Coarse grained steels have (A) Low toughness (B) No tendency to distort (C) High density (D) Very high toughness

Coarse grained steels have
(A) Low toughness
(B) No tendency to distort
(C) High density
(D) Very high toughness
by

1 Answer

Answer :

(B) No tendency to distort
by

Related questions

Fine grained steels have (A) High brittleness (B) Higher tendency to distort (C) High ductility (D) None of these

Description : Fine grained steels have (A) High brittleness (B) Higher tendency to distort (C) High ductility (D) None of these

Last Answer : (C) High ductility

Pick up the correct statement from the following: (A) The dry density reduces by addition of water after attaining optimum moisture content (B) The line joining the peak of three moisture content graphs obtained by using three compactive energies, is called line of optimus (C) Well graded coarse grained soils can be compacted to a very high density as compared to fine grained soils (D) All the above

Description : Pick up the correct statement from the following: (A) The dry density reduces by addition of water after attaining optimum moisture content (B) The line joining the peak of three moisture content graphs ... be compacted to a very high density as compared to fine grained soils (D) All the above

Last Answer : Answer: Option D

Which of the following has a very high carbide forming tendency in steels? (A) Silicon (B) Chromium (C) Nickel (D) Vanadium

Description : Which of the following has a very high carbide forming tendency in steels? (A) Silicon (B) Chromium (C) Nickel (D) Vanadium

Last Answer : (D) Vanadium

Shock resisting steels should possess high (A) Hardness (B) Toughness (C) Tensile strength (D) Wear resistance

Description : Shock resisting steels should possess high (A) Hardness (B) Toughness (C) Tensile strength (D) Wear resistance

Last Answer : (B) Toughness

Steels with high carbon equivalent have poor Weldability, because in these steels during welding (A) Carbon and other alloying elements get oxidised from the weld pool (B) Excessive ferrite forms in the heat affected zone leading to poor toughness of the weld (C) Martensite forms in the heat affected zone leading to poor toughness/ductility of the weld (D) Segregation of carbon and other element occurs in the weld pool leading to poor properties of the weld

Description : Steels with high carbon equivalent have poor Weldability, because in these steels during welding (A) Carbon and other alloying elements get oxidised from the weld pool (B) Excessive ferrite forms in the ... of carbon and other element occurs in the weld pool leading to poor properties of the weld

Last Answer : (C) Martensite forms in the heat affected zone leading to poor toughness/ductility of the weld

Chrome vanadium steels usually contain 0.8 to 1.1% Cr, 0.25 to 0.35% C and < 0.25% V. It is (A) Used for making axle & shafts of aeroplanes, automobiles and locomotives (B) Having poor fatigue resistance (C) Having poor toughness (D) Not helpful in producing cleaner steel due to oxidising action of vanadium

Description : Chrome vanadium steels usually contain 0.8 to 1.1% Cr, 0.25 to 0.35% C and < 0.25% V. It is (A) Used for making axle & shafts of aeroplanes, automobiles and locomotives (B) ... resistance (C) Having poor toughness (D) Not helpful in producing cleaner steel due to oxidising action of vanadium

Last Answer : (A) Used for making axle & shafts of aeroplanes, automobiles and locomotives

Most important property of steels for use in automobile bodies is the (A) Formability (B) Yield strength (C) Toughness (D) Resilience

Description : Most important property of steels for use in automobile bodies is the (A) Formability (B) Yield strength (C) Toughness (D) Resilience

Last Answer : (A) Formability

What kind of rock is coarse grained rock?

Description : What kind of rock is coarse grained rock?

Last Answer : Need answer

What is Under which condition below you expect a coarse grained instrusive rock like diorite to form?

Description : What is Under which condition below you expect a coarse grained instrusive rock like diorite to form?

Last Answer : What is the answer ?

_______ in GAE provides coarse-grained locking service a) Bigtable b) Chubby c) MapReduce d) GFS

Description : _______ in GAE provides coarse-grained locking service a) Bigtable b) Chubby c) MapReduce d) GFS

Last Answer : Chubby

Coarse grained soils are best compacted by a (A) Drum roller (B) Rubber tyred roller (C) Sheep's foot roller (D) Vibratory roller

Description : Coarse grained soils are best compacted by a (A) Drum roller (B) Rubber tyred roller (C) Sheep's foot roller (D) Vibratory roller

Last Answer : (D) Vibratory roller

A coarse-grained soil has a voids ratio 0.75, and specific gravity as 2.75. The critical gradient at which quick sand condition occurs, is (A) 0.25 (B) 0.50 (C) 0.75 (D) 1.00

Description : A coarse-grained soil has a voids ratio 0.75, and specific gravity as 2.75. The critical gradient at which quick sand condition occurs, is (A) 0.25 (B) 0.50 (C) 0.75 (D) 1.00

Last Answer : (D) 1.00

Which of the following methods is best suited for determination of permeability of coarse-grained soils? (A) Constant head method (B) Falling head method (C) Both the above (D) None of the above

Description : Which of the following methods is best suited for determination of permeability of coarse-grained soils? (A) Constant head method (B) Falling head method (C) Both the above (D) None of the above

Last Answer : Answer: Option A

For better strength and stability, the fine grained soils and coarse grained soils are compacted respectively as (A) Dry of OMC and wet of OMC (B) Wet of OMC and dry of OMC (C) Wet of OMC and wet of OMC (D) Dry of OMC and dry of OMC where OMC is optimum moisture content

Description : For better strength and stability, the fine grained soils and coarse grained soils are compacted respectively as (A) Dry of OMC and wet of OMC (B) Wet of OMC and dry of OMC (C) Wet of OMC and wet of OMC (D) Dry of OMC and dry of OMC where OMC is optimum moisture content

Last Answer : Answer: Option B

Select the incorrect statement. (A) Effective cohesion of a soil can never have a negative value. (B) Effective angle of internal friction for coarse grained soils is rarely below 30°. (C) Effective angle of internal friction for a soil increases as state of compactness increases. (D) Effective angle of internal friction is a complicated function of mineralogy and clay size content.

Description : Select the incorrect statement. (A) Effective cohesion of a soil can never have a negative value. (B) Effective angle of internal friction for coarse grained soils is rarely below 30°. (C ... (D) Effective angle of internal friction is a complicated function of mineralogy and clay size content.

Last Answer : Answer: Option A

Pick up the correct statement from the following: (A) The permeability of the coarse-grained soils may be reduced by grouting (B) The process of injecting fluids (i.e. grouts) into the pores space of the soil is called grouting (C) The grouting increases the soil strength (D) All the above

Description : Pick up the correct statement from the following: (A) The permeability of the coarse-grained soils may be reduced by grouting (B) The process of injecting fluids (i.e. grouts) into the pores space of the soil is called grouting (C) The grouting increases the soil strength (D) All the above

Last Answer : Answer: Option D

Which of the following describes the Gabbro? (A) fine-grained, dark-colored igneous rock poor in silica (B) Coarse-grained, dark-colored igneous rock poor in silica (C) Fine-grained, dark-colored igneous rock rich in silica (D) Coarse -grained, dark-colored igneous rock rich in silica

Description : Which of the following describes the Gabbro? (A) fine-grained, dark-colored igneous rock poor in silica (B) Coarse-grained, dark-colored igneous rock poor in silica (C) Fine-grained, dark-colored igneous rock rich in silica (D) Coarse -grained, dark-colored igneous rock rich in silica

Last Answer : Coarse-grained, dark-colored igneous rock poor in silica

What do mean by coarse grain soil and fine grained soil.

Description : What do mean by coarse grain soil and fine grained soil.

Last Answer : Coarse Grain Soil:- 1. If more than 50% of soil is retained on sieve 0.075mm it is called as coarse grain soil. 2. A coarse grain soil is called as gravel if 50% or more of the ... liquid limit is less than 50% or more than 50% respectively. Organic soil are also included in fine grain soil.

Detrimental property of a material for shock load applications (a) High density (b) Low toughness (c) High strength (d) Low hardness

Description : Detrimental property of a material for shock load applications (a) High density (b) Low toughness (c) High strength (d) Low hardness  

Last Answer : (b) Low toughness

Pick out the wrong statement regarding the solubility characteristics of high polymers. (A) Greater the degree of cross-linking in the polymer, lesser is its solubility (B) Polymers having more aliphatic character are more soluble in aliphatic solvents, while those polymers having more aromatic character are more soluble in aromatic solvents (C) Swelling tendency or solubility of polymers in a particular solvent decreases with increase in molecular weight of the solvent (D) High molecular weight polymers on dissolving gives solution of very low viscosity

Description : Pick out the wrong statement regarding the solubility characteristics of high polymers. (A) Greater the degree of cross-linking in the polymer, lesser is its solubility (B) Polymers having more ... of the solvent (D) High molecular weight polymers on dissolving gives solution of very low viscosity

Last Answer : (D) High molecular weight polymers on dissolving gives solution of very low viscosity

Presence of SO2 in furnace gases attacks the ferrous metal by way of (A) Accelerating the rate of scaling (B) Causing metal embrittlement (C) Attacking the grain boundaries; particularly severe on low carbon and nickel bearing steels at high temperature (D) All (A), (B) and (C)

Description : Presence of SO2 in furnace gases attacks the ferrous metal by way of (A) Accelerating the rate of scaling (B) Causing metal embrittlement (C) Attacking the grain boundaries; particularly severe on low carbon and nickel bearing steels at high temperature (D) All (A), (B) and (C)

Last Answer : (D) All (A), (B) and (C)

To obtain a very high strength concrete, use very fine grained (A) Granite (B) Magnetite (C) Barite (D) Volcanic

Description : To obtain a very high strength concrete, use very fine grained (A) Granite (B) Magnetite (C) Barite (D) Volcanic

Last Answer : Answer: Option A

What is the permissible flux density in case of cold rolled grained oriented steel?

Description : What is the permissible flux density in case of cold rolled grained oriented steel?

Last Answer : The permissible flux density in case of cold rolled grained oriented steel is 1.7 Wb/m2.

A bearing metal should not have (A) Enough plasticity (B) Low thermal conductivity (C) Low co-efficient of friction (D) High toughness

Description : A bearing metal should not have (A) Enough plasticity (B) Low thermal conductivity (C) Low co-efficient of friction (D) High toughness

Last Answer : (B) Low thermal conductivity

Molybdenum steels containing 0.15 to 0.40% molybdenum (A) Are prone to temper brittleness (B) Are used for automobile parts like gears, axle, shaft, bearings etc. (C) Have very poor fatigue resistance

Description : Molybdenum steels containing 0.15 to 0.40% molybdenum (A) Are prone to temper brittleness (B) Are used for automobile parts like gears, axle, shaft, bearings etc. (C) Have very poor fatigue resistance

Last Answer : (B) Are used for automobile parts like gears, axle, shaft, bearings etc

Identify the false statement (A) Martensitic steels are less susceptible to pitting corrosion than austenitic steels (B) Pitting corrosion is usually very localised (C) Hydrogen embrittlement is facilitated by tensile stress (D) Stress corrosion cracking is facilitated by tensile stress

Description : Identify the false statement (A) Martensitic steels are less susceptible to pitting corrosion than austenitic steels (B) Pitting corrosion is usually very localised (C) Hydrogen embrittlement is facilitated by tensile stress (D) Stress corrosion cracking is facilitated by tensile stress

Last Answer : (A) Martensitic steels are less susceptible to pitting corrosion than austenitic steels

Manganese steels (A) Are non-magnetic (B) Possess high electrical resistance (C) Possess low coefficient of expansion (D) All the above

Description : Manganese steels (A) Are non-magnetic (B) Possess high electrical resistance (C) Possess low coefficient of expansion (D) All the above

Last Answer : Answer: Option D

Low carbon steels are those in which carbon percentage is around (A) 0.1 to 0.35 (B) 0.4 to 0.7 (C) 0.8 to 1.5 (D) 1.5 to 2

Description : Low carbon steels are those in which carbon percentage is around (A) 0.1 to 0.35 (B) 0.4 to 0.7 (C) 0.8 to 1.5 (D) 1.5 to 2

Last Answer : (A) 0.1 to 0.35

Generally __________ are subjected to galvanising (i.e., zinc coating). (A) Non-ferrous metals (B) Non-metals (C) Low carbon steels (D) Stainless steel

Description : Generally __________ are subjected to galvanising (i.e., zinc coating). (A) Non-ferrous metals (B) Non-metals (C) Low carbon steels (D) Stainless steel

Last Answer : (C) Low carbon steels

Pick out the wrong statement pertaining to leaching. (A) Fine solids cannot be leached in a Pachuca tank (B) Door classifier can be used for leaching of coarse solids (C) Vegetable seeds can be leached in either of Bollman extractor, Rotocel or Kennedy extractor (D) Very high temperature is not needed for the leaching of sugar beet

Description : Pick out the wrong statement pertaining to leaching. (A) Fine solids cannot be leached in a Pachuca tank (B) Door classifier can be used for leaching of coarse solids (C) Vegetable seeds can be ... , Rotocel or Kennedy extractor (D) Very high temperature is not needed for the leaching of sugar beet

Last Answer : (A) Fine solids cannot be leached in a Pachuca tank

Dislocation cross-slip is difficult in those materials, which have (A) Large number of slip systems (B) High work hardening rate (C) Coarse grain size (D) Low stacking fault energy

Description : Dislocation cross-slip is difficult in those materials, which have (A) Large number of slip systems (B) High work hardening rate (C) Coarse grain size (D) Low stacking fault energy

Last Answer : (D) Low stacking fault energy

If the value of Sx=1 and Sy=1 then a.Reduce the size of object b.Distort the picture c.Produce an enlargement d.No change in the size of an object

Description : If the value of Sx=1 and Sy=1 then a.Reduce the size of object b.Distort the picture c.Produce an enlargement d.No change in the size of an object

Last Answer : d.No change in the size of an object

Refractory bricks burnt at very high temperature have got (A) Greater resistance to corrosion by slags (B) Less resistance to corrosion by slags (C) High spalling tendency (D) None of these

Description : Refractory bricks burnt at very high temperature have got (A) Greater resistance to corrosion by slags (B) Less resistance to corrosion by slags (C) High spalling tendency (D) None of these

Last Answer : (A) Greater resistance to corrosion by slags

With increase in moisture content of coal, its (A) Calorific value increases sometimes (B) Bulk density always decreases (C) Clinkering tendency during combustion increases (D) None of these

Description : With increase in moisture content of coal, its (A) Calorific value increases sometimes (B) Bulk density always decreases (C) Clinkering tendency during combustion increases (D) None of these

Last Answer : (D) None of these

A major difference between light cured and chemical cured composite is that during setting or in function the light cured material tends to:******** VERY IMP A. Seal the margins better and completely B. Exhibit less wear on time C. Undergo greater colour change D. Shrink more rapidly E. Posses greater fracture toughness

Description : A major difference between light cured and chemical cured composite is that during setting or in function the light cured material tends to:******** VERY IMP A. Seal the margins better and ... on time C. Undergo greater colour change D. Shrink more rapidly E. Posses greater fracture toughness

Last Answer : D. Shrink more rapidly

Weld decay occurs in which of the following steel types? a) Carbon/Manganese b) Low alloy c) Any stainless steel d) Austenitic stainless steels

Description : Weld decay occurs in which of the following steel types? a) Carbon/Manganese b) Low alloy c) Any stainless steel d) Austenitic stainless steels

Last Answer : d) Austenitic stainless steels

Specialty low-alloy steel DMR-1700 a cost-effective replacement of mar- aging steels is product of (a) DLRL (b) DEAL (c) DMRL (d) DEBEL

Description : Specialty low-alloy steel DMR-1700 a cost-effective replacement of mar- aging steels is product of (a) DLRL (b) DEAL (c) DMRL (d) DEBEL

Last Answer : (c) DMRL

Higher boiling fractions like atmospheric residue is distilled under vacuum at low temperature because at high temperature, there is a tendency of the predominance of(A) Thermal cracking(B) Gum formation(C) Coking(D) Discoloration

Description : Higher boiling fractions like atmospheric residue is distilled under vacuum at low temperature because at high temperature, there is a tendency of the predominance of (A) Thermal cracking (B) Gum formation (C) Coking (D) Discoloration

Last Answer : (C) Coking

Steam distillation is not recommended to be used, if the (A) Azeotropic mixture is to be separated and the final product is miscible with water (B) Liquids decompose, if distilled directly at atmospheric pressure (C) Material cannot be distilled by indirect heating even under low pressure, because of the high boiling temperature (D) Material to be distilled is thermally unstable or has the tendency to react with other components associated with it, at the boiling temperature

Description : Steam distillation is not recommended to be used, if the (A) Azeotropic mixture is to be separated and the final product is miscible with water (B) Liquids decompose, if ... unstable or has the tendency to react with other components associated with it, at the boiling temperature

Last Answer : (A) Azeotropic mixture is to be separated and the final product is miscible with water

High speed cutting tool steels contain about __________ percent of tungsten. (A) 6-8 (B) 18-20 (C) 30-35 (D) 50-55

Description : High speed cutting tool steels contain about __________ percent of tungsten. (A) 6-8 (B) 18-20 (C) 30-35 (D) 50-55

Last Answer : (B) 18-20

Pick out the wrong statement (A) Hardening makes the steel more brittle (B) High alloy steels contain more than 50% alloying element (C) 18/8 stainless steel is a magnetic steel (D) Both (B) and (C)

Description : Pick out the wrong statement (A) Hardening makes the steel more brittle (B) High alloy steels contain more than 50% alloying element (C) 18/8 stainless steel is a magnetic steel (D) Both (B) and (C)

Last Answer : (D) Both (B) and (C)

Secondary hardening in steels arises out of the (A) Precipitation of fine alloy carbides at high temperatures (B) Refinement of ferrite grain size by working (C) Decomposition of retained austenite upon heat treatment (D) Precipitation of complex inter-metallic upon heat treatment

Description : Secondary hardening in steels arises out of the (A) Precipitation of fine alloy carbides at high temperatures (B) Refinement of ferrite grain size by working (C) Decomposition of retained austenite upon heat treatment (D) Precipitation of complex inter-metallic upon heat treatment

Last Answer : Option C

What must be considered when using flanges at the ratings listed in ASME B16.5 at low temperatures? a) Toughness. b) Shock loadings. c) Sudden changes of stress or temperature. d) All of the above.

Description : What must be considered when using flanges at the ratings listed in ASME B16.5 at low temperatures? a) Toughness. b) Shock loadings. c) Sudden changes of stress or temperature. d) All of the above.

Last Answer : c) Sudden changes of stress or temperature.

Wet sieving is employed, when the product contains __________ materials. (A) Abrasive (B) Large quantity of very fine (C) Coarse (D) Non-sticky

Description : Wet sieving is employed, when the product contains __________ materials. (A) Abrasive (B) Large quantity of very fine (C) Coarse (D) Non-sticky

Last Answer : (B) Large quantity of very fine

Zeigler process (A) Produces high density polythene(B) Uses no catalyst(C) Produces low density polythene(D) Employs very high pressure

Description : Zeigler process (A) Produces high density polythene (B) Uses no catalyst (C) Produces low density polythene (D) Employs very high pressure

Last Answer : (A) Produces high density polythene

Zeigler process (A) Produces high density polyethylene (B) Produces low density polyethylene (C) Uses no catalyst (D) Employs very high pressure

Description : Zeigler process (A) Produces high density polyethylene (B) Produces low density polyethylene (C) Uses no catalyst (D) Employs very high pressure

Last Answer : (A) Produces high density polyethylene

Plasticisers are high boiling liquids added to plastic polymers to impart toughness and flexibility at ordinary temperature. Which of the following is not a plasticiser? (A) Ethylene glycol (B) Stearic acid estors (C) Tricresyl phosphate (D) Esters of phthalic acid

Description : Plasticisers are high boiling liquids added to plastic polymers to impart toughness and flexibility at ordinary temperature. Which of the following is not a plasticiser? (A) Ethylene glycol (B) Stearic acid estors (C) Tricresyl phosphate (D) Esters of phthalic acid

Last Answer : (A) Ethylene glycol

High degree of toughness is a must for (A) High speed steel (B) Shock resisting steel (C) Cold work tool steel (D) None of these

Description : High degree of toughness is a must for (A) High speed steel (B) Shock resisting steel (C) Cold work tool steel (D) None of these

Last Answer : (B) Shock resisting steel

Cold work tool steel should have (A) High toughness (B) Poor hardenability (C) High wear resistance (D) All (A), (B) & (C)

Description : Cold work tool steel should have (A) High toughness (B) Poor hardenability (C) High wear resistance (D) All (A), (B) & (C)

Last Answer : (C) High wear resistance

High speed steel should have high (A) Toughness (B) Wear resistance (C) Hardenability (D) Both (B) & (C)

Description : High speed steel should have high (A) Toughness (B) Wear resistance (C) Hardenability (D) Both (B) & (C)

Last Answer : (D) Both (B) & (C)