The manner of loading and the rate of loading promote the transition from ductile to brittle fracture. A machine member may have ductile failure under static loading but may fail in brittle fashion when the load is fluctuating. Similarly a material may evidence ductile failure under tensile loading at ordinary testing speed, but if the load is applied at a high velocity then failure may be brittle.