Description : Which of the following cements contains maximum percentage of dicalcium silicate? (A) Ordinary Portland cement (B) Low heat cement (C) Rapid hardening cement (D) Sulphate resisting cement
Last Answer : Answer: Option B
Description : You are asked to construct a massive dam, the type of cement you will use, is (A) Ordinary Portland cement (B) Rapid hardening cement (C) Low heat cement (D) Blast furnace slag cement
Last Answer : Answer: Option C
Description : The cement whose strength is a little lower than the ordinary cement during the first three months but attains afterwards the same strength, is known as (A) Low-heat Portland cement (B) Rapid hardening Portland cement (C) Portland blast slag cement (D) Portland pozzolana cement
Last Answer : Answer: Option A
Description : For the construction of thin R.C.C. structures, the type of cement to be avoided, is (A) Ordinary Portland cement (B) Rapid hardening cement (C) Low heat cement (D) Blast furnace slag cement
Last Answer : Answer: Option D
Description : For road pavements, the cement generally used, is (A) Ordinary Portland cement (B) Rapid hardening cement (C) Low heat cement (D) Blast furnace slag cement
Description : Which of the following cements is suitable for use in massive concrete structures such as large dams? (A) Ordinary Portland cement (B) Low heat cement (C) Rapid hardening cement (D) Sulphate resisting cement
Description : Which of the following cements is expected to have the highest compressive strength after 3 days (a) Ordinary Portland cement (b) Rapid hardening cement (c) High alumina cement (d) Sulphate resisting cement.
Last Answer : (c) High alumina cement
Description : For mass concrete work, the type of cement preferable is [ A ] Ordinary Portland cement [ B ] Rapid hardening cement [ C ] Low heat cement [ D ] Blast furnace slag cement
Last Answer : [ C ] Low heat cement
Description : For road pavements, the cement generally used, is [ A ] Ordinary Portland cement [ B ] Rapid hardening cement [ C ] Low heat cement [ D ] Blast furnace slag cement
Last Answer : [ A ] Ordinary Portland cement
Description : Rapid hardening cement attains early strength due to (A) Larger proportion of lime grounded finer than normal cement (B) Lesser proportion of lime grounded coarser than normal cement (C) Lesser proportion of lime grounded finer than normal cement (D) Excess percentage of gypsum
Description : The high strength of rapid hardening cement at early stage, is due to its (A) Finer grinding (B) Burning at high temperature (C) Increased lime cement (D) Higher content of tricalcium
Description : For construction of structures in sea water, the cement generally preferred to, is (A) Portland-pozzolana cement (B) Quick setting cement (C) Low heat Portland cement (D) Rapid hardening cement
Description : Portland cement manufactured from pure white chalk and clay but free from iron-oxide, is known as (A) Quick setting cement (B) Rapid hardening cement (C) White cement (D) Low heat Portland cement
Description : Low heat cement contains more amount of __________ than that of ordinary Portland cement [ A ] C3S [ B ] C2S [ C ] C3A [ D ] None of the above
Last Answer : [ B ] C2S
Description : Which cement should not be used for bridge slabs ro RCC frames a) OPC b) Portland Pozzolana cement * c) Portland furnace slag cement d) Rapid hardening cement
Last Answer : b) Portland Pozzolana cement *
Description : Ordinary Portland cement is manufactured from (A) Lime stone and clay (B) Gypsum and lime (C) Pozzolana (D) Lime, pozzolana and clay
Description : Chief constituent of ordinary Portland cement is [ A ] Lime [ B ] Alumina [ C ] Magnesia [ D ] Iron oxide
Last Answer : [ A ] Lime
Description : As compared to ordinary Portland cement, use of pozzolana cement (A) Reduces workability (B) Increases bleeding (C) Increases shrinkage (D) Increases strength
Description : As compared to ordinary Portland cement, high alumina cement has (A) Higher initial setting time but lower final setting time (B) Lower initial setting time but higher final setting time (C) Higher initial and final setting times (D) Lower initial and final setting times
Description : Rapid hardening cement contains (A) Tri-calcium silicate (B) Tri-calcium aluminate (C) Tetra-calcium alumino-ferrite (D) Di-calcium silicate
Description : (3) preventing rapid setting of cement Explanation: Portland cement clinker is a hydraulic material which shall consist of at least two-thirds by mass of calcium silicates, the remainder consisting of ... mixed with water by way of a complex series of chemical reactions still only partly understood.
Last Answer : Milk is a colloidal system in which: (1) Water is dispersed in fat (2) Fat is dispersed in water (3) Fat and water are dispersed in each other (4) Fat is dissolved
Description : Hardening of cement occurs at (A) Rapid rate during the first few days and afterwards it continues to increase at a decreased rate (B) Slow rate during the first few days and afterwards it continues to increase at a rapid rate (C) Uniform rate throughout its age (D) None of these
Description : Pick up the correct statement from the following: (A) High percentage of C3S and low percentage of C2S cause rapid hardening (B) High percentage of C3S and low percentage of C2S make the cement ... ) Low percentage of C3S and high percentage of C2S contribute to slow hardening (D) All the above
Description : Name the type of cement from the following for canal linings: (A) Sulphate resisting cement (B) Rapid hardening cement (C) Quick setting cement (D) Pozzolana cement
Description : Early attainment of strength in rapid hardening cement is mainly due to (A) Gypsum (B) Finer grinding (C) Tri-calcium silicate (D) Tri-calcium aluminate
Description : Which of the following statements is correct? (a) Sulphate resisting cement is particularly used for canal lining. (b) Low heat cement should not be used for thin concrete structures. (c) Rapid hardening cement should not be used for massive concrete structures (d) All of the above
Last Answer : (d) All of the above
Description : Rapid hardening cement is used (a) Where high early strength is desired (b) Where form work is to be removed as early as possible (c) For construction of road pavements. (d) All of the above
Description : High percentage of tricalcium silicate and low percentage of dicalcium silicate in cement results in. (a) Rapid hardening (b) High early strength (c) High heat of generation (d) All the above
Last Answer : (d) All the above
Description : Newly constructed pavement with ordinary Portland cement attains its working strength after (A) 7 days (B) 14 days (C) 21 days (D) 28 days
Description : An ordinary Portland cement when tested for its fineness, should not leave any residue on I.S. sieve No. 9, more than (A) 5 % (B) 10 % (C) 15 % (D) 20 %
Last Answer : (B) 10 %
Description : For an ordinary Portland cement (A) Residual does not exceed 10% when sieved through IS Sieve No. 9 (B) Soundness varies from 5 to 10 mm (C) Initial setting time is not less than 30 minutes (D) Compressive stress after 7 days, is not less than 175 kg/cm2
Last Answer : (C) Initial setting time is not less than 30 minutes
Description : The normal consistency of ordinary Portland cement is about (A) 10 % (B) 20 % (C) 30 % (D) 40 %
Description : Addition of pozzolana to ordinary Portland cement increases (A) Bleeding (B) Shrinkage (C) Permeability (D) Heat of hydration
Description : According to IS specifications, the compressive strength of ordinary Portland cement after three days should not be less than (A) 7 MPa (B) 11.5 MPa (C) 16 MPa (D) 21 MPa
Description : As per IS specifications, the maximum final setting time for ordinary Portland cement should be (A) 30 minutes (B) 1 hour (C) 6 hours (D) 10 hour
Description : The initial setting time for ordinary Portland cement as per IS specifications should not be less than (A) 10 minutes (B) 30 minutes (C) 60 minutes (D) 600 minutes
Description : The compressive strength an ordinary Portland cement (1:3) after 7 days test should not be less than. (a) 11N/mm2 (b) 17.5 N/mm2 (c) 22 N/mm2 (d) 27.5N/m2
Last Answer : (b) 17.5 N/mm2
Description : According to IS Code , the requirement of an ordinary Portland cement is (a) The residue does not exceed 10% when sieved through is sieve no .9 (b) Its initial setting time is not less than 30 minutes. (c) its expansion is not morethan 10mm for unaerated cement (d) All the above.
Last Answer : (d) All the above.
Description : For Ordinary Portland cement concrete exposed to dry and hot weather conditions, good moist curing period is [ A ] 7 days [ B ] 10 days [ C ] 14 days [ D ] None of the above
Last Answer : [ B ] 10 days
Description : Minimum compressive strength of cement required at the age of 3 days for ordinary Portland cement of grade 33 is [ A ] 1.15 N/mm2 [ B ] 11.5 N/mm2 [ C ] 2.10 N/mm2 [ D ] 21 N/mm2
Last Answer : [ B ] 11.5 N/mm2
Description : Ordinary Portland cement requires a specific surface of [ A ] 1250 cm2/gm [ B ] 2250 cm 2/gm [ C ] 3250 cm 2/gm [ D ] 3500 cm 2/gm
Last Answer : [ B ] 2250 cm 2/gm
Description : For the manufacture of Portland cement, the proportions of raw materials used, are (A) Lime 63% ; silica 22% ; other ingredients 15% (B) Lime 22% ; silica 63% ; other ingredients 15% (C) Silica 40% ; lime 40% ; other ingredients 20% (D) Silica 70% ; lime 20% ; other ingredients 10%
Description : The main ingredients of Portland cement are (A) Lime and silica (B) Lime and alumina (C) Silica and alumina (D) Lime and iron
Description : The proportion of lime, silica, alumina and iron oxide in a Portland cement is (a) 63:22:6:3 (b) 63:22:3:6 (c) 22:63:6:3 (d) All the above
Last Answer : (a) 63:22:6:3
Description : When compared with the co-latitude of the place of observation, the declination of a circumpolar star is always, (a) Lesser (b) Greater (c) Equal (d) Either lesser or equal
Last Answer : (b) Greater
Description : While compared with singly reinforced beams, the depth of doubly reinforced beam is [ A ] Greater [ B ] Lesser [ C ] almost equal [ D ] twice
Last Answer : [ B ] Lesser
Description : White cement contains less amount of ___________ [ A ] Lime [ B ] Silica [ C ] Alumina [ D ] Iron oxide
Last Answer : [ D ] Iron oxide
Description : Which type of following cement is used for mass concrete work a) High Alumina cement b) Quick setting cement c) Rapid hardening cement d) Low heat cement*
Last Answer : d) Low heat cement*
Description : The addition of gypsum to portland cement helps in : (1) increasing the strength of cement (2) rapid setting of cement (3) preventing rapid setting of cement (4) reduction in the cost of cement
Last Answer : preventing rapid setting of cement
Description : Formation of ordinary Portland cement?
Last Answer : Ordinary Portland cement is form from materials of limestone or chalk and clay in proportion of 78and 22% respectively. The limestone and the clay are crushed and water is added to form slurry. The ... powder and a range of gypsum is added which generate setting or hardening when water is added.