Pick up the incorrect statement from the following: (A) Tricalcium silicate (C3S) hydrates rapidly (B) Tricalcium silicate (C3S) generates more heat of hydration (C) Tricalcium silicate (C3S) develops early strength (D) Tricalcium silicate (C3S) has more resistance to sulphate attac

Pick up the incorrect statement from the following:
(A) Tricalcium silicate (C3S) hydrates rapidly
(B) Tricalcium silicate (C3S) generates more heat of hydration
(C) Tricalcium silicate (C3S) develops early strength
(D) Tricalcium silicate (C3S) has more resistance to sulphate attack
by

1 Answer

Answer :

Answer: Option D
by

Related questions

The presence of tricalcium silicate in cement (a) Hydrates the cement rapidly (b) Generates less heat of hydration. (c) Offer high resistance to sulphate attack (d) All of these

Description : The presence of tricalcium silicate in cement (a) Hydrates the cement rapidly (b) Generates less heat of hydration. (c) Offer high resistance to sulphate attack (d) All of these

Last Answer : (a) Hydrates the cement rapidly

Di-calcium silicate (C2S) (A) Hydrates rapidly (B) Generates less heat of hydration (C) Hardens rapidly (D) Provides less ultimate strength to cement

Description : Di-calcium silicate (C2S) (A) Hydrates rapidly (B) Generates less heat of hydration (C) Hardens rapidly (D) Provides less ultimate strength to cement

Last Answer : Answer: Option B

The presence of dicalcium silicate in cement. (a) Hydrates the cement slowly. (b) Generates less heat of hydration. (c) Has more resistance to sulphate attack. (d) All of these

Description : The presence of dicalcium silicate in cement. (a) Hydrates the cement slowly. (b) Generates less heat of hydration. (c) Has more resistance to sulphate attack. (d) All of these

Last Answer : (d) All of these

Dicalcium silicate (C2S) [ A ] rates rapidly [ B ] Hardens rapidly [ C ] Generates less heat of hydration [ D ] Has less resistance to sulphate attack

Description : Dicalcium silicate (C2S) [ A ] rates rapidly [ B ] Hardens rapidly [ C ] Generates less heat of hydration [ D ] Has less resistance to sulphate attack

Last Answer : [ C ] Generates less heat of hydration

Tricalcium aluminate (C3A) (A) Reacts fast with water (B) Generates less heat of hydration (C) Causes initial setting and early strength of cement (D) Does not contribute to develop ultimate strength

Description : Tricalcium aluminate (C3A) (A) Reacts fast with water (B) Generates less heat of hydration (C) Causes initial setting and early strength of cement (D) Does not contribute to develop ultimate strength

Last Answer : Answer: Option B

Dicalcium silicate a) Hydrates rapidly b) Generate less heat of hydration* c) Hardens rapidly d) Reacts with water only

Description : Dicalcium silicate a) Hydrates rapidly b) Generate less heat of hydration* c) Hardens rapidly d) Reacts with water only

Last Answer : b) Generate less heat of hydration*

The development of first 28 days strength is on account of the hydration of (a) Tricalcium silicate (b) Dicalcium silicate (c) Tricalcium aluminate (d) Tetra calcium alumina ferrite

Description : The development of first 28 days strength is on account of the hydration of (a) Tricalcium silicate (b) Dicalcium silicate (c) Tricalcium aluminate (d) Tetra calcium alumina ferrite

Last Answer : (a) Tricalcium silicate

Pick out the wrong statement. (A) High early strength cement are made from materials having high silica to lime ratio (B) The function of gypsum in cement is to enhance its initial setting rate (C) Acid resistant cements are known as silicate cement (D) Major component of greyish Portland cement is tricalcium silicate

Description : Pick out the wrong statement. (A) High early strength cement are made from materials having high silica to lime ratio (B) The function of gypsum in cement is to enhance its initial ... cements are known as silicate cement (D) Major component of greyish Portland cement is tricalcium silicate

Last Answer : (A) High early strength cement are made from materials having high silica to lime ratio

High percentage of tricalcium silicate and low percentage of dicalcium silicate in cement results in. (a) Rapid hardening (b) High early strength (c) High heat of generation (d) All the above

Description : High percentage of tricalcium silicate and low percentage of dicalcium silicate in cement results in. (a) Rapid hardening (b) High early strength (c) High heat of generation (d) All the above

Last Answer : (d) All the above

Hydration of cement is due to chemical action of water with (A) Tricalcium silicate and dicalcium silicate (B) Dicalcium silicate and tricalcium aluminate (C) Tricalcium aluminate and tricalcium alumino ferrite (D) All the above

Description : Hydration of cement is due to chemical action of water with (A) Tricalcium silicate and dicalcium silicate (B) Dicalcium silicate and tricalcium aluminate (C) Tricalcium aluminate and tricalcium alumino ferrite (D) All the above

Last Answer : Answer: Option D

Hydration of cement is due to the chemical action of water with. (a) Tricalcium silicate (b) Dicalcium silicate (c) Tricalcium aluminate (d) All of these

Description : Hydration of cement is due to the chemical action of water with. (a) Tricalcium silicate (b) Dicalcium silicate (c) Tricalcium aluminate (d) All of these

Last Answer : (d) All of these

__________ is the major constituent of the Portland cement. (A) Calcium carbonate (B) Calcium oxide (C) Tricalcium silicate (D) Calcium sulphate

Description : __________ is the major constituent of the Portland cement. (A) Calcium carbonate (B) Calcium oxide (C) Tricalcium silicate (D) Calcium sulphate

Last Answer : (C) Tricalcium silicate

Too much fineness of cement (a) Results cracks in concrete (b) Generates greater heat (c) Develops later strength (d) All the above

Description : Too much fineness of cement (a) Results cracks in concrete (b) Generates greater heat (c) Develops later strength (d) All the above

Last Answer : (d) All the above

Pick up the incorrect statement (A) The cross-sectional area of the welded member is effective (B) A welded joint develops strength of its parent metal (C) Welded joints provide rigidity (D) Welding takes more time than riveting

Description : Pick up the incorrect statement (A) The cross-sectional area of the welded member is effective (B) A welded joint develops strength of its parent metal (C) Welded joints provide rigidity (D) Welding takes more time than riveting

Last Answer : (D) Welding takes more time than riveting

Pick up the incorrect statement from the following: (A) The degree of grinding of cement, is called fineness (B) The process of changing cement paste into hard mass, is known as setting of cement (C) The phenomenon by virtue of which cement does not allow transmission of sound, is known as soundness of cement (D) The heat generated during chemical reaction of cement with water, is known as heat of hydration

Description : Pick up the incorrect statement from the following: (A) The degree of grinding of cement, is called fineness (B) The process of changing cement paste into hard mass, is known as setting of ... (D) The heat generated during chemical reaction of cement with water, is known as heat of hydration

Last Answer : Answer: Option C

Which compound in cement, gives early age strength (a) C3S (b) C2S (c) C3A (d) C4AF

Description : Which compound in cement, gives early age strength (a) C3S (b) C2S (c) C3A (d) C4AF

Last Answer : (a) C3S

The following compound has the property of early strength as well as ultimate strength [ A ] C3S [ B ] C2S [ C ] C3A [ D ] C4AF

Description : The following compound has the property of early strength as well as ultimate strength [ A ] C3S [ B ] C2S [ C ] C3A [ D ] C4AF

Last Answer : [ A ] C3S

Pick up the compound responsible for early strength of cement from the following: (A) Tetra-calcium alumino-ferrite (B) Tri-calcium silicate (C) Tri-calcium aluminate (D) Di-calcium silicate

Description : Pick up the compound responsible for early strength of cement from the following: (A) Tetra-calcium alumino-ferrite (B) Tri-calcium silicate (C) Tri-calcium aluminate (D) Di-calcium silicate

Last Answer : Answer: Option B

ick up the incorrect statement from the following: (A) Admixtures accelerate hydration (B) Admixtures make concrete water proof (C) Admixtures make concrete acid proof (D) Admixtures give high strength

Description : ick up the incorrect statement from the following: (A) Admixtures accelerate hydration (B) Admixtures make concrete water proof (C) Admixtures make concrete acid proof (D) Admixtures give high strength

Last Answer : Answer: Option A

The sum of the percentage of tricalcium silicate and dicalcium silicate for Portland cement varies from. (a) 50 to 60% (b) 60 to 70% (c) 70 to 80% (d) 80 to 90%

Description : The sum of the percentage of tricalcium silicate and dicalcium silicate for Portland cement varies from. (a) 50 to 60% (b) 60 to 70% (c) 70 to 80% (d) 80 to 90%

Last Answer : (c) 70 to 80%

The first compound which reacts with water when mixed with cement is (a) Tricalcium Aluminate (b) Tricalcium silicate (c) Di-calcium silicate (d) Teracalcium aluminate

Description : The first compound which reacts with water when mixed with cement is (a) Tricalcium Aluminate (b) Tricalcium silicate (c) Di-calcium silicate (d) Teracalcium aluminate

Last Answer : (a) Tricalcium Aluminate

About 70% to 80% of cement is contributed by [ A ] Tricalcium silicate and Tricalcium aluminate [ B ] Tricalcium silicate and Dicalcium silicate [ C ] Tricalcium Aluminate and Dicalcium silicate [ D ] Tricalcium Aluminate and Tetra calcium Aluminoferrite

Description : About 70% to 80% of cement is contributed by [ A ] Tricalcium silicate and Tricalcium aluminate [ B ] Tricalcium silicate and Dicalcium silicate [ C ] Tricalcium Aluminate and Dicalcium silicate [ D ] Tricalcium Aluminate and Tetra calcium Aluminoferrite

Last Answer : [ B ] Tricalcium silicate and Dicalcium silicate

The high strength of rapid hardening cement at early stage, is due to its (A) Finer grinding (B) Burning at high temperature (C) Increased lime cement (D) Higher content of tricalcium

Description : The high strength of rapid hardening cement at early stage, is due to its (A) Finer grinding (B) Burning at high temperature (C) Increased lime cement (D) Higher content of tricalcium

Last Answer : Answer: Option C

Setting of plaster of paris involves – (1) dehydration process (2) hydration to form other hydrates (3) oxidation process (4) reduction process

Description : Setting of plaster of paris involves – (1) dehydration process (2) hydration to form other hydrates (3) oxidation process (4) reduction process

Last Answer : (2) hydration to form other hydrates Explanation: The setting of plaster of Paris takes place by hydration due to the formation of a solid crystalline hydrate and hardening of Plaster of Paris is ... . A slight expansion takes place in the process and heat is evolved. This process is exothermic.

Setting of plaster of paris involves (1) dehydration process (2) hydration to form other hydrates (3) oxidation process (4) reduction process

Description : Setting of plaster of paris involves (1) dehydration process (2) hydration to form other hydrates (3) oxidation process (4) reduction process

Last Answer : hydration to form other hydrates

Pick up the correct statement from the following: (A) High percentage of C3S and low percentage of C2S cause rapid hardening (B) High percentage of C3S and low percentage of C2S make the cement less resistive to chemical attack (C) Low percentage of C3S and high percentage of C2S contribute to slow hardening (D) All the above

Description : Pick up the correct statement from the following: (A) High percentage of C3S and low percentage of C2S cause rapid hardening (B) High percentage of C3S and low percentage of C2S make the cement ... ) Low percentage of C3S and high percentage of C2S contribute to slow hardening (D) All the above

Last Answer : Answer: Option D

Pick up the correct statement from the following: (A) The concrete gains strength due to hydration of cement (B) The concrete does not set at freezing point (C) The strength of concrete increases with its age (D) All the above

Description : Pick up the correct statement from the following: (A) The concrete gains strength due to hydration of cement (B) The concrete does not set at freezing point (C) The strength of concrete increases with its age (D) All the above

Last Answer : Answer: Option D

Pick up the correct statement from the following: (A) Water cement paste hardens due to hydration (B) During hardening cement binds the aggregates together (C) Cement provides strength, durability and water tightness to the concrete (D) All the above

Description : Pick up the correct statement from the following: (A) Water cement paste hardens due to hydration (B) During hardening cement binds the aggregates together (C) Cement provides strength, durability and water tightness to the concrete (D) All the above

Last Answer : Answer: Option D

Tricalcium aluminate (C3A) [ A ] Hydrating less rapidly [ B ] Is a redundant compound [ C ] To be attacked by alkalies and salts [ D ] None of these

Description : Tricalcium aluminate (C3A) [ A ] Hydrating less rapidly [ B ] Is a redundant compound [ C ] To be attacked by alkalies and salts [ D ] None of these

Last Answer : [ C ] To be attacked by alkalies and salts

A slow setting cement will have higher percentage of a) tricalcium aluminate b) tricalcium silicate c) Gypsum d) Dicalcium silicate*

Description : A slow setting cement will have higher percentage of a) tricalcium aluminate b) tricalcium silicate c) Gypsum d) Dicalcium silicate*

Last Answer : C2s

The constituent of cement which act as Binders are a) Sand and silica b) Silica and carbon c) tricalcium silicate dicalcium silicate and carbon d) tricalcium aluminate,dicalcium silicate and tricalcium silicate *

Description : The constituent of cement which act as Binders are a) Sand and silica b) Silica and carbon c) tricalcium silicate dicalcium silicate and carbon d) tricalcium aluminate,dicalcium silicate and tricalcium silicate *

Last Answer : d) tricalcium aluminate,dicalcium silicate and tricalcium silicate *

Which of the following cements contains maximum percentage of dicalcium silicate? (A) Ordinary Portland cement (B) Low heat cement (C) Rapid hardening cement (D) Sulphate resisting cement

Description : Which of the following cements contains maximum percentage of dicalcium silicate? (A) Ordinary Portland cement (B) Low heat cement (C) Rapid hardening cement (D) Sulphate resisting cement

Last Answer : Answer: Option B

Early attainment of strength in rapid hardening cement is mainly due to (A) Gypsum (B) Finer grinding (C) Tri-calcium silicate (D) Tri-calcium aluminate

Description : Early attainment of strength in rapid hardening cement is mainly due to (A) Gypsum (B) Finer grinding (C) Tri-calcium silicate (D) Tri-calcium aluminate

Last Answer : Answer: Option B

A 68-year-old male who underwent a repair of an abdominal aortic aneurysm 5 days ago, develops tachycardia, tachypnea, hypotension with cool, pale, mottled cyanotic extremities. He is agitated and complains of shortness of breath. Which of the following statement(s) is/ are correct concerning his diagnosis and management? a. Myocardial ischemia secondary to preexisting coronary artery disease is most likely the underlying cause of this problem b. Invasive hemodynamic monitoring with a Swan-Gantz catheter will demonstrate a low cardiac output, a high systemic vascular resistance, and elevated cardiac filling pressures c. The use of morphine sulphate and nitrates should be part of the initial management d. The primary pharmacologic treatment involves the use of moderate doses of inotropic ag

Description : A 68-year-old male who underwent a repair of an abdominal aortic aneurysm 5 days ago, develops tachycardia, tachypnea, hypotension with cool, pale, mottled cyanotic extremities. He ... use of moderate doses of inotropic agents e. Afterload reduction with nitroprusside is absolutely contraindicated

Last Answer : Answer: a, b, d Intrinsic cardiogenic shock results from failure of the heart as an effective pump. Coronary artery disease is the most common cause of myocardial ... hemodynamic monitoring. Infusion of afterload-reducing agents can be administered in conjunction with inotropic support

Low heat cement contains more amount of __________ than that of ordinary Portland cement [ A ] C3S [ B ] C2S [ C ] C3A [ D ] None of the above

Description : Low heat cement contains more amount of __________ than that of ordinary Portland cement [ A ] C3S [ B ] C2S [ C ] C3A [ D ] None of the above

Last Answer : [ B ] C2S

Addition of pozzolana to cement (A) Decreases workability (B) Increases strength (C) Increases heat of hydration (D) None of these

Description : Addition of pozzolana to cement (A) Decreases workability (B) Increases strength (C) Increases heat of hydration (D) None of these

Last Answer : Answer: Option D

The following is true of anti-H.pylori therapy except: A. It is indicated in all patients of peptic ulcer B. Resistance to any single antimicrobial drug develops rapidly C. Concurrent suppression of gastric acid enhances efficacy of the regimen D. Colloidal bismuth directly inhibits H.pylori but has poor patient acceptability

Description : The following is true of anti-H.pylori therapy except: A. It is indicated in all patients of peptic ulcer B. Resistance to any single antimicrobial drug develops rapidly C. Concurrent ... efficacy of the regimen D. Colloidal bismuth directly inhibits H.pylori but has poor patient acceptability

Last Answer : A. It is indicated in all patients of peptic ulcer

Pick up the incorrect statement from the following. If water cement ratio is (A) Increased, strength of concrete increases (B) Decreased, strength of concrete increases(D) None of these (C) Increased, strength of concrete is not affected

Description : Pick up the incorrect statement from the following. If water cement ratio is (A) Increased, strength of concrete increases (B) Decreased, strength of concrete increases (C) Increased, strength of concrete is not affected (D) None of these

Last Answer : Answer: Option C

Pick up the incorrect statement from the following: (A) With passage of time, the strength of cement increases (B) With passage of time, the strength of cement decreases (C) After a period of 24 months, the strength of cement reduces to 50% (D) The concrete made with storage deteriorated cement, gains strength with time

Description : Pick up the incorrect statement from the following: (A) With passage of time, the strength of cement increases (B) With passage of time, the strength of cement decreases (C) After a ... of cement reduces to 50% (D) The concrete made with storage deteriorated cement, gains strength with time

Last Answer : Answer: Option A

Pick up the incorrect statement from the following. For performing compressive strength test of cement (A) Cement and standard sand mortar are used in the ratio of 1 : 3 (B) Water is added at the rate of (P/4) + 3.0 percentage of water where P is the percentage of water for standard consistency (C) A cube mould of 10 cm × 10 cm × 10 cm is used (D) The prepared moulds are kept in a atmosphere of 50% relative humidity

Description : Pick up the incorrect statement from the following. For performing compressive strength test of cement (A) Cement and standard sand mortar are used in the ratio of 1 : 3 (B) Water is added at the ... cm 10 cm is used (D) The prepared moulds are kept in a atmosphere of 50% relative humidity

Last Answer : Answer: Option A

Select the incorrect statement [ A ] R.C.C has better fire resistance than steel [ B ] R.C.C. structure is economical than steel structure [ C ] Strength of concrete decreases as age increases [ D ] R.C.C can be used for under water and marine structures

Description : Select the incorrect statement [ A ] R.C.C has better fire resistance than steel [ B ] R.C.C. structure is economical than steel structure [ C ] Strength of concrete decreases as age increases [ D ] R.C.C can be used for under water and marine structures

Last Answer : [ C ] Strength of concrete decreases as age increases

Portland pozzolana cement possesses (A) Higher resistance to chemical attack (B) Lower heat of hydration (C) Lower shrinkage on drying (D) All the above

Description : Portland pozzolana cement possesses (A) Higher resistance to chemical attack (B) Lower heat of hydration (C) Lower shrinkage on drying (D) All the above

Last Answer : Answer: Option D

Pick up the incorrect statement from the following: The torsional resistance of a shaft is directly proportional to (A) Modulus of rigidity (B) Angle of twist (C) Reciprocal of the length of the shaft (D) Moment of inertia of the shaft section

Description : Pick up the incorrect statement from the following: The torsional resistance of a shaft is directly  proportional to  (A) Modulus of rigidity  (B) Angle of twist  (C) Reciprocal of the length of the shaft  (D) Moment of inertia of the shaft section 

Last Answer : (D) Moment of inertia of the shaft section 

In case of cement concrete pavements, pick up the incorrect statement (A) Tractive resistance is low (B) Initial cost of construction is high (C) Initial cost of construction is low (D) Visibility during nights is high

Description : In case of cement concrete pavements, pick up the incorrect statement (A) Tractive resistance is low (B) Initial cost of construction is high (C) Initial cost of construction is low (D) Visibility during nights is high

Last Answer : Answer: Option C

Pick out the wrong statement. (A) Fibrillation of fibre during paper manufacture is done to develop the strength in paper (B) Alkali consumption in digestion/cooking of bamboo is measured in terms of permanganate number (C) Bagasse fibre contains both lignin & cellulose (D) Presence of sodium sulphate in pulp makes the pulp bleachability poor

Description : Pick out the wrong statement. (A) Fibrillation of fibre during paper manufacture is done to develop the strength in paper (B) Alkali consumption in digestion/cooking of bamboo is measured in terms ... both lignin & cellulose (D) Presence of sodium sulphate in pulp makes the pulp bleachability poor

Last Answer : (D) Presence of sodium sulphate in pulp makes the pulp bleachability poor

Which of the following compound is susceptible to be attached by alkalies and salts [ A ] C3S [ B ] C3S [ C ] C3A [ D ] C3AF

Description : Which of the following compound is susceptible to be attached by alkalies and salts [ A ] C3S [ B ] C3S [ C ] C3A [ D ] C3AF

Last Answer : [ C ] C3A

Which of the following compounds is considered to be an undesirable compound for cement [ A ] C3S [ B ] C2S [ C ] C3A [ D ] C4AF

Description : Which of the following compounds is considered to be an undesirable compound for cement [ A ] C3S [ B ] C2S [ C ] C3A [ D ] C4AF

Last Answer : [ D ] C4AF

Pick up the incorrect definition from the following: (A) Ratio of the compressive strength of unconfined undisturbed soil to that of remoulded soil, is known as the sensitivity of the soil sample (B) The rotation of soil particles into stable state while remoulding, is known as the thiostropy of soil (C) The water content at which a soil flows, is known plastic limit of the soil (D) None of these

Description : Pick up the incorrect definition from the following: (A) Ratio of the compressive strength of unconfined undisturbed soil to that of remoulded soil, is known as the sensitivity of the soil sample (B) The ... content at which a soil flows, is known plastic limit of the soil (D) None of these

Last Answer : Answer: Option D

Pick up the correct statement from the following: (A) The distance of the eccentric axial load from the C.G. beyond which tension develops, is known as kern distance (B) In visco-elastic material, stress-strain relation is dependent on time (C) An orthotropic material has different properties in three mutually perpendicular directions (D) All the above

Description : Pick up the correct statement from the following: (A) The distance of the eccentric axial load from the C.G. beyond which tension develops, is known as kern distance (B) In visco ... (C) An orthotropic material has different properties in three mutually perpendicular directions (D) All the above

Last Answer : (D) All the above

Pick up the correct statement from the following: (A) To an agriculturist, soil is the substance existing on the earth's surface, which grows and develops plants (B) To a geologist, soil is the material in a relatively thin surface zone within which roots occur, and rest of the crust is termed as rock irrespective of hardness (C) To an engineer, soil is the unaggregated and uncemented deposits of minerals and organic particles covering the earth's crust (D) All the above

Description : Pick up the correct statement from the following: (A) To an agriculturist, soil is the substance existing on the earth's surface, which grows and develops plants (B) To a geologist, soil ... and uncemented deposits of minerals and organic particles covering the earth's crust (D) All the above

Last Answer : (D) All the above