Portland pozzolana cement possesses (A) Higher resistance to chemical attack (B) Lower heat of hydration (C) Lower shrinkage on drying (D) All the above

Portland pozzolana cement possesses
(A) Higher resistance to chemical attack
(B) Lower heat of hydration
(C) Lower shrinkage on drying
(D) All the above
by

1 Answer

Answer :

Answer: Option D
by

Related questions

Addition of pozzolana to ordinary Portland cement increases (A) Bleeding (B) Shrinkage (C) Permeability (D) Heat of hydration

Description : Addition of pozzolana to ordinary Portland cement increases (A) Bleeding (B) Shrinkage (C) Permeability (D) Heat of hydration

Last Answer : Answer: Option B

As compared to ordinary Portland cement, use of pozzolana cement (A) Reduces workability (B) Increases bleeding (C) Increases shrinkage (D) Increases strength

Description : As compared to ordinary Portland cement, use of pozzolana cement (A) Reduces workability (B) Increases bleeding (C) Increases shrinkage (D) Increases strength

Last Answer : Answer: Option C

The cement whose strength is a little lower than the ordinary cement during the first three months but attains afterwards the same strength, is known as (A) Low-heat Portland cement (B) Rapid hardening Portland cement (C) Portland blast slag cement (D) Portland pozzolana cement

Description : The cement whose strength is a little lower than the ordinary cement during the first three months but attains afterwards the same strength, is known as (A) Low-heat Portland cement (B) Rapid hardening Portland cement (C) Portland blast slag cement (D) Portland pozzolana cement

Last Answer : Answer: Option A

Addition of pozzolana to ordinary port land cement, causes (A) Decrease in early strength (B) Reduction in chemical action with sulphates (C) Increase in shrinkage (D) All the above

Description : Addition of pozzolana to ordinary port land cement, causes (A) Decrease in early strength (B) Reduction in chemical action with sulphates (C) Increase in shrinkage (D) All the above

Last Answer : Answer: Option D

Addition of pozzolana to cement (A) Decreases workability (B) Increases strength (C) Increases heat of hydration (D) None of these

Description : Addition of pozzolana to cement (A) Decreases workability (B) Increases strength (C) Increases heat of hydration (D) None of these

Last Answer : Answer: Option D

Addition of pozzolana to cement causes (A) Reduction in permeability (B) Loss of heat of hydration (C) Reduction in bleeding (D) All the above

Description : Addition of pozzolana to cement causes (A) Reduction in permeability (B) Loss of heat of hydration (C) Reduction in bleeding (D) All the above

Last Answer : Answer: Option D

For construction of structures in sea water, the cement generally preferred to, is (A) Portland-pozzolana cement (B) Quick setting cement (C) Low heat Portland cement (D) Rapid hardening cement

Description : For construction of structures in sea water, the cement generally preferred to, is (A) Portland-pozzolana cement (B) Quick setting cement (C) Low heat Portland cement (D) Rapid hardening cement

Last Answer : Answer: Option A

The presence of dicalcium silicate in cement. (a) Hydrates the cement slowly. (b) Generates less heat of hydration. (c) Has more resistance to sulphate attack. (d) All of these

Description : The presence of dicalcium silicate in cement. (a) Hydrates the cement slowly. (b) Generates less heat of hydration. (c) Has more resistance to sulphate attack. (d) All of these

Last Answer : (d) All of these

The presence of tricalcium silicate in cement (a) Hydrates the cement rapidly (b) Generates less heat of hydration. (c) Offer high resistance to sulphate attack (d) All of these

Description : The presence of tricalcium silicate in cement (a) Hydrates the cement rapidly (b) Generates less heat of hydration. (c) Offer high resistance to sulphate attack (d) All of these

Last Answer : (a) Hydrates the cement rapidly

Ordinary Portland cement is manufactured from (A) Lime stone and clay (B) Gypsum and lime (C) Pozzolana (D) Lime, pozzolana and clay

Description : Ordinary Portland cement is manufactured from (A) Lime stone and clay (B) Gypsum and lime (C) Pozzolana (D) Lime, pozzolana and clay

Last Answer : Answer: Option B

Which cement should not be used for bridge slabs ro RCC frames a) OPC b) Portland Pozzolana cement * c) Portland furnace slag cement d) Rapid hardening cement

Description : Which cement should not be used for bridge slabs ro RCC frames a) OPC b) Portland Pozzolana cement * c) Portland furnace slag cement d) Rapid hardening cement

Last Answer : b) Portland Pozzolana cement *

The lower water cement ratio in concrete, introduces (A) Smaller creep and shrinkage (B) Greater density and smaller permeability (C) Improved frost resistance (D) All the above

Description : The lower water cement ratio in concrete, introduces (A) Smaller creep and shrinkage (B) Greater density and smaller permeability (C) Improved frost resistance (D) All the above

Last Answer : Answer: Option D

As compared to ordinary Portland cement, high alumina cement has (A) Higher initial setting time but lower final setting time (B) Lower initial setting time but higher final setting time (C) Higher initial and final setting times (D) Lower initial and final setting times

Description : As compared to ordinary Portland cement, high alumina cement has (A) Higher initial setting time but lower final setting time (B) Lower initial setting time but higher final setting time (C) Higher initial and final setting times (D) Lower initial and final setting times

Last Answer : Answer: Option A

Pozzolana (or surkhi) is used in lime (A) To impart hydraulicity (B) To prevent shrinkage (C) To decrease the cost of construction (D) To decrease the setting time

Description : Pozzolana (or surkhi) is used in lime (A) To impart hydraulicity (B) To prevent shrinkage (C) To decrease the cost of construction (D) To decrease the setting time

Last Answer : Answer: Option A

Dicalcium silicate (C2S) [ A ] rates rapidly [ B ] Hardens rapidly [ C ] Generates less heat of hydration [ D ] Has less resistance to sulphate attack

Description : Dicalcium silicate (C2S) [ A ] rates rapidly [ B ] Hardens rapidly [ C ] Generates less heat of hydration [ D ] Has less resistance to sulphate attack

Last Answer : [ C ] Generates less heat of hydration

Pick up the incorrect statement from the following: (A) The degree of grinding of cement, is called fineness (B) The process of changing cement paste into hard mass, is known as setting of cement (C) The phenomenon by virtue of which cement does not allow transmission of sound, is known as soundness of cement (D) The heat generated during chemical reaction of cement with water, is known as heat of hydration

Description : Pick up the incorrect statement from the following: (A) The degree of grinding of cement, is called fineness (B) The process of changing cement paste into hard mass, is known as setting of ... (D) The heat generated during chemical reaction of cement with water, is known as heat of hydration

Last Answer : Answer: Option C

Shrinkage volume in cement setting does not depend upon the (A) Sand to cement ratio (B) Water to cement ratio (C) Ambient temperature fluctuation (D) Drying period

Description : Shrinkage volume in cement setting does not depend upon the (A) Sand to cement ratio (B) Water to cement ratio (C) Ambient temperature fluctuation (D) Drying period

Last Answer : (A) Sand to cement ratio

The minimum water content at which the soil retains its liquid state and also possesses a small shearing strength against flowing, is known (A) Liquid limit (B) Plastic limit (C) Shrinkage limit (D) Permeability limit

Description : The minimum water content at which the soil retains its liquid state and also possesses a small shearing strength against flowing, is known (A) Liquid limit (B) Plastic limit (C) Shrinkage limit (D) Permeability limit

Last Answer : (A) Liquid limit

The process of keeping the concrete structure moist is called [ A ] Hydration [ B ] Curing [ C ] Creep [ D ] Shrinkage

Description : The process of keeping the concrete structure moist is called [ A ] Hydration [ B ] Curing [ C ] Creep [ D ] Shrinkage

Last Answer : [ B ] Curing

The process of hardening of concrete in the presence of water is called [ A ] Creep [ B ] Hydration [ C ] Shrinkage [ D ] Curing

Description : The process of hardening of concrete in the presence of water is called [ A ] Creep [ B ] Hydration [ C ] Shrinkage [ D ] Curing

Last Answer : [ B ] Hydration

Hydration of cement is due to chemical action of water with (A) Tricalcium silicate and dicalcium silicate (B) Dicalcium silicate and tricalcium aluminate (C) Tricalcium aluminate and tricalcium alumino ferrite (D) All the above

Description : Hydration of cement is due to chemical action of water with (A) Tricalcium silicate and dicalcium silicate (B) Dicalcium silicate and tricalcium aluminate (C) Tricalcium aluminate and tricalcium alumino ferrite (D) All the above

Last Answer : Answer: Option D

Concrete gains strength due to (A) Chemical reaction of cement with sand and coarse aggregates (B) Evaporation of water from concrete (C) Hydration of cement (D) All the above

Description : Concrete gains strength due to (A) Chemical reaction of cement with sand and coarse aggregates (B) Evaporation of water from concrete (C) Hydration of cement (D) All the above

Last Answer : Answer: Option C

Hydration of cement is due to the chemical action of water with. (a) Tricalcium silicate (b) Dicalcium silicate (c) Tricalcium aluminate (d) All of these

Description : Hydration of cement is due to the chemical action of water with. (a) Tricalcium silicate (b) Dicalcium silicate (c) Tricalcium aluminate (d) All of these

Last Answer : (d) All of these

Concrete gains strength due to [ A ] Chemical reaction of cement with sand and coarse aggregates [ B ] Evaporation of water from concrete [ C ] Hydration of cement [ D ] All the above

Description : Concrete gains strength due to [ A ] Chemical reaction of cement with sand and coarse aggregates [ B ] Evaporation of water from concrete [ C ] Hydration of cement [ D ] All the above

Last Answer : [ C ] Hydration of cement

Pick up the correct statement regarding low heat cement from the following: (A) It possesses less compressive strength (B) Its initial setting time is about one hour (C) Its final setting time is about 10 hours (D) All the above

Description : Pick up the correct statement regarding low heat cement from the following: (A) It possesses less compressive strength (B) Its initial setting time is about one hour (C) Its final setting time is about 10 hours (D) All the above

Last Answer : Answer: Option D

Percentage of pozzolanic material containing clay upto 80% used for the manufacture of pozzolana cement, is (A) 30 % (B) 40 % (C) 50 % (D) 60 %

Description : Percentage of pozzolanic material containing clay upto 80% used for the manufacture of pozzolana cement, is (A) 30 % (B) 40 % (C) 50 % (D) 60 %

Last Answer : (A) 30 %

Pozzolana cement is used with confidence for construction of (A) Dams (B) Massive foundations (C) R.C.C. structures (D) All the above

Description : Pozzolana cement is used with confidence for construction of (A) Dams (B) Massive foundations (C) R.C.C. structures (D) All the above

Last Answer : (D) All the above

Quick setting cement is produced by adding (A) Less amount of gypsum in very fine powdered form (B) More amount of gypsum in very fine powdered form (C) Aluminium sulphate in very fine powdered form (D) Pozzolana in very fine powdered form

Description : Quick setting cement is produced by adding (A) Less amount of gypsum in very fine powdered form (B) More amount of gypsum in very fine powdered form (C) Aluminium sulphate in very fine powdered form (D) Pozzolana in very fine powdered form

Last Answer : Answer: Option C

Name the type of cement from the following for canal linings: (A) Sulphate resisting cement (B) Rapid hardening cement (C) Quick setting cement (D) Pozzolana cement

Description : Name the type of cement from the following for canal linings: (A) Sulphate resisting cement (B) Rapid hardening cement (C) Quick setting cement (D) Pozzolana cement

Last Answer : Answer: Option A

Di-calcium silicate (C2S) (A) Hydrates rapidly (B) Generates less heat of hydration (C) Hardens rapidly (D) Provides less ultimate strength to cement

Description : Di-calcium silicate (C2S) (A) Hydrates rapidly (B) Generates less heat of hydration (C) Hardens rapidly (D) Provides less ultimate strength to cement

Last Answer : Answer: Option B

Tricalcium aluminate (C3A) (A) Reacts fast with water (B) Generates less heat of hydration (C) Causes initial setting and early strength of cement (D) Does not contribute to develop ultimate strength

Description : Tricalcium aluminate (C3A) (A) Reacts fast with water (B) Generates less heat of hydration (C) Causes initial setting and early strength of cement (D) Does not contribute to develop ultimate strength

Last Answer : Answer: Option B

The heat of hydration for low heat cement at the age of 7 days shall not exceed [ A ] 80 cal / gm [ B ] 75 cal / gm [ C ] 70 cal / gm [ D ] 65 cal / gm

Description : The heat of hydration for low heat cement at the age of 7 days shall not exceed [ A ] 80 cal / gm [ B ] 75 cal / gm [ C ] 70 cal / gm [ D ] 65 cal / gm

Last Answer : [ D ] 65 cal / gm

You are asked to construct a massive dam, the type of cement you will use, is (A) Ordinary Portland cement (B) Rapid hardening cement (C) Low heat cement (D) Blast furnace slag cement

Description : You are asked to construct a massive dam, the type of cement you will use, is (A) Ordinary Portland cement (B) Rapid hardening cement (C) Low heat cement (D) Blast furnace slag cement

Last Answer : Answer: Option C

For the construction of thin R.C.C. structures, the type of cement to be avoided, is (A) Ordinary Portland cement (B) Rapid hardening cement (C) Low heat cement (D) Blast furnace slag cement

Description : For the construction of thin R.C.C. structures, the type of cement to be avoided, is (A) Ordinary Portland cement (B) Rapid hardening cement (C) Low heat cement (D) Blast furnace slag cement

Last Answer : Answer: Option D

For road pavements, the cement generally used, is (A) Ordinary Portland cement (B) Rapid hardening cement (C) Low heat cement (D) Blast furnace slag cement

Description : For road pavements, the cement generally used, is (A) Ordinary Portland cement (B) Rapid hardening cement (C) Low heat cement (D) Blast furnace slag cement

Last Answer : Answer: Option B

Portland cement manufactured from pure white chalk and clay but free from iron-oxide, is known as (A) Quick setting cement (B) Rapid hardening cement (C) White cement (D) Low heat Portland cement

Description : Portland cement manufactured from pure white chalk and clay but free from iron-oxide, is known as (A) Quick setting cement (B) Rapid hardening cement (C) White cement (D) Low heat Portland cement

Last Answer : Answer: Option C

Which of the following cements is suitable for use in massive concrete structures such as large dams? (A) Ordinary Portland cement (B) Low heat cement (C) Rapid hardening cement (D) Sulphate resisting cement

Description : Which of the following cements is suitable for use in massive concrete structures such as large dams? (A) Ordinary Portland cement (B) Low heat cement (C) Rapid hardening cement (D) Sulphate resisting cement

Last Answer : Answer: Option B

Which of the following cements contains maximum percentage of dicalcium silicate? (A) Ordinary Portland cement (B) Low heat cement (C) Rapid hardening cement (D) Sulphate resisting cement

Description : Which of the following cements contains maximum percentage of dicalcium silicate? (A) Ordinary Portland cement (B) Low heat cement (C) Rapid hardening cement (D) Sulphate resisting cement

Last Answer : Answer: Option B

For mass concrete work, the type of cement preferable is [ A ] Ordinary Portland cement [ B ] Rapid hardening cement [ C ] Low heat cement [ D ] Blast furnace slag cement

Description : For mass concrete work, the type of cement preferable is [ A ] Ordinary Portland cement [ B ] Rapid hardening cement [ C ] Low heat cement [ D ] Blast furnace slag cement

Last Answer : [ C ] Low heat cement

For road pavements, the cement generally used, is [ A ] Ordinary Portland cement [ B ] Rapid hardening cement [ C ] Low heat cement [ D ] Blast furnace slag cement

Description : For road pavements, the cement generally used, is [ A ] Ordinary Portland cement [ B ] Rapid hardening cement [ C ] Low heat cement [ D ] Blast furnace slag cement

Last Answer : [ A ] Ordinary Portland cement

Low heat cement contains more amount of __________ than that of ordinary Portland cement [ A ] C3S [ B ] C2S [ C ] C3A [ D ] None of the above

Description : Low heat cement contains more amount of __________ than that of ordinary Portland cement [ A ] C3S [ B ] C2S [ C ] C3A [ D ] None of the above

Last Answer : [ B ] C2S

Pick up the incorrect statement from the following: (A) Tricalcium silicate (C3S) hydrates rapidly (B) Tricalcium silicate (C3S) generates more heat of hydration (C) Tricalcium silicate (C3S) develops early strength (D) Tricalcium silicate (C3S) has more resistance to sulphate attac

Description : Pick up the incorrect statement from the following: (A) Tricalcium silicate (C3S) hydrates rapidly (B) Tricalcium silicate (C3S) generates more heat of hydration (C) Tricalcium silicate (C3S) develops early strength (D) Tricalcium silicate (C3S) has more resistance to sulphate attack

Last Answer : Answer: Option D

The shrinkage of concrete (A) Is proportional to water content is the mix (B) Is proportional to cement concrete (C) Increases with age of concrete (D) All the above

Description : The shrinkage of concrete (A) Is proportional to water content is the mix (B) Is proportional to cement concrete (C) Increases with age of concrete (D) All the above

Last Answer : (D) All the above

Shrinkage in concrete can be reduced by using (A) Low water cement ratio (B) Less cement in the concrete (C) Proper concrete mix (D) All the above

Description : Shrinkage in concrete can be reduced by using (A) Low water cement ratio (B) Less cement in the concrete (C) Proper concrete mix (D) All the above

Last Answer : Answer: Option D

Consider the following statements: Cement mortars richer than 1 : 3 are not used in masonry work because 1. There is no gain in strength of masonry 2. There is high shrinkage 3. They are prone to segregation Which of these statements are correct? (a) 1, 2 and 3 (b) 1 and 2 only (c) 2 and 3 only (d) 1 and 3 only

Description : Consider the following statements: Cement mortars richer than 1 : 3 are not used in masonry work because 1. There is no gain in strength of masonry 2. There is high shrinkage 3. They are prone to segregation Which of these statements ... 1, 2 and 3 (b) 1 and 2 only (c) 2 and 3 only (d) 1 and 3 only

Last Answer : (b) 1 and 2 only

Which one of the following statements is not correct with respect to PSC beams? (a) Loss due to shrinkage is proportional to water-cement ratio used in concrete (b) Loss due to creep is proportional to the age of the member at the time of loading. (c) Loss due to elastic deformation is directly proportionally to the modulus of elasticity of concrete (d) Loss due to friction occurs in post tensioned concrete members

Description : Which one of the following statements is not correct with respect to PSC beams? (a) Loss due to shrinkage is proportional to water-cement ratio used in concrete (b) Loss due to creep is ... to the modulus of elasticity of concrete (d) Loss due to friction occurs in post tensioned concrete members

Last Answer : (c) Loss due to elastic deformation is directly proportionally to the modulus of elasticity of concrete

Shrinkage of concrete is mostly influenced by [ A ] Environmental conditions [ B ] Size of member [ C ] Cement in concrete [ D ] The total amount of water present in concrete

Description : Shrinkage of concrete is mostly influenced by [ A ] Environmental conditions [ B ] Size of member [ C ] Cement in concrete [ D ] The total amount of water present in concrete

Last Answer : [ D ] The total amount of water present in concrete

Shrinkage in concrete can be reduced by using (i) Low water cement ratio (ii) More amount of cement in the concrete (iii) Presaturated aggregates [ A ] i [ B ] i and ii [ C ] i and iii [ D ] i, ii and iii

Description : Shrinkage in concrete can be reduced by using (i) Low water cement ratio (ii) More amount of cement in the concrete (iii) Presaturated aggregates [ A ] i [ B ] i and ii [ C ] i and iii [ D ] i, ii and iii

Last Answer : [ C ] i and iii

When each particle of aggregates is thinly coated with cement paste, a heterogeneous solid is formed, which is known as (A) Hydration (B) Gel (C) Concrete (D) None of these

Description : When each particle of aggregates is thinly coated with cement paste, a heterogeneous solid is formed, which is known as (A) Hydration (B) Gel (C) Concrete (D) None of these

Last Answer : Answer: Option C

The condition not applicable to water cement ratio law, is (A) Internal moisture conditions on hydration continue till complete strength is gained (B) Concrete specimens may be tested at any temperature (C) Concrete specimens need be of same age (D) Concrete specimens need be of same size

Description : The condition not applicable to water cement ratio law, is (A) Internal moisture conditions on hydration continue till complete strength is gained (B) Concrete specimens may be tested at any temperature (C) Concrete specimens need be of same age (D) Concrete specimens need be of same size

Last Answer : Answer: Option B