Pick out the wrong statement. (A) Both annealing and normalising release the internal stresses of the material besides improving the mechanical properties (B) Low carbon steel does not respond to the heat treatment for hardening of the material, hence it is subjected to case hardening or surface hardening processes like cyaniding, carburising, nitriding etc., which produces high carbon outer layers resulting in increase of surface hardness (C) Induction hardening and flame hardening techniques are also used for surface hardening (D) Martempering of a material is a hardening process

Pick out the wrong statement.
(A) Both annealing and normalising release the internal stresses of the
material besides improving the mechanical properties
(B) Low carbon steel does not respond to the heat treatment for hardening of
the material, hence it is subjected to case hardening or surface hardening
processes like cyaniding, carburising, nitriding etc., which produces high carbon
outer layers resulting in increase of surface hardness
(C) Induction hardening and flame hardening techniques are also used for
surface hardening
(D) Martempering of a material is a hardening process
by

1 Answer

Answer :

Option C
by

Related questions

__________ is not a case hardening process.(A) Carburising (B) Nitriding (C) Cyaniding (D) Annealing

Description : __________ is not a case hardening process. (A) Carburising (B) Nitriding (C) Cyaniding (D) Annealing

Last Answer : (D) Annealing

Pick out the correct statement. (A) Hot worked materials are subjected to annealing to remove internal stresses (B) Annealing of steel hardens it slightly (C) Normalising of a material induces stresses (D) Tempering of a material improves ductility & toughness but reduces hardness & brittleness

Description : Pick out the correct statement. (A) Hot worked materials are subjected to annealing to remove internal stresses (B) Annealing of steel hardens it slightly (C) Normalising of a material induces stresses (D) Tempering of a material improves ductility & toughness but reduces hardness & brittleness

Last Answer : (D) Tempering of a material improves ductility & toughness but reduces hardness & brittleness Share

Nitriding of steel is a process for (A) Case hardening (B) Spheroidising (C) Normalising (D) Annealing

Description : Nitriding of steel is a process for (A) Case hardening (B) Spheroidising (C) Normalising (D) Annealing

Last Answer : (A) Case hardening

Which of the following heat treatment processes is usually applied to castings? (A) Tempering (B) Annealing (C) Normalising (D) Carburising

Description : Which of the following heat treatment processes is usually applied to castings? (A) Tempering (B) Annealing (C) Normalising (D) Carburising

Last Answer : (D) Carburising

Pick the odd man out of the following. (A) Calorising (B) Pack carburising (C) Nitriding (D) Cyaniding

Description : Pick the odd man out of the following. (A) Calorising (B) Pack carburising (C) Nitriding (D) Cyaniding

Last Answer : (A) Calorising

__________ of hard alloy and tool steel is done to make it easily machinable. (A) Case carburising (B) Tempering (C) Normalising (D) Annealing

Description : __________ of hard alloy and tool steel is done to make it easily machinable. (A) Case carburising (B) Tempering (C) Normalising (D) Annealing

Last Answer : (B) Tempering

Cold worked steel parts are normally subjected to (A) Normalising (B) Hardening (C) Annealing (D) Shot peening

Description : Cold worked steel parts are normally subjected to (A) Normalising (B) Hardening (C) Annealing (D) Shot peening

Last Answer : (C) Annealing

The heat treatment process to which castings and the steel balls produced by cold heading are subjected is (A) Tempering (B) Normalising (C) Annealing (D) None of these

Description : The heat treatment process to which castings and the steel balls produced by cold heading are subjected is (A) Tempering (B) Normalising (C) Annealing (D) None of these

Last Answer : (B) Normalising

Pick out the wrong statement. (A) Addition of methane to the furnace atmosphere reduces decarburising by hydrogen (B) Nitrogen in presence of steam decor-burises high carbon steel, whereas hydrocarbon gases carburise the surface of steel at annealing temperatures (C) Active nitrogen (formed by cracking ammonia at the metal surface) cause nitride formation with increase in surface hardness (D) None of these

Description : Pick out the wrong statement. (A) Addition of methane to the furnace atmosphere reduces decarburising by hydrogen (B) Nitrogen in presence of steam decor-burises high carbon steel, whereas hydrocarbon ... the metal surface) cause nitride formation with increase in surface hardness (D) None of these

Last Answer : (D) None of these

________ is not a heat treatment process. (A) Cyaniding (B) Parkerizing (C) Austempering (D) Martempering

Description : ________ is not a heat treatment process. (A) Cyaniding (B) Parkerizing (C) Austempering (D) Martempering

Last Answer : (B) Parkerizing

Case hardening of a material is (A) Followed by tempering or carburising (B) Preceded by its tempering (C) Done to get a soft ductile interior with a very hard surface (D) Carried out to get extreme hardness in its core

Description : Case hardening of a material is (A) Followed by tempering or carburising (B) Preceded by its tempering (C) Done to get a soft ductile interior with a very hard surface (D) Carried out to get extreme hardness in its core

Last Answer : (D) Carried out to get extreme hardness in its core

Hardened steel is softened by (A) Normalising (B) Tempering (C) Annealing (D) Carburising

Description : Hardened steel is softened by (A) Normalising (B) Tempering (C) Annealing (D) Carburising

Last Answer : (B) Tempering

Softening of hardened steel is done by its (A) Normalising (B) Tempering (C) Annealing (D) Carburising

Description : Softening of hardened steel is done by its (A) Normalising (B) Tempering (C) Annealing (D) Carburising

Last Answer : (B) Tempering

Softening of hardened steel is done by its (A) Normalising (B) Tempering (C) Annealing (D) Carburising

Description : Softening of hardened steel is done by its (A) Normalising (B) Tempering (C) Annealing (D) Carburising

Last Answer : (A) Normalising

Which of the following heat treatment processes is used for softening the hardened material? (A) Normalising (B) Tempering (C) Annealing (D) None of these

Description : Which of the following heat treatment processes is used for softening the hardened material? (A) Normalising (B) Tempering (C) Annealing (D) None of these

Last Answer : (B) Tempering

Spheroidising of a material is a/an __________ process. (A) Normalising (B) Annealing (C) Tempering (D) Hardening

Description : Spheroidising of a material is a/an __________ process. (A) Normalising (B) Annealing (C) Tempering (D) Hardening

Last Answer : (B) Annealing

Steel will respond to hardening by heat treatment processes, only when the minimum carbon content in it is __________ percent. (A) 0.02 (B) 0.2 (C) 0.35 (D) 0.5

Description : Steel will respond to hardening by heat treatment processes, only when the minimum carbon content in it is __________ percent. (A) 0.02 (B) 0.2 (C) 0.35 (D) 0.5

Last Answer : (B) 0.2

Pick out the wrong statement about the machinability of metals. Machinability of a metal (A) Decreases with increase in strain hardening tendencies (B) Decreases with increase in hardness, in general (C) Depend on the composition, microstructure and physical & mechanical

Description : Pick out the wrong statement about the machinability of metals. Machinability of a metal (A) Decreases with increase in strain hardening tendencies (B) Decreases with increase in hardness, in general (C) Depend on the composition, microstructure and physical & mechanical

Last Answer : Option C

While normal carburising and nitriding surface treatments increase fatigue strength, excessive treatment may decrease the fatigue strength. Why ?

Description : While normal carburising and nitriding surface treatments increase fatigue strength, excessive treatment may decrease the fatigue strength. Why ?

Last Answer : .Normal carburising/nitriding treatments increase volume due to phase transformation at Surface and introduce residual compressive surface stress and thus increase the fatigue strength. By excessive treatment the ... develop in the regions of high tensile stress and lead to early fatigue failure.

The heat treatment process applied to cold formed steel parts is (A) Normalising (B) Tempering (C) Artificial ageing (D) Solution annealing

Description : The heat treatment process applied to cold formed steel parts is (A) Normalising (B) Tempering (C) Artificial ageing (D) Solution annealing

Last Answer : (D) Solution annealing

Which of the following processes follows the hardening process for reducing the hardening strains & increasing the toughness of the steel part? (A) Anodising (B) Tempering (C) Carburising

Description : Which of the following processes follows the hardening process for reducing the hardening strains & increasing the toughness of the steel part? (A) Anodising (B) Tempering (C) Carburising

Last Answer : (B) Tempering

Globular form of cementite is formed during the __________ process. (A) Spheroidising (B) Hardening (C) Annealing (D) Normalising

Description : Globular form of cementite is formed during the __________ process. (A) Spheroidising (B) Hardening (C) Annealing (D) Normalising

Last Answer : (B) Hardening

. To improve the machinability of steel, it is generally subjected to (A) Spheroidising (B) Tempering (C) Normalising (D) Annealing

Description : . To improve the machinability of steel, it is generally subjected to (A) Spheroidising (B) Tempering (C) Normalising (D) Annealing

Last Answer : (A) Spheroidising

o improve the machinability of steel, it is generally subjected to (A) Spheroidising (B) Tempering (C) Normalising (D) Annealing

Description : o improve the machinability of steel, it is generally subjected to (A) Spheroidising (B) Tempering (C) Normalising (D) Annealing

Last Answer : Option A

The increase in hardness of metal due to its cold working is termed as the __________ hardening. (A) Work (B) Age (C) Induction (D) Flame

Description : The increase in hardness of metal due to its cold working is termed as the __________ hardening. (A) Work (B) Age (C) Induction (D) Flame

Last Answer : (A) Work

Heating the Hypo-eutectoid steels to 30°C above the upper critical temperature line, soaking at that temperature and then cooling slowly to the room temperature to form a pearlite & ferrite structure is called (A) Tempering (B) Hardening (C) Annealing (D) Normalising

Description : Heating the Hypo-eutectoid steels to 30°C above the upper critical temperature line, soaking at that temperature and then cooling slowly to the room temperature to form a pearlite & ferrite structure is called (A) Tempering (B) Hardening (C) Annealing (D) Normalising

Last Answer : Option C

The heat treatment to which the steel wire containing > 0.25% carbon is subjected to is (A) Full annealing (B) Bright annealing (C) Patenting (D) None of these

Description : The heat treatment to which the steel wire containing > 0.25% carbon is subjected to is (A) Full annealing (B) Bright annealing (C) Patenting (D) None of these

Last Answer : C) Patenting

Nitriding of a steel part does not increase its (A) Grain size (B) Fatigue limit (C) Surface hardness (D) Wear resistance

Description : Nitriding of a steel part does not increase its (A) Grain size (B) Fatigue limit (C) Surface hardness (D) Wear resistance

Last Answer : Option B

Normalising of a casting does not (A) Induce stresses in it (B) Refine its grain structure (C) Reduce segregation (D) Improve its mechanical properties

Description : Normalising of a casting does not (A) Induce stresses in it (B) Refine its grain structure (C) Reduce segregation (D) Improve its mechanical properties

Last Answer : (A) Induce stresses in it

Post weld heat treatment is done by (A) Normalising (B) Stress relieving (C) Tempering (D) Solution annealing

Description : Post weld heat treatment is done by (A) Normalising (B) Stress relieving (C) Tempering (D) Solution annealing

Last Answer : (B) Stress relieving

Pick out the wrong statement. (A) Mechanical agitation is required, if the system has low interfacial tension (B) Sieve tray towers are generally used for systems having low interfacial tension (C) When Henry's law constant is very small, then the mass transfer rate is controlled by the gas film resistance (D) Taylor-Prandtl analogy for heat and mass transfer considers the transfer through both laminar and turbulent layers

Description : Pick out the wrong statement. (A) Mechanical agitation is required, if the system has low interfacial tension (B) Sieve tray towers are generally used for systems having low ... Prandtl analogy for heat and mass transfer considers the transfer through both laminar and turbulent layers

Last Answer : (A) Mechanical agitation is required, if the system has low interfacial tension

Cold working of a material results in increase in hardness, which is termed as the __________ hardening. (A) Cold (B) Work (C) Age (D) Induction

Description : Cold working of a material results in increase in hardness, which is termed as the __________ hardening. (A) Cold (B) Work (C) Age (D) Induction

Last Answer : (B) Work

Pick out the wrong statement pertaining to the cooling towers. (A) In case of induced draft cooling tower, the fan is placed at the top of the tower (B) Effectiveness of forced draft cooling tower is reduced by the recirculation of the humid and hot discharged air (C) A natural draft cooling tower is recommended to be used, when the air humidity is low and air temperature is also low (D) Effectiveness of a mechanical draft cooling tower is reduced with increase in air wet-bulb temperature

Description : Pick out the wrong statement pertaining to the cooling towers. (A) In case of induced draft cooling tower, the fan is placed at the top of the tower (B) Effectiveness of ... Effectiveness of a mechanical draft cooling tower is reduced with increase in air wet-bulb temperature

Last Answer : (D) Effectiveness of a mechanical draft cooling tower is reduced with increase in air wet-bulb temperature

Case hardening is not done by (A) Nitriding (B) Hot dipping (C) Electroplating (D) Both ‘b’ & ‘c’

Description : Case hardening is not done by (A) Nitriding (B) Hot dipping (C) Electroplating (D) Both ‘b’ & ‘c’

Last Answer : Option D

The minimum carbon content in steel should be __________ percent for it to respond to a hardening treatment. (A) 0.2 (B) 0.4 (C) 0.6 (D) 0.8

Description : The minimum carbon content in steel should be __________ percent for it to respond to a hardening treatment. (A) 0.2 (B) 0.4 (C) 0.6 (D) 0.8

Last Answer : Option A

Elimination of brittleness resulting from welding of saw blades is done by __________ of the welded portion. (A) Annealing (B) Toughening (C) Work hardening (D) Tempering

Description : Elimination of brittleness resulting from welding of saw blades is done by __________ of the welded portion. (A) Annealing (B) Toughening (C) Work hardening (D) Tempering

Last Answer : (A) Annealing

Pick out the wrong statement (A) Hardening makes the steel more brittle (B) High alloy steels contain more than 50% alloying element (C) 18/8 stainless steel is a magnetic steel (D) Both (B) and (C)

Description : Pick out the wrong statement (A) Hardening makes the steel more brittle (B) High alloy steels contain more than 50% alloying element (C) 18/8 stainless steel is a magnetic steel (D) Both (B) and (C)

Last Answer : (D) Both (B) and (C)

Steel is welded using the __________ flame(A) Carburising (B) Neutral (C) Oxidising (D) All (A), (B) & (C)

Description : Steel is welded using the __________ flame. (A) Carburising (B) Neutral (C) Oxidising (D) All (A), (B) & (C)

Last Answer : Option B

Normalising does not __________ of a metal. (A) Improve machinability & tensile strength (B) Remove internal stresses (C) Refine the structure (D) Remove strains caused by cold working

Description : Normalising does not __________ of a metal. (A) Improve machinability & tensile strength (B) Remove internal stresses (C) Refine the structure (D) Remove strains caused by cold working

Last Answer : Option B

Pick up the correct statement from the following: (A) Catalysts are added to assist and accelerate the hardening of resin (B) The fillers are inert materials and they impart strength and hardness (C) Fibrous fillers increase thermal resistance (D) All the above

Description : Pick up the correct statement from the following: (A) Catalysts are added to assist and accelerate the hardening of resin (B) The fillers are inert materials and they impart strength and hardness (C) Fibrous fillers increase thermal resistance (D) All the above

Last Answer : Answer: Option D

Pick out the wrong statement. (A) Alkylation produces a larger iso-paraffin (having higher octane number) from the reaction of an olefin with smaller iso-paraffin (B) Catalytic alkylation processes use HF, AlCl3 & H2SO4 as Catalysts (C) All the alkylation processes use very high temperature (> 1000°C) (D) Gasoline having an octane number of 90 can be produced by alkylation process

Description : Pick out the wrong statement. (A) Alkylation produces a larger iso-paraffin (having higher octane number) from the reaction of an olefin with smaller iso-paraffin (B) Catalytic alkylation processes use HF ... (> 1000°C) (D) Gasoline having an octane number of 90 can be produced by alkylation process

Last Answer : (C) All the alkylation processes use very high temperature (> 1000°C)

Pick out the wrong statement. (A) Weldability of high carbon steel is poorer compared to low carbon steel (B) Invar is a magnetic alloy (C) Magnetic permeability of the diamagnetic material is less than one (D) Martenistic transformation never goes to completion (i.e., 100%) at room temperature

Description : Pick out the wrong statement. (A) Weldability of high carbon steel is poorer compared to low carbon steel (B) Invar is a magnetic alloy (C) Magnetic permeability of the diamagnetic material is less than one (D) Martenistic transformation never goes to completion (i.e., 100%) at room temperature

Last Answer : Option B

Pick out the wrong statement. (A) Minimum number of degree of freedom of a system is zero (B) Degree of freedom of a system containing a gaseous mixture of helium, carbon dioxide and hydrogen is 4 (C) For a two phase system in equilibrium made up of fourchemical species, the number of degrees of freedom is 4 (D) Enthalpy and internal energy change is zero during phase change processes like melting, vaporisation and sublimation

Description : Pick out the wrong statement. (A) Minimum number of degree of freedom of a system is zero (B) Degree of freedom of a system containing a gaseous mixture of helium, carbon ... ) Enthalpy and internal energy change is zero during phase change processes like melting, vaporisation and sublimation

Last Answer : (D) Enthalpy and internal energy change is zero during phase change processes like melting, vaporisation and sublimation

Pick out the wrong statement. (A) Fluid movement under the influence of buoyant forces resulting from change in density takes place in case of natural convection (B) The ratio NNu /NRe . Npr is called the Stanton number (C) The Peclet number is a measure of the ratio of energy transport by convection to that by conduction (D) The Colburn jH factor for heat transfer is given by Nst Npr

Description : Pick out the wrong statement. (A) Fluid movement under the influence of buoyant forces resulting from change in density takes place in case of natural convection (B) The ratio NNu /NRe . Npr is ... convection to that by conduction (D) The Colburn jH factor for heat transfer is given by Nst Npr

Last Answer : (D) The Colburn jH factor for heat transfer is given by Nst Npr

Statement - 1 : Nitriding is the process of heating steel in presence of `N_(2)` to form iron nirides . Statement -2 : The surface of steel becomes ha

Description : Statement - 1 : Nitriding is the process of heating steel in presence of `N_(2)` to form iron nirides . Statement -2 : The surface of steel becomes ha

Last Answer : Statement - 1 : Nitriding is the process of heating steel in presence of `N_(2)` to form iron ... Statement-1 : is false , statement-2 : is true

When the steel is subjected to normalising, its __________ decreases. (A) Yield point (B) Ductility (C) Ultimate tensile strength (UTS)

Description : When the steel is subjected to normalising, its __________ decreases. (A) Yield point (B) Ductility (C) Ultimate tensile strength (UTS)

Last Answer : (B) Ductility

Normalising of an object does not (A) Refine coarse grain structure obtained during hot working (B) Improve ductility (C) Improve yield strength (D) Improve mechanical properties

Description : Normalising of an object does not (A) Refine coarse grain structure obtained during hot working (B) Improve ductility (C) Improve yield strength (D) Improve mechanical properties

Last Answer : (B) Improve ductility

A solid material shows case hardening properties while drying. Which of the following should be controlled to control the drying process? (A) Flow rate of inlet air (B) Relative humidity of outlet air (C) Humidity of inlet air (D) Temperature of the solid

Description : A solid material shows case hardening properties while drying. Which of the following should be controlled to control the drying process? (A) Flow rate of inlet air (B) Relative humidity of outlet air (C) Humidity of inlet air (D) Temperature of the solid

Last Answer : (D) Temperature of the solid

Pick out the wrong statement. (A) Tin can be readily and very easily drawn into very fine wire (B) Tin can be severely cold worked without the necessity of annealing due to its low recrystallisation temperature (C) Tin exists in two allotropic forms

Description : Pick out the wrong statement. (A) Tin can be readily and very easily drawn into very fine wire (B) Tin can be severely cold worked without the necessity of annealing due to its low recrystallisation temperature (C) Tin exists in two allotropic forms

Last Answer : (A) Tin can be readily and very easily drawn into very fine wire

What causes hardness in steel ? How heat treatment alters properties of steel ?

Description : What causes hardness in steel ? How heat treatment alters properties of steel ?

Last Answer : The shape and distribution of the carbides in the iron determines the hardness of the steel. Carbides can be dissolved in austenite is the basis of the heat treatment of steel. If ... range will produce the desired size and distribution of carbides in the ferrite, imparting different properties.