High content copper amalgam . . . a. generally requires greater energy to accomplish trituration b. should be placed rapidly in large increments c. Continues to leak since the corrosion products do not form d. does not cause galvanism in oral environment e. is equally effective as conventional alloys in clinical studies

High content copper amalgam . . .  
a. generally requires greater energy to accomplish trituration  
b. should be placed rapidly in large increments  
c. Continues to leak since the corrosion products do not form  
d. does not cause galvanism in oral environment  
e. is equally effective as conventional alloys in clinical studies
by

1 Answer

Answer :

a. generally requires greater energy to accomplish trituration
by

Related questions

Corrosion and discolouration of amalgam restorations is usually caused by: A. Sulphur oxides B. Oxygen C. Chlorides D. Over trituration

Description : Corrosion and discolouration of amalgam restorations is usually caused by: A. Sulphur oxides B. Oxygen C. Chlorides D. Over trituration

Last Answer : A. Sulphur oxides

High copper amalgam lasts longer than low copper amalgam because of:** A. Increased compressive strength B. Increased corrosion resistance C. High creep D. Increased tensile strength E. Decreased setting expansion

Description : High copper amalgam lasts longer than low copper amalgam because of:**  A. Increased compressive strength  B. Increased corrosion resistance  C. High creep  D. Increased tensile strength  E. Decreased setting expansion 

Last Answer : A. Increased compressive strength 

.The main advantage of amalgam with high content of Cu is: A. Better marginal sealing B. Less corrosion C. Better tensile strength D. Higher and immediate compressive strength

Description : .The main advantage of amalgam with high content of Cu is: A. Better marginal sealing B. Less corrosion C. Better tensile strength D. Higher and immediate compressive strength

Last Answer : B. Less corrosion

The less mercury remaining in condensed amalgam: A. The stronger the restoration which contains fewer matrix alloys and fewer voids B. The weaker the restoration C. The more matrix alloys D. The more voids E. None of the above

Description : The less mercury remaining in condensed amalgam: A. The stronger the restoration which contains fewer matrix alloys and fewer voids B. The weaker the restoration C. The more matrix alloys D. The more voids E. None of the above

Last Answer : A. The stronger the restoration which contains fewer matrix alloys and fewer voids

Alloys having more than 80% copper are generally more (A) Abrasion resistant (B) Corrosion resistant (C) Prone to season cracking (D) Machinable

Description : Alloys having more than 80% copper are generally more (A) Abrasion resistant (B) Corrosion resistant (C) Prone to season cracking (D) Machinable

Last Answer : (B) Corrosion resistant

Oral mucosal pigmentation; what is TRUE: a. Commonly depends on ethnicity. b. Commonly an amalgam tattoo. c. Commonly oral melanoma. d. Commonly melanotic naevus.

Description : Oral mucosal pigmentation; what is TRUE: a. Commonly depends on ethnicity. b. Commonly an amalgam tattoo. c. Commonly oral melanoma. d. Commonly melanotic naevus.

Last Answer : a. Commonly depends on ethnicity.

What is TRUE about Oral mucosal pigmentation;: A. Commonly seen in ethnic groups B. Commonly an amalgam tattoo C. Commonly oral melanoma D. Commonly melanotic naevus What is TRUE about Oral mucosal pigmentation;: A. Commonly seen in ethnic groups B. Commonly an amalgam tattoo C. Commonly oral melanoma D. Commonly melanotic naevus

Description : What is TRUE about Oral mucosal pigmentation;: A. Commonly seen in ethnic groups B. Commonly an amalgam tattoo C. Commonly oral melanoma D. Commonly melanotic naevus

Last Answer : A. Commonly seen in ethnic groups

When incrementally placing a large composite resin restoration, what effect does an air-inhibited layer on the surface of the first increment have on the bond between the first and the second increments? A. It has no effect on the bond B. It is desirable and improves the bond C. It is undesirable and should be removed

Description : When incrementally placing a large composite resin restoration, what effect does an air-inhibited layer on the surface of the first increment have on the bond between the first and the second increments? A. ... B. It is desirable and improves the bond C. It is undesirable and should be removed

Last Answer : B. It is desirable and improves the bond

What is correct in regard to high copper amalgam, A. Reacts and strengthens the amalgam by its dispersion properties B. Reacts to form copper-tin phase thereby eliminating the tin-mercury phase C. Reacts to form copper-silver phase thereby eliminating the silver mercury phase D. Reacts and strengthens the amalgam by its grain diffusion

Description : What is correct in regard to high copper amalgam, A. Reacts and strengthens the amalgam by its dispersion properties B. Reacts to form copper-tin phase thereby eliminating the tin-mercury ... thereby eliminating the silver mercury phase D. Reacts and strengthens the amalgam by its grain diffusion

Last Answer : B. Reacts to form copper-tin phase thereby eliminating the tin-mercury phase

Which one of following statement about Overdenture is not correct: A. Greater occlusal loads can be applied by the patient B. Retention and stability are generally better than with conventional complete denture C. Alveolar bone resorption is reduced D. The retained roots are covered by the denture thus protecting them from caries and periodontal diseases

Description : Which one of following statement about Overdenture is not correct: A. Greater occlusal loads can be applied by the patient B. Retention and stability are generally better than with ... The retained roots are covered by the denture thus protecting them from caries and periodontal diseases

Last Answer : D. The retained roots are covered by the denture thus protecting them from caries and periodontal diseases

What is the property of high copper amalgam A. Reduced physical creep B. Higher retention

Description : What is the property of high copper amalgam A. Reduced physical creep B. Higher retention

Last Answer : A. Reduced physical creep

The cervical finish line of a full veneer crown preparation should be placed: A. Just supragingival whenever is possible B. According to the depth of gingival crevice C. Subgingival to reduce ability of recurrent caries D. At the junction of tooth and amalgam core

Description : The cervical finish line of a full veneer crown preparation should be placed: A. Just supragingival whenever is possible B. According to the depth of gingival crevice C. Subgingival to reduce ability of recurrent caries D. At the junction of tooth and amalgam core

Last Answer : A. Just supragingival whenever is possible

The retention pin in an amalgam restoration should be placed, A. Parallel to the outer wall B. Parallel to the long axis of tooth

Description : The retention pin in an amalgam restoration should be placed, A. Parallel to the outer wall B. Parallel to the long axis of tooth

Last Answer : A. Parallel to the outer wall

Choose a statement that correctly defines the term AMALGAM: A. Amalgam is a metallic powder composed of silver, tin, copper and zinc B. Amalgam is an alloy of two or more metals that have been dissolved in each other in the molten state. C. Amalgam is an alloy of two or more metals, one of them is mercury D. Amalgam is a metallic substance in powder or tablet from that is mixed with mercury E. Amalgam is an alloy of two or more metals, one of them is tin

Description : Choose a statement that correctly defines the term AMALGAM: A. Amalgam is a metallic powder composed of silver, tin, copper and zinc B. Amalgam is an alloy of two or more metals that have been dissolved in ... is mixed with mercury E. Amalgam is an alloy of two or more metals, one of them is tin

Last Answer : C. Amalgam is an alloy of two or more metals, one of them is mercury

he dominant pharmacokinetic feature of penicillin G is: A. It is equally distributed extra- and intracellularly B. It is rapidly secreted by proximal renal tubules C. It has low oral bioavailability due to high first pass metabolism in liver D. It does not cross blood–CSF barrier even when meninges are inflamed

Description : he dominant pharmacokinetic feature of penicillin G is: A. It is equally distributed extra- and intracellularly B. It is rapidly secreted by proximal renal tubules C. It has low oral bioavailability ... pass metabolism in liver D. It does not cross blood-CSF barrier even when meninges are inflamed

Last Answer : B. It is rapidly secreted by proximal renal tubules

Which of the following statement about the defective margins of amalgam restorations is true?+M07 A. The larger the breakdown, the greater the chance of decay. IF THERE IS MARGINAL BREAKDOWN THIS DOSNT NECESSITATE THE PRESENCE OF CARIES ALONG MARGIN So the ans is Chances are increased

Description : Which of the following statement about the defective margins of amalgam restorations is true?+M07 A. The larger the breakdown, the greater the chance of decay. IF THERE IS MARGINAL BREAKDOWN THIS DOSNT NECESSITATE THE PRESENCE OF CARIES ALONG MARGIN So the ans is Chances are increased

Last Answer : A. The larger the breakdown, the greater the chance of decay.

A large amalgam core is to be condensed around several pins in a vital molar tooth; what type of amalgam mix would you prefer: A. A large mix to ensure homogeneity B. A large with extra mercury to give easier manipulative qualities C. Several small mixes, sequentially triturated D. Several small mixes with varying mercury/alloy ratios E. A basic mix to which additional mercury is added as needed

Description : A large amalgam core is to be condensed around several pins in a vital molar tooth; what type of amalgam mix would you prefer: A. A large mix to ensure homogeneity B. A large with ... small mixes with varying mercury/alloy ratios E. A basic mix to which additional mercury is added as needed

Last Answer : C. Several small mixes, sequentially triturated

The principle cause of failure of amalgam restoration is: A. Improperly prepared amalgam B. Improper cavity preparation C. Perio involvement D. Particles of amalgam

Description : The principle cause of failure of amalgam restoration is: A. Improperly prepared amalgam B. Improper cavity preparation C. Perio involvement D. Particles of amalgam

Last Answer : B. Improper cavity preparation

The most common cause of fracture at the isthmus of class II dental amalgam restoration is: A. Delayed expansion B. Inadequate depth at the isthmus area C. Inadequate width at the isthmus area

Description : The most common cause of fracture at the isthmus of class II dental amalgam restoration is: A. Delayed expansion B. Inadequate depth at the isthmus area C. Inadequate width at the isthmus area

Last Answer : B. Inadequate depth at the isthmus area

Hastelloy C is a good material of construction in chemical process industry, since it is (A) Highly corrosion resistant and is readily fabricated (B) Relatively inexpensive although it can be fabricated with some difficulty (C) Corrosion resistant to most alkalis, particularly because of its copper content (D) Light and resists attack by acids

Description : Hastelloy C is a good material of construction in chemical process industry, since it is (A) Highly corrosion resistant and is readily fabricated (B) Relatively inexpensive although it can be ... most alkalis, particularly because of its copper content (D) Light and resists attack by acids

Last Answer : (D) Light and resists attack by acids

The use of antibiotics can be based on either the clinical course of a patient without the benefit of well-defined microbiologic data (empiric therapy), or targeted at specific identified pathogens once sensitivity reports are available (directed therapy). The following statement(s) is/are true concerning these therapies. a. The issue of toxic side effects of antibiotics is only important in dealing with emperic therapy b. Single agent therapy is generally inferior to specific multi-drug therapy (aminoglycoside plus an antianaerobic agent) for the treatment of secondary bacterial peritonitis due to appendicitis, diverticulitis, penetrating gastrointestinal injury, or anastomotic leak c. With the empiric use of antibiotics, a diligent search for the septic source should be undertaken and co

Description : The use of antibiotics can be based on either the clinical course of a patient without the benefit of well-defined microbiologic data (empiric therapy), or targeted at ... which polymicrobial infection is identified, specifically-directed treatment for the predominant organism is satisfactory

Last Answer : Answer: c The use of empiric therapy without the benefit of well-defined microbiologic data is appropriate when there is sufficient clinical evidence to support the diagnosis such that it would ... components of the infection if the body site is such that these microorganisms may be present

A major difference between light cured and chemical cured composite is that during setting or in function the light cured material tends to:******** VERY IMP A. Seal the margins better and completely B. Exhibit less wear on time C. Undergo greater colour change D. Shrink more rapidly E. Posses greater fracture toughness

Description : A major difference between light cured and chemical cured composite is that during setting or in function the light cured material tends to:******** VERY IMP A. Seal the margins better and ... on time C. Undergo greater colour change D. Shrink more rapidly E. Posses greater fracture toughness

Last Answer : D. Shrink more rapidly

To reduce the risk of side effects of local anaesthetic injections; you should follow all of the following EXCEPT: A. Aspirate before injection B. Use the smallest effective volume C. Use the weakest efficient percentage strength D. Inject rapidly

Description : To reduce the risk of side effects of local anaesthetic injections; you should follow all of the following EXCEPT: A. Aspirate before injection B. Use the smallest effective volume C. Use the weakest efficient percentage strength D. Inject rapidly

Last Answer : D. Inject rapidly

The most common cause of caries in children is, A. Soft diet B. High intake of carbohydrate C. Poor oral hygiene

Description : The most common cause of caries in children is, A. Soft diet B. High intake of carbohydrate C. Poor oral hygiene

Last Answer : B. High intake of carbohydrate

Denture hyperplasia is generally attributed to: A. Poor oral hygiene B. Denture movement

Description : Denture hyperplasia is generally attributed to: A. Poor oral hygiene B. Denture movement

Last Answer : B. Denture movement

Choose the correct statement about use of βadrenergic blockers in CHF: A. All β blockers are equally effective in CHF B. They are used as alternative to conventional therapy with ACE inhibitors ± digitalis/ diuretic C. They are most useful in mild to moderate cases with systolic dysfunction due to dilated cardiomyopathy D. They are indicated only in asymptomatic left ventricular dysfunction

Description : Choose the correct statement about use of βadrenergic blockers in CHF: A. All β blockers are equally effective in CHF B. They are used as alternative to conventional therapy with ... dysfunction due to dilated cardiomyopathy D. They are indicated only in asymptomatic left ventricular dysfunction

Last Answer : C. They are most useful in mild to moderate cases with systolic dysfunction due to dilated cardiomyopathy

What sort of alloys do you use for bridges: A. Ductile B. Hard C. High sensitivity

Description : What sort of alloys do you use for bridges: A. Ductile B. Hard C. High sensitivity

Last Answer : B. Hard

The principal reasons for placing a gingival interproximal wedge in conjunction with a matrix for amalgam condensation are to: 1. separate the teeth slightly 2. keep the band tight at the gingival margin 3. contribute to the interproximal contact of the restoration 4. retract the gingival tissue a. 1,2,3 b. 1,2,4 c. 2,3,4 d. 1,3,4 e. all of the above

Description : The principal reasons for placing a gingival interproximal wedge in conjunction with a matrix for amalgam condensation are to: 1. separate the teeth slightly 2. keep the band tight at the gingival margin 3. contribute to the ... b. 1,2,4 c. 2,3,4 d. 1,3,4 e. all of the above

Last Answer : e. all of the above

Occasional sensitivity in a shallow class I amalgam restoration after two days would be managed by: A. Replace old filing immediately B. Oxide Zinc and eugenol C. Using thicker mix of cements D. Tell patient the discomfort will disappear after 4 t o6 weeks E. Ledermix

Description : Occasional sensitivity in a shallow class I amalgam restoration after two days would be managed by: A. Replace old filing immediately B. Oxide Zinc and eugenol C. Using thicker mix of cements D. Tell patient the discomfort will disappear after 4 t o6 weeks E. Ledermix

Last Answer : D. Tell patient the discomfort will disappear after 4 t o6 weeks

Function of matrix band: A. Substitute for the missing wall so adequate condensation forces can be applied B. Permit re-establishment of proper contact lines C. Restrict extrusion of amalgam and prevent formation of an “overhang” D. Provide adequate physiological contour for the proximal surface E. Provide an acceptable surface texture to the proximal surface F. All of the above

Description : Function of matrix band: A. Substitute for the missing wall so adequate condensation forces can be applied B. Permit re-establishment of proper contact lines C. Restrict extrusion of amalgam and prevent ... E. Provide an acceptable surface texture to the proximal surface F. All of the above

Last Answer : F. All of the above

Reduced occlusal area means: A. More fracture potential for amalgam B. Less fracture potential for amalgam C. Pulpal involvement D. Perio involvement E. None of the above

Description : Reduced occlusal area means: A. More fracture potential for amalgam B. Less fracture potential for amalgam C. Pulpal involvement D. Perio involvement E. None of the above

Last Answer : B. Less fracture potential for amalgam

The optimum cavosurface angle for occlusal amalgam surface is: A. 45-60° B. 70-85° C. 45-80° D. 95-110° E. 130-150°

Description : The optimum cavosurface angle for occlusal amalgam surface is: A. 45-60° B. 70-85° C. 45-80° D. 95-110° E. 130-150°

Last Answer : D. 95-110°

How much would you reduce a cusp to be replaced with amalgam onlay: A. 2 mm to achieve a good retention form B. 2mm to achieve a good resistance form C. 1mm

Description : How much would you reduce a cusp to be replaced with amalgam onlay: A. 2 mm to achieve a good retention form B. 2mm to achieve a good resistance form C. 1mm

Last Answer : B. 2mm to achieve a good resistance form

For an amalgam restoration of a weakened cusp you should, A. reduce cusp by 2mm on a flat base for more resistance B. reduce cusp by 2mm following the outline of the cusp C. reduce 2mm for retention form

Description : For an amalgam restoration of a weakened cusp you should, A. reduce cusp by 2mm on a flat base for more resistance B. reduce cusp by 2mm following the outline of the cusp C. reduce 2mm for retention form

Last Answer : A. reduce cusp by 2mm on a flat base for more resistance

.Which of the following is true: A. Antibiotics are useful in the treatment of periodontitis B. Trauma from occlusion causes thickening of the marginal gingivae C. Periodontitis is the primary cause of teeth lost after the age of 35. D. All periodontal pockets can be identified by x-ray E. Periodontitis is the most common disease in the oral cavity

Description : .Which of the following is true:  A. Antibiotics are useful in the treatment of periodontitis   B. Trauma from occlusion causes thickening of the marginal gingivae  C. Periodontitis is the ... can be identified by x-ray  E. Periodontitis is the most common disease in the oral cavity

Last Answer : E. Periodontitis is the most common disease in the oral cavity

In regard to external resorption:** A. Continues after successful endo treatment B. Stops in most cases following successful endodontic treatment C. Continues only in mandibular incisors after successful endo treatment D. Stops in maxillary lateral incisors after successful endodontic treatment E. None of the above

Description : In regard to external resorption:** A. Continues after successful endo treatment B. Stops in most cases following successful endodontic treatment C. Continues only in mandibular incisors after ... D. Stops in maxillary lateral incisors after successful endodontic treatment E. None of the above

Last Answer : B. Stops in most cases following successful endodontic treatment

Distortion or change in shape of a cast partial denture clasp during its clinical use probably indicates that the: A. Ductility was too low B. Hardness was too great C. Ultimate tensile strength was too low D. Tension temperature was too high E. Elastic limit was exceeded

Description : Distortion or change in shape of a cast partial denture clasp during its clinical use probably indicates that the: A. Ductility was too low B. Hardness was too great C. Ultimate tensile strength was too low D. Tension temperature was too high E. Elastic limit was exceeded

Last Answer : E. Elastic limit was exceeded

Amalgam restoration, when do you have to replace it? a. Ditching of the edges. b. The probe penetrates the area between the margin and tooth tissue. c. Fissure of the surface of the amalgam. d. When there is chronic inflammation of the pulp.

Description : Amalgam restoration, when do you have to replace it? a. Ditching of the edges. b. The probe penetrates the area between the margin and tooth tissue. c. Fissure of the surface of the amalgam. d. When there is chronic inflammation of the pulp.

Last Answer : c. Fissure of the surface of the amalgam.

Burnishing the amalgam after carving, what is the benefit? a.Completing the condensation at the marginal edges. b.eleminating excessive mercury

Description : Burnishing the amalgam after carving, what is the benefit? a.Completing the condensation at the marginal edges. b.eleminating excessive mercury

Last Answer : .Completing the condensation at the marginal edges.

In preparing a very small proximal amalgam cavity on a molar tooth what would consider, A. Extend the cavity to the gingival margin B. Extend the cavity beyond the contacts areas C. Achieve at least 2mm in dentine D. Extend cavity just beyond dento enamel junction

Description : In preparing a very small proximal amalgam cavity on a molar tooth what would consider, A. Extend the cavity to the gingival margin B. Extend the cavity beyond the contacts areas C. Achieve at least 2mm in dentine D. Extend cavity just beyond dento enamel junction

Last Answer : D. Extend cavity just beyond dento enamel junction

Which one of this restorative methods will be LEAST compromised by a core, A. Amalgam B. Composite C. GIC D. Cast gold

Description : Which one of this restorative methods will be LEAST compromised by a core, A. Amalgam B. Composite C. GIC D. Cast gold

Last Answer : D. Cast gold

After the placement of a class I amalgam the patient comes back to you complaining of pain on masticating and biting; what is the first thing you would look at, A. Occlusal height B. Contacts areas

Description : After the placement of a class I amalgam the patient comes back to you complaining of pain on masticating and biting; what is the first thing you would look at, A. Occlusal height B. Contacts areas

Last Answer : A. Occlusal height

In a posterior vital molar with a core the best material to restore is: A. Amalgam B. Composite resin C. GIC

Description : In a posterior vital molar with a core the best material to restore is: A. Amalgam B. Composite resin C. GIC

Last Answer : A. Amalgam

A vital tooth has a crown cemented to a pin-retained amalgam core; where does a failure occur: A. Between crown and cement B. Between core and cement C. In the crown and the root D. In the core and the margin preparation

Description : A vital tooth has a crown cemented to a pin-retained amalgam core; where does a failure occur: A. Between crown and cement B. Between core and cement C. In the crown and the root D. In the core and the margin preparation

Last Answer : B. Between core and cement

In regard to marginal leakage in amalgam: A. The wider the gap the better the chance of secondary caries B. Seal the margin with fissure sealant would prevent further breakdown C. Secondary caries may develop

Description : In regard to marginal leakage in amalgam: A. The wider the gap the better the chance of secondary caries B. Seal the margin with fissure sealant would prevent further breakdown C. Secondary caries may develop

Last Answer : A. The wider the gap the better the chance of secondary caries

At what angle to the external surface should proximal cavosurface walls in Class II preparation for the reception of an amalgam filling be finished: A. Acute angle B. Right angle C. Obtuse angle D. 45 angle

Description : At what angle to the external surface should proximal cavosurface walls in Class II preparation for the reception of an amalgam filling be finished: A. Acute angle B. Right angle C. Obtuse angle D. 45 angle

Last Answer : C. Obtuse angle

When is a gingival groove LEAST required: A. When restoring with GIC for abrasion B. When restoring with GIC for root caries C. When restoring with GIC base and composite lamination D. When restoring with amalgam

Description : When is a gingival groove LEAST required: A. When restoring with GIC for abrasion B. When restoring with GIC for root caries C. When restoring with GIC base and composite lamination D. When restoring with amalgam

Last Answer : C. When restoring with GIC base and composite lamination

Retention for occlusal amalgam cavities in premolars is BEST provided by A. Slightly undercutting of walls with inversed cone bur B. Mesial and distal undercuts C. Buccal and lingual undercuts

Description : Retention for occlusal amalgam cavities in premolars is BEST provided by A. Slightly undercutting of walls with inversed cone bur B. Mesial and distal undercuts C. Buccal and lingual undercuts

Last Answer : C. Buccal and lingual undercuts

Pin Restoration with which material has the best retention: A. Amalgam B. Gold inlay C. Composite D. Glass Ionomer

Description : Pin Restoration with which material has the best retention:  A. Amalgam  B. Gold inlay  C. Composite  D. Glass Ionomer 

Last Answer : C. Composite