Description : Why is it essential to clean the excess weld metal on completion of the production weld? a) So it can be ready for painting b) To remove any rust c) To ensure it is suitably clean for visual inspection and NDT d) To remove slag from the undercut
Last Answer : c) To ensure it is suitably clean for visual inspection and NDT
Description : Why would visual inspection of the excess weld metal at the bottom of a cross country pipeline be important? a) It is the most difficult area to weld b) It is the dirtiest part of the pipe as ... ground c) Welders always forget to weld the bottom d) It is the most difficult area to radiograph
Last Answer : a) It is the most difficult area to weld
Description : What is the maximum distance that bracing can be installed from a node point on a scaffold? a. 200mm (8 inches) b. 300mm (12 inches) c. 150mm (6 inches) d. 250mm (10 inches)
Last Answer : b. 300mm (12 inches)
Description : A guardrail system must be fitted if the distance between a working platform a wall is more than? a. 100mm (4 inches) b. 360mm (14 inches) c. 200mm (8 inches) d. 460mm (18 inches)
Last Answer : b. 360mm (14 inches)
Description : The inverse Square Law is concerned with intensity of radiation using type D film of 200mm target to film distance, the exposure time was 0.25s. What would be the exposure for the same situation with 400mm target to film distance? M07********** A. 0.5s B. 1.0s C. 2.0s D. 0.25s E. 0.125s
Last Answer : B. 1.0s
Description : What is the minimum overlap required when splicing bracing? a. 300mm (12 inches) b. 400mm (16 inches) c. 600mm (24 inches) d. 450mm (18 inches)
Last Answer : a. 300mm (12 inches)
Description : The size of a plane table is (a) 750mm x 900 mm (b) 600mm x 750 mm* (c) 450mm x 600 mm
Last Answer : (b) 600mm x 750 mm*
Description : With the DPI method of inspection after the contact time has elapsed the dye should be removed by: a) Spraying the surface with the remover till all dye has gone then wipe with clean cloth b) Spraying with ... remover d) it doesn't matter how it is done as long as all traces of dye are removed
Last Answer : c) Wipe clean, using a clean cloth soaked in a solvent remover
Description : What is the recommended minimum range of illumination required by BS EN 970 for inspection of a welded surface? a) 90 to 125 lux b) 150 to 250 lux c) 350 to 500 lux d) 35 to 50 lux
Last Answer : c) 350 to 500 lux
Description : If shaft diameter is 60mm, how many bolts are recommended for rigid flange coupling? a) 2 b) 3 c) 4 d) 5
Last Answer : c) 4
Description : If shaft diameter is 40mm, calculate the diameter of sleeves in clamp coupling. a) 100mm b) 80mm c) 60mm d) 40mm
Last Answer : a) 100mm
Description : For dam construction the size of aggregates are (a) 40mm (b) 50mm (c) 60mm (d) 75mm
Last Answer : (a) 40mm
Description : The length of the vicat plunger is (a) 40mm (b) 60mm (c) 50mm (d) 30mm
Last Answer : (c) 50mm
Description : The bright-flash ERG: a. comes only from the cones b. is generated in a fully dark adapted eye by the highest intensity of light c. can be used to assess the overall retinal integrity in the presence of media opacity d. is abnormal in patients with age-related macular degeneration
Last Answer : can be used to assess the overall retinal integrity in the presence of media opacity
Description : What is the responsibility of an auditor who is engaged to audit the financial statements of a government entity? a. Assess control risk with respect to each component of internal ... the statements are free of material misstatements resulting from illegal acts having direct or indirect effects
Last Answer : Obtain an understanding of the possible financial statement effects of laws and regulations having direct and material effects on amounts reported.
Description : Tamron 18-270mm vs Canon 18-200mm vs Canon 18-135mm vs Canon 18-55mm+Canon 55-250mm --Which should I get?
Last Answer : answer:270 needs more light. As does the 250. IE Slower shutter speed and/or larger aperture.
Description : Nikon 55-200mm vs Nikon 70-300mm. Would you pick the former, or the latter?
Last Answer : i’d go for the 55–200 but i was never a big fan of telephoto. still, i think the versatility and price clinch it.
Description : has amplitude of vibration is 200mm and frequency of operation is 400 cycle/ sec. b. Acme tooth harrow c. Blade harrow d. None of the above
Last Answer : Ans- a. Reciprocating power harrow
Description : The top diameter, bottom diameter and height of the mould used for slump test are (a) 100mm, 200mm, 300mm (b) 200mm,100mm,300mm (c) 200mm,300mm,100mm (d) 100mm,300mm,200mm
Last Answer : (a) 100mm, 200mm, 300mm
Description : The height of a toe board must be at least? a. 100mm (4 inches) b. 200mm (8 inches) c. 150mm (6 inches) d. 230mm (9 inches)
Last Answer : c. 150mm (6 inches)
Description : The size of bridge timber required for the standard spans up to 18.3 m a) 250 x 150mm*. b) 250 x 180mm. c) 250 x 240mm d) 250 x 200mm
Last Answer : a) 250 x 150mm*.
Description : __________ is used for examining the macro-structure of a material. (A) Metallurgical microscope (B) Optical microscope (C) X-rays (D) Visual inspection by naked eye
Last Answer : (D) Visual inspection by naked eye
Description : On inspecting a completed weld which has charpy impact requirements some small, smooth, shallow areas of undercut have been found
Last Answer : d) Only allow the welder to cosmetically blend out the undercut
Description : A post weld heat treatment may also be of benefit in minimizing the risk of weld decay, this heat treatment would be called? a) Stress relief b) Normalizing c) Quench and Tempering d) Solution treatment over 1000 °C
Last Answer : d) Solution treatment over 1000 °C
Description : Weld decay can be minimized by specifying steel with: a) Higher carbon level b) higher chromium level c) lower carbon level d) lower chromium level
Last Answer : c) lower carbon level
Description : Weld decay will cause which of the following problems? a) A reduced resistance to corrosion b) a lower tensile strength c) The toughness is reduced d) The hardness will increase
Last Answer : a) A reduced resistance to corrosion
Description : Weld decay is caused by the formation of a compound with carbon. The other element in this compound is: a) Manganese b) Sulphur c) Chromium d) Nickel
Last Answer : c) Chromium
Description : Weld decay occurs in which of the following steel types? a) Carbon/Manganese b) Low alloy c) Any stainless steel d) Austenitic stainless steels
Last Answer : d) Austenitic stainless steels
Description : When MMA welding what will be the effect on the weld f the power source was changed from AC to DC-ve? a) None b) Higher deposition rate c) It would slightly increase the depth of penetration d) The arc would become unstable
Last Answer : b) Higher deposition rate
Description : A butt weld has been made by MMA in a 50mm thick impact tested steel plate. The welding electrode used was a basic type, 5mm diameter. The measured welding parameters for one of the runs was 250 amps, 24 volts, using DC ... given to calculate the arc energy b) 1.9 kJ/mm c) 1.87 kJ/mm d) 2.0 kJ/mm
Last Answer : d) 2.0 kJ/mm
Description : Root and face bends from an 8mm thick butt weld require testing. The specimens are cut to 20mm wide. The code calls for a 4t bend. Which of the following rollers should be selected for the testing? a) 50mm radius b) 50mdiameter c) 32mm radius d) 32mm diameter
Last Answer : d) 32mm diameter
Description : In a transverse WELD tensile test, if the break was in the weld metal, the sample would he: a) Rejected b) Acceptable if the UTS is equal to or greater than the specified UTS of the plate c) Retested d) Acceptable if the UTS is between 80 - 90% of the specified UTS of the plate
Last Answer : b) Acceptable if the UTS is equal to or greater than the specified UTS of the plate
Description : Who has the final responsibility of sentencing and accepting a weld on completion? a) The contractor’s inspector b) Site manager c) The welder d) The client’s inspector or certifying authority
Last Answer : d) The client’s inspector or certifying authority
Description : What is meant by the term PWHT? a) Pipe weld heat treatment b) Pre weld heat treatment c) Post weld hydrogen tearing d) Post weld het treatment
Last Answer : d) Post weld het treatment
Description : What information should be recorded as a minimum, on a completed production weld? a) Size and type of electrode and b) Welding supervisor’s name c) Welder’s Identification, date and weld number d) Welding inspectors name
Last Answer : c) Welder’s Identification, date and weld number
Description : The welders have increased the voltage on the SAW welding set, what would be the effect on the weld appearance? a) No effect b) The weld width would be narrower c) The penetration will be increased d) The weld width would be wider
Last Answer : d) The weld width would be wider
Description : t is permissible to allow trainee welder to carry out production welding? a) Never b) Yes as long as the supervisor is happy with his workmanship standard c) Yes as long as he has the approved ... cover the intended scope of work d) Yes as long as no NDT is required on the finished weld
Last Answer : a) Never
Description : What does the term WPQR means? a) Weld productivity quality review b) Weld production quality requirments c) Welding procedure
Last Answer : c) Welding procedure
Description : How is preheat for tack welds during assembly and fit up determined? a) By the welders as they have extensive knowledge b) The fabrication specification/WPS will give the requirements c) The fabrication drawing will give all the information d) Any temperature will do as it is only a tack weld
Last Answer : b) The fabrication specification/WPS will give the requirements
Description : Who determines what the correct weld preparation (root gap, root face, included angle) should be? a) The welding engineer b) The welding supervisor c) The welder will decide d) The inspector will recommend what is suitable
Last Answer : a) The welding engineer
Description : hat is the minimum distance between AT Weld and other joint exist in track? (i) 2 Mt. (ii) 3 Mt. (iii) 4 Mt.* (iv) 4.5 Mt.
Last Answer : (iii) 4 Mt.*
Description : What is the greatest disadvantage of radiographic inspection? a) the inability to size defects accurately b) The physical size of the equipment c) The skill level of the operator d) The harmful effects of ionizing radiation
Last Answer : d) The harmful effects of ionizing radiation
Description : Who should select the specific welds for NDT, to cover the 10% contractual percentage required by the specification/Code? a) Anyone can select the welds as its just a random choice b) The welder ... welding is always carried out to a high standard the use of percentage NDT is of no real value
Last Answer : c) This will be referenced in the inspection and test plan
Description : In order to assess the maximum revenue generated by an Ad on the app, which of the following metrics is chosen by the developer? a. eCPI b. eCOM c. eCPA d. None of the above
Last Answer : c. eCPA
Description : What is the meaning of the different symbols and abbreviations found on the documents that they use (such as surface finish to be achieved linear and geometric tolerances electronic components weld s?
Last Answer : Need answer
Description : Pick out the wrong statement. (A) Cold cracking of a weld is due to the presence of hydrogen gas in the weld (B) True stress is given by, σ = σE (1 + εE), where σE and εE ... in the iron blast furnace (D) High residual stress at the surface is beneficial for fatigue properties of a material
Last Answer : Option C
Description : Marking on weld should be done (i) On centre of the rail head (ii) 10 mm below the top surface of rail head.* (iii) 10 mm above the bottom surface of rail head. (iv) None of the above
Last Answer : ii) 10 mm below the top surface of rail head.*
Description : Painting of weld is done up to (i) 10 CM minimum both side of weld & on welded surface .* (ii) 15 CM minimum both side of weld & on welded surface (iii) 20 CM minimum both side of weld & on welded surface (iv) None of the above
Last Answer : (i) 10 CM minimum both side of weld & on welded surface .*