (A) Ordinary Portland cement (B) Rapid hardening cement (C) Low heat cement (D) Blast furnace slag cement
Description : The normal consistency of ordinary Portland cement is about (A) 10 % (B) 20 % (C) 30 % (D) 40 %
Description : Addition of pozzolana to ordinary Portland cement increases (A) Bleeding (B) Shrinkage (C) Permeability (D) Heat of hydration
Description : Which of the following cements is suitable for use in massive concrete structures such as large dams? (A) Ordinary Portland cement (B) Low heat cement (C) Rapid hardening cement (D) Sulphate resisting cement
Description : As per IS specifications, the maximum final setting time for ordinary Portland cement should be (A) 30 minutes (B) 1 hour (C) 6 hours (D) 10 hour
Description : The initial setting time for ordinary Portland cement as per IS specifications should not be less than (A) 10 minutes (B) 30 minutes (C) 60 minutes (D) 600 minutes
Description : Which of the following cements contains maximum percentage of dicalcium silicate? (A) Ordinary Portland cement (B) Low heat cement (C) Rapid hardening cement (D) Sulphate resisting cement
Description : Chief constituent of ordinary Portland cement is [ A ] Lime [ B ] Alumina [ C ] Magnesia [ D ] Iron oxide
Last Answer : [ A ] Lime
Description : For mass concrete work, the type of cement preferable is [ A ] Ordinary Portland cement [ B ] Rapid hardening cement [ C ] Low heat cement [ D ] Blast furnace slag cement
Last Answer : [ C ] Low heat cement
Description : For road pavements, the cement generally used, is [ A ] Ordinary Portland cement [ B ] Rapid hardening cement [ C ] Low heat cement [ D ] Blast furnace slag cement
Last Answer : [ A ] Ordinary Portland cement
Description : Ordinary Portland cement requires a specific surface of [ A ] 1250 cm2/gm [ B ] 2250 cm 2/gm [ C ] 3250 cm 2/gm [ D ] 3500 cm 2/gm
Last Answer : [ B ] 2250 cm 2/gm
Description : Low heat cement contains more amount of __________ than that of ordinary Portland cement [ A ] C3S [ B ] C2S [ C ] C3A [ D ] None of the above
Last Answer : [ B ] C2S
Description : When compared to ordinary Portland cement, Rapid hardening Portland cement contains ______________ amount of lime content [ A ] Equal [ B ] Greater [ C ] Lesser [ D ] Zero
Last Answer : [ B ] Greater
Description : The compound of Portland cement which contributes to the strength after two to three years is (A) Tri-calcium silicate (B) Di-calcium silicate (C) Tri-calcium aluminate (D) Tetra-calcium alumino ferrite
Description : For quality control of Portland cement, the test essentially done is (A) Setting time (B) Tensile strength (C) Consistency (D) All the above
Last Answer : D
Description : The compressive strength of cement should not be less than about 110Kg/cm2 after three days & not less than 170Kg/cm2 after seven days. The fineness of an ordinary cement as determined by turbidimetric method should be about __________ cm2 /gm. (A) 800 (B) 1600 (C) 4000 (D) 8500
Last Answer : (B) 1600
Description : Formation of ordinary Portland cement?
Last Answer : Ordinary Portland cement is form from materials of limestone or chalk and clay in proportion of 78and 22% respectively. The limestone and the clay are crushed and water is added to form slurry. The ... powder and a range of gypsum is added which generate setting or hardening when water is added.
Description : List four major compounds of cement with their percentage in ordinary Portland cement.
Last Answer : List four major compounds of cement with their percentage in ordinary Portland cement.
Description : Water required per bag of cement, is (A) 7 kg (B) 14 kg (C) 21 kg (D) 35 kg
Last Answer : (D) 35 kg
Description : Following type of pavement is generally known as flexible pavement (A) Water-bound macadam roads (B) Stabilised soil roads (C) Road constructed with various layers of building material well compacted (D) All the above
Description : Addition of pozzolana to ordinary port land cement, causes (A) Decrease in early strength (B) Reduction in chemical action with sulphates (C) Increase in shrinkage (D) All the above
Description : The approximate ratio between the strength of cement concrete at seven days and 28 days is a) 3/ 4 b) 2/3* c) 1/2 d) 1/3
Last Answer : b) 2/3*
Description : Pick out the wrong statement. (A) High early strength cement are made from materials having high silica to lime ratio (B) The function of gypsum in cement is to enhance its initial ... cements are known as silicate cement (D) Major component of greyish Portland cement is tricalcium silicate
Last Answer : (A) High early strength cement are made from materials having high silica to lime ratio
Description : Pick up the correct statement from the following: (A) A soil having pH value more than 7 is an acidic soil (B) A soil having pH value less than 7 is an acidic soil (C) A soil ... more than 7 is an alkaline soil (D) A soil containing chemicals for the manufacture of Portland cement is preferred
Description : The form Work including the props can be removed from beams, only after (A) 3 day (B) 7 days (C) 14 days (D) 21 days
Description : The addition of gypsum to portland cement helps in : (1) increasing the strength of cement (2) rapid setting of cement (3) preventing rapid setting of cement (4) reduction in the cost of cement
Last Answer : preventing rapid setting of cement
Description : When a cohesionless soil attains quick condition, it looses (A) Shear strength (B) Bearing capacity (C) Both (a) and (b) (D) Neither (a) nor (6